Alkali-free glass plate

ABSTRACT

The present invention provides an alkali-free glass sheet, including as a glass composition, in terms of mol %, 55% to 80% of SiO2, 10% to 25% of Al2O3, 0% to 4% of B2O3, 0% to 30% of MgO, 0% to 25% of CaO, 0% to 15% of SrO, 0% to 15% of BaO, 0% to 5% of ZnO, and 0% to less than 1.0% of Y2O3+La2O3, being substantially free of an alkali metal oxide, and having a strain point of 750° C. or more.

TECHNICAL FIELD

The present invention relates to an alkali-free glass sheet, and more particularly, to an alkali-free glass sheet suitable as a substrate for forming a TFT circuit in a flat panel display, such as a liquid crystal display or an OLED display, or as a carrier glass for holding a resin substrate for forming the TFT circuit.

BACKGROUND ART

As is well known, a liquid crystal panel or an OLED panel includes a thin film transistor (TFT) for driving control.

As a thin film transistor configured to drive a display, amorphous silicon, low-temperature polysilicon, high-temperature polysilicon, and the like have been known. In recent years, along with the spread of large liquid crystal displays, smartphones, tablet PCs, and the like, there is an increasing need for higher resolution of a display. A low-temperature polysilicon TFT can meet this need, but a high-temperature film forming process of from 500° C. to 600° C. is involved. However, a related-art glass sheet has a large thermal shrinkage amount before and after the high-temperature film forming process, and hence pattern deviation of the thin film transistor is caused. Accordingly, in order to increase the resolution of the display, a glass sheet with low thermal shrinkage is required. In recent years, a further increase in definition of the display has been investigated. In this case, a further reduction in thermal shrinkage of the glass sheet is required.

CITATION LIST

-   Patent Literature 1: JP 5769617 B2

SUMMARY OF INVENTION Technical Problem

As a main method of reducing the thermal shrinkage of the glass sheet, two methods are given. A first method is a method involving holding the glass sheet in advance at a temperature around a heat treatment temperature of the film forming process to anneal the glass sheet. In this method, glass undergoes structural relaxation and shrinks at the time of annealing, and hence a thermal shrinkage amount in the subsequent film forming process at high temperature can be suppressed. However, this method entails an increase in number of manufacturing steps and a longer manufacturing time, resulting in a rise in manufacturing cost of the glass sheet.

A second method is a method involving increasing the strain point of the glass sheet. In an overflow down-draw method, glass is generally cooled from a melting temperature to a forming temperature in a relatively short time. Under the influence of this, the fictive temperature of the glass sheet is increased, and the thermal shrinkage of the glass sheet is increased. In view of the foregoing, when the strain point of the glass sheet is increased, the viscosity of the glass sheet at a heat treatment temperature of the film forming process is increased, with the result that structural relaxation hardly proceeds. As a result, the thermal shrinkage of the glass sheet can be suppressed. Moreover, as the heat treatment temperature of the film forming process becomes higher, an increase in strain point has a higher effect on a reduction in thermal shrinkage. Accordingly, in the case of the low-temperature polysilicon TFT, it is desired that the strain point of the glass sheet be increased to the extent possible.

In Patent Literature 1, a high-strain-point glass including Y₂O₃ and/or La₂O₃ is disclosed. However, Y₂O₃ and La₂O₃ are rare earth elements, resulting in high raw material cost. There is a problem of a rise in manufacturing cost of the glass sheet.

The present invention has been made in view of the above-mentioned circumstances, and a technical object of the present invention is to devise an alkali-free glass sheet which has a high strain point and enables a reduction in manufacturing cost.

Solution to Problem

The inventors of the present invention have made extensive investigations, and as a result, have found that the above-mentioned technical object can be achieved by strictly restricting the contents of components and restricting a strain point to a predetermined value or more. The finding is proposed as the present invention. That is, according to one embodiment of the present invention, there is provided an alkali-free glass sheet, comprising as a glass composition, in terms of mol %, 55% to 80% of SiO₂, 10% to 25% of Al₂O₃, 0% to 4% of B₂O₃, 0% to 30% of MgO, 0% to 25% of CaO, 0% to 15% of SrO, 0% to 15% of BaO, 0% to 5% of ZnO, and 0% to less than 1.0% of Y₂O₃+La₂O₃, being substantially free of an alkali metal oxide, and having a strain point of 750° C. or more. Herein, the “Y₂O₃+La₂O₃” refers to the total content of Y₂O₃ and La₂O₃. The “substantially free of an alkali metal oxide” refers to a case in which the content of an alkali metal oxide (Li₂O, Na₂O, K₂O) in the glass composition is less than 0.5 mol %. The “strain point” refers to a value measured based on a method of ASTM C336.

In addition, it is preferred that the alkali-free glass sheet according to the one embodiment of the present invention satisfy a relationship of [SiO₂]+14×[Al₂O₃]-15×[B₂O₃]+6×[MgO]+[CaO]+14×[SrO]+16×[BaO]≥360 mol %. Herein, the [SiO₂] refers to the content of SiO₂ in terms of mol %, the [SiO₂] refers to the content of SiO₂ in terms of mol %, the [Al₂O₃] refers to the content of Al₂O₃ in terms of mol %, the [B₂O₃] refers to the content of B₂O₃ in terms of mol %, the [MgO] refers to the content of MgO in terms of mol %, the [CaO] refers to the content of CaO in terms of mol %, the [SrO] refers to the content of SrO in terms of mol %, and the [BaO] refers to the content of BaO in terms of mol %.

In addition, it is preferred that the alkali-free glass sheet according to the one embodiment of the present invention satisfy a relationship of 17.8×[SiO₂]+23.1×[Al₂O₃]+3.7×[B₂O₃]+12.9×[MgO]+14.1×[CaO]+15.5×[SrO]+15.0×[BaO]+7.2×[ZnO]≥1,786 mol %.

In addition, it is preferred that the alkali-free glass sheet according to the one embodiment of the present invention have a content of Rh of from 0.1 ppm by mass to 3 ppm by mass. Herein, the “Rh” includes not only Rh but also RhO₂ and Rh₂O₃, and RhO₂ and Rh₂O₃ are each represented in terms of Rh.

In addition, it is preferred that the alkali-free glass sheet according to the one embodiment of the present invention have a Young's modulus of 82 GPa or more. Herein, the “Young's modulus” may be measured by a flexural resonance method.

DESCRIPTION OF EMBODIMENTS

An alkali-free glass sheet of the present invention comprises as a glass composition, in terms of mol %, 55% to 80% of SiO₂, 10% to 25% of Al₂O₃, 0% to 4% of B₂O₃, 0% to 30% of MgO, 0% to 25% of CaO, 0% to 15% of SrO, 0% to 15% of BaO, 0% to 5% of ZnO, and 0% to less than 1.0% of Y₂O₃+La₂O₃, and is substantially free of an alkali metal oxide. The reasons why the contents of the components are limited as describe above are described below. In the descriptions of the contents of the components, the expression “%” represents “mol %”, unless otherwise specified.

SiO₂ is a component which forms a glass skeleton, and is also a component which increases a strain point. Accordingly, the content of SiO₂ is preferably 55% or more, 60% or more, 63% or more, 65% or more, or 67% or more, particularly preferably 68% or more. Meanwhile, when the content of SiO₂ is too large, a viscosity at high temperature is increased, and thus meltability is liable to be reduced. Accordingly, the content of SiO₂ is preferably 80% or less, 78% or less, 75% or less, 74% or less, or 73% or less, particularly preferably 72% or less.

Al₂O₃ is a component which forms the glass skeleton, and is also a component which increases the strain point. Further, Al₂O₃ is a component which suppresses phase separation. Accordingly, the content of Al₂O₃ is preferably 10% or more, 10.5% or more, 11% or more, or 11.5% or more, particularly preferably 12% or more. Meanwhile, when the content of Al₂O₃ is too large, the viscosity at high temperature is increased, and thus the meltability is liable to be reduced. Accordingly, the content of Al₂O₃ is preferably 25% or less, 22% or less, 20% or less, 18% or less, 16% or less, or 15% or less, particularly preferably 14% or less.

The total content of SiO₂ and Al₂O₃ is preferably 70% or more, 75% or more, 80% or more, 81% or more, 82% or more, 83% or more, or 84% or more, particularly preferably 85% or more. When the total content of SiO₂ and Al₂O₃ is too small, the strain point is liable to be reduced. Meanwhile, when the total content of SiO₂ and Al₂O₃ is too large, the viscosity at high temperature is increased, and thus the meltability is liable to be reduced. Accordingly, the total content of SiO₂ and Al₂O₃ is preferably 90% or less, 89% or less, 88% or less, or 87% or less, particularly preferably 86% or less.

B₂O₃ is an optional component, but its introduction in a small amount leads to an improvement in meltability. Accordingly, the content of B₂O₃ is preferably 0.01% or more, 0.1% or more, 0.2% or more, 0.3% or more, or 0.4% or more, particularly preferably 0.5% or more. Meanwhile, when the content of B₂O₃ is too large, the strain point is significantly reduced, or β-OH is significantly increased. While the details are described later, when the β-OH is increased, a thermal shrinkage rate is increased. Accordingly, the content of B₂O₃ is preferably 4% or less, 3.5% or less, 3% or less, 2.5% or less, 2% or less, or 1.5% or less, particularly preferably 1% or less.

MgO is a component which reduces the viscosity at high temperature to improve the meltability, and is also a component which improves devitrification resistance through balance with other components. Further, from the viewpoint of mechanical characteristics, MgO is a component which remarkably increases a Young's modulus. Accordingly, the content of MgO is preferably 0% or more, 0.5% or more, 1% or more, or 1.5% or more, particularly preferably 2% or more. Meanwhile, when the content of MgO is too large, the strain point is liable to be reduced, or the balance with other components is lost, resulting in a higher devitrification tendency. Accordingly, the content of MgO is preferably 30% or less, 15% or less, 10% or less, 9% or less, 8% or less, 7.5% or less, 7% or less, or 6.5% or less, particularly preferably 6% or less.

CaO is a component which reduces the viscosity at high temperature to improve the meltability, and is also a component which improves the devitrification resistance through balance with other components. Accordingly, the content of CaO is preferably 0% or more, 0.5% or more, 1% or more, or 1.5% or more, particularly preferably 2% or more. Meanwhile, when the content of CaO is too large, the strain point is liable to be reduced. Accordingly, the content of CaO is preferably 25% or less, 15% or less, 10% or less, 9% or less, 8% or less, 7.5% or less, 7% or less, or 6.5% or less, particularly preferably 6% or less.

SrO is a component which reduces the viscosity at high temperature to improve the meltability, and is also a component which improves the devitrification resistance through balance with other components. Accordingly, the content of SrO is preferably 0% or more, 0.5% or more, 1% or more, or 1.5% or more, particularly preferably 2% or more. Meanwhile, when the content of SrO is too large, the strain point is liable to be reduced. Accordingly, the content of SrO is preferably 15% or less, 10% or less, 9% or less, 8% or less, 7% or less, 6% or less, or 5% or less, particularly preferably 4% or less.

BaO is a component which reduces the viscosity at high temperature to improve the meltability, and is also a component which improves the devitrification resistance through balance with other components. Accordingly, the content of BaO is preferably 0% or more, 0.5% or more, 1% or more, 1.5% or more, 2% or more, or 2.5% or more, particularly preferably 3% or more. Meanwhile, when the content of BaO is too large, the strain point is liable to be reduced. Accordingly, the content of SrO is preferably 15% or less, 10% or less, 9% or less, 8% or less, 7.5% or less, 7% or less, or 6.5% or less, particularly preferably 6% or less.

The total content of SrO and BaO is preferably 0% or more, 2% or more, 3% or more, or 4% or more, particularly preferably 5% or more. When the total content of SrO and BaO is too small, the meltability is liable to be reduced. Meanwhile, when the total content of SrO and BaO is too large, the glass composition loses its component balance, and the devitrification resistance is liable to be reduced. Accordingly, the total content of SrO and BaO is preferably 20% or less, 16% or less, 14% or less, 12% or less, 10% or less, or 9% or less, particularly preferably 8% or less.

The total content of MgO, CaO, SrO, and BaO is preferably 9.9% or more, 12% or more, 12.5% or more, 13% or more, or 13.5% or more, particularly preferably 14% or more. When the total content of MgO, CaO, SrO, and BaO is too small, the meltability is liable to be reduced. Meanwhile, when the total content of MgO, CaO, SrO, and BaO is too large, the strain point is reduced, or the glass composition loses its component balance and the devitrification resistance is liable to be reduced. Accordingly, the total content of MgO, CaO, SrO, and BaO is preferably 25% or less, 20% or less, 16% or less, 15.5% or less, 15% or less, or 14.5% or less, particularly preferably 14% or less.

The mole percent ratio [B₂O₃]/([SrO]+[BaO]) is preferably from 0 to 0.5, from 0 to 0.45, from 0 to 0.4, from 0 to 0.35, from 0.01 to 0.3, or from 0.05 to 0.25, particularly preferably from 0.1 to 0.2. When the mole percent ratio [B₂O₃]/([SrO]+[BaO]) is outside the above-mentioned ranges, the balance between the components is lost in a glass system according to the present invention, and the devitrification resistance is liable to be reduced. The “[B₂O₃]/([SrO]+[BaO])” refers to a value obtained by dividing the content of B₂O₃ by the total content of SrO and BaO.

[SiO₂]+14×[Al₂O₃]−15×[B₂O₃]+6×[MgO]+[CaO]+14×[SrO]+16×[BaO] is preferably 300% or more, 330% or more, 350% or more, 360% or more, 370% or more, 380% or more, 390% or more, 400% or more, 410% or more, 420% or more, or 430% or more. When [SiO₂]+14×[Al₂O₃]−15×[B₂O₃]+6×[MgO]+[CaO]+14×[SrO]+16×[BaO] is too small, it becomes difficult to achieve all of a high strain point, a high Young's modulus, and high devitrification resistance.

17.8×[SiO₂]+23.1×[Al₂O₃]+3.7×[B₂O₃]+12.9×[MgO]+14.1×[CaO]+15.5×[SrO]+15.0×[BaO]+7.2×[ZnO] is preferably 1,740% or more, 1,750% or more, 1,760% or more, 1,770% or more, or 1,780% or more, particularly preferably 1,786% or more. When 17.8×[ SiO₂]+23.1×[Al₂O₃]+3.7×[B₂O₃]+12.9×[MgO]+14.1×[CaO]+15.5×[ SrO]+15.0×[BaO]+7.2×[ZnO] is too large, the thermal shrinkage of the glass sheet is liable to be increased.

[Al₂O₃]+[B₂O₃]−[CaO]−[SrO]−[BaO] is preferably 0% or more or 0.1% or more, particularly preferably 1.0% or more. When [Al₂O₃]±[B₂O₃]−[CaO]−[SrO]−[BaO] is too small, the amount of non-bridging oxygen or the like in glass is increased, and structural imbalance is liable to occur, with the result that thermal shrinkage is liable to occur in the glass sheet in a film forming process at high temperature. Meanwhile, when [Al₂O₃]+[B₂O₃]−[CaO]−[SrO]−[BaO] is too large, a melting load is increased, or the devitrification resistance is reduced, resulting in a rise in manufacturing cost of the glass sheet. Accordingly, [Al₂O₃]+[B₂O₃]−[CaO]−[SrO]−[BaO] is preferably 10.0% or less, 6.0% or less, 5.0% or less, 4.5% or less, 4.0% or less, or 3.0% or less, particularly preferably 2.0% or less.

Y₂O₃ is a component which increases the strain point, the Young's modulus, and the like. However, when the content thereof is too large, a density and raw material cost are liable to be increased. Accordingly, the content of Y₂O₃ is preferably from 0% to 0.8%, from 0% to 0.7%, from 0% to 0.5%, or from 0% to 0.2%, particularly preferably from 0% to 0.1%.

La₂O₃ is a component which increases the strain point, the Young's modulus, and the like. However, when the content thereof is too large, the density and the raw material cost are liable to be increased. Accordingly, the content of La₂O₃ is preferably from 0% to 0.8%, from 0% to 0.7%, from 0% to 0.5%, or from 0% to 0.2%, particularly preferably from 0% to 0.1%.

The total content of Y₂O₃ and La₂O₃ is preferably from 0% to less than 1.0%, from 0% to 0.8%, from 0% to 0.7%, from 0% to 0.5%, or from 0% to 0.2%, particularly preferably from 0% to 0.1%. However, when the total content of Y₂O₃ and La₂O₃ is too large, the density and the raw material cost are liable to be increased.

The alkali-free glass sheet of the present invention may comprise the following components in the glass composition in addition to the above-mentioned components.

ZnO is a component which increases the meltability. However, when ZnO is contained in a large amount, the glass is liable to devitrify, and in addition, the strain point is liable to be reduced. The content of ZnO is preferably from 0% to 5%, from 0% to 3%, from 0% to 0.5%, or from 0% to 0.3%, particularly preferably from 0% to 0.2%.

P₂O₅ is a component which remarkably reduces the liquidus temperature of an Al-based devitrified crystal while maintaining the strain point. However, when P₂O₅ is contained in a large amount, the Young's modulus is reduced, or the glass undergoes phase separation. In addition, P may be diffused from the glass and affect the performance of a TFT. Accordingly, the content of P₂O₅ is preferably from 0% to 1.5%, from 0% to 1.2%, or from 0% to 1%, particularly preferably from 0% to 0.5%.

TiO₂ is a component which reduces the viscosity at high temperature and thus increases the meltability, and is also a component which suppresses solarisation. However, when TiO₂ is contained in a large amount, the glass is colored, and thus a transmittance is liable to be reduced. Accordingly, the content of TiO₂ is preferably from 0 ppm by mass to 500 ppm by mass, from 0.1 ppm by mass to 100 ppm by mass, from 0.1 ppm by mass to 50 ppm by mass, from 0.5 ppm by mass to 30 ppm by mass, from 1 ppm by mass to 20 ppm by mass, or from 3 ppm by mass to 15 ppm by mass, particularly preferably from 5 ppm by mass to 10 ppm by mass.

SnO₂ is a component which exhibits a satisfactory fining action in a high temperature region. In addition, SnO₂ is a component which increases the strain point, and is also a component which reduces the viscosity at high temperature. The content of SnO₂ is preferably from 0% to 1%, from 0.001% to 1%, or from 0.05% to 0.5%, particularly preferably from 0.08% to 0.2%. When the content of SnO₂ is too large, a devitrified crystal of SnO₂ is liable to precipitate. When the content of SnO₂ is less than 0.001%, it becomes difficult to exhibit the above-mentioned effects.

SnO₂ is suitable as a fining agent, but any other fining agent than SnO₂ may be used as long as the characteristics of the glass are not significantly impaired. Specifically, As₂O₃, Sb₂O₃, CeO₂, F₂, Cl₂, SO₃, and C may be added at a total content of, for example, up to 0.5%, and metal powders, such as Al and Si, may be added at a total content of, for example, up to 0.5%.

As₂O₃ and Sb₂O₃ are excellent in fining property, but from an environmental viewpoint, it is preferred to introduce As₂O₃ and Sb₂O₃ in as small amounts as possible. Further, when As₂O₃ is contained in a large amount in the glass, solarization resistance tends to be reduced. Accordingly, the content thereof is preferably 1,000 ppm by mass or less or 100 ppm by mass or less, particularly preferably less than 30 ppm by mass. In addition, the content of Sb₂O₃ is preferably 1,000 ppm by mass or less or 100 ppm by mass or less, particularly preferably less than 30 ppm by mass.

Cl has an effect of promoting the melting of alkali-free glass. When Cl is added, a reduction in melting temperature can be achieved, and the action of the fining agent is promoted. As a result, while melting cost is reduced, the lifetime of a glass production kiln can be prolonged. However, when the content of Cl is too large, the strain point is liable to be reduced. Accordingly, the content of Cl is preferably 0.5% or less, particularly preferably 0.1% or less. An alkaline earth metal chloride, such as strontium chloride, aluminum chloride, or the like may be used as a raw material for introducing Cl.

Rh is a component which is included in a melting facility, and is thus a component which is eluted in a glass texture when the glass is melted at high temperature. Meanwhile, Rh is a component which colors the glass when Rh coexists with SnO₂. The content of Rh is preferably from 0 ppm by mass to 3 ppm by mass, from 0.1 ppm by mass to 3 ppm by mass, from 0.1 ppm by mass to 3 ppm by mass, from 0.2 ppm by mass to 2.5 ppm by mass, from 0.3 ppm by mass to 2 ppm by mass, or from 0.4 ppm by mass to 1.5 ppm by mass, particularly preferably from 0.5 ppm by mass to 1 ppm by mass. When the melting temperature is reduced, the content of Rh is easily reduced.

Ir has higher heat resistance than Pt or a Pt—Rh alloy, and is a component which can reduce bubbling of molten glass at an interface with the molten glass. In addition, Ir is a component which is included in the melting facility, and is thus a component which is eluted in the glass texture when the glass is melted at high temperature. Meanwhile, when the elution amount of Ir is increased, Ir may be precipitated as foreign matter in the glass. Accordingly, the content of Ir is preferably from 0 ppm by mass to 10 ppm by mass, from 0.01 ppm by mass to 10 ppm by mass, from 0.02 ppm by mass to 5 ppm by mass, from 0.03 ppm by mass to 3 ppm by mass, or from 0.04 ppm by mass to 2 ppm by mass, particularly preferably from 0.05 ppm by mass to 1 ppm by mass. The “Ir” includes not only Ir but also IrO₂ and Ir₂O₃, and IrO₂ and Ir₂O₃ are each represented in terms of Ir.

Molybdenum is a component which is used for an electrode in a melting step, and is thus a component which is eluted as MoO₃ in the glass texture when the glass is melted at high temperature. The content of MoO₃ is preferably from 0 ppm by mass to 50 ppm by mass, from 1 ppm by mass to 50 ppm by mass, from 3 ppm by mass to 40 ppm by mass, from 5 ppm by mass to 30 ppm by mass, or from 5 ppm by mass to 25 ppm by mass, particularly preferably from 5 ppm by mass to 20 ppm by mass. When the content of MoO₃ is too small, it becomes difficult to heat the molten glass through application of a current with a heating electrode, and hence it becomes difficult to reduce the β-OH.

ZrO₂ is a component which is included in a refractory in the melting step, and is thus a component which is eluted in the glass texture when the glass is melted at high temperature. In addition, ZrO₂ is a component which increases the liquidus temperature and weather resistance. Meanwhile, when the content of ZrO₂ is to be excessively reduced, an expensive refractory needs to be used in the melting step, which may result in a rise in manufacturing cost of the glass sheet. Accordingly, the content of ZrO₂ is preferably from 0 ppm by mass to 2,000 ppm by mass, from 500 ppm by mass to 2,000 ppm by mass, or from 550 ppm by mass to 1,500 ppm by mass, particularly preferably from 600 ppm by mass to 1,200 ppm by mass.

Fe₂O₃ is a component which is mixed in as a raw material impurity, and is also a component which reduces an electrical resistivity. The content of Fe₂O₃ is preferably from 50 ppm by mass to 300 ppm by mass or from 80 ppm by mass to 250 ppm by mass, particularly preferably from 100 ppm by mass to 200 ppm by mass. When the content of Fe₂O₃ is too small, the raw material cost is liable to rise. Meanwhile, when the content of Fe₂O₃ is too large, it becomes difficult to perform electric melting owing to an increase in electrical resistivity of the molten glass.

The alkali-free glass sheet of the present invention is substantially free of an alkali metal oxide, but a case in which an alkali metal oxide is mixed in as an inevitable impurity is not excluded. When an alkali metal oxide is mixed in as an inevitable impurity, the content of the alkali metal oxide (total content of Li₂O, Na₂O, and K₂O) is preferably from 10 ppm by mass to 1,000 ppm by mass, from 30 ppm by mass to 600 ppm by mass, from 50 ppm by mass to 300 ppm by mass, or from 70 ppm by mass to 200 ppm by mass, particularly preferably from 80 ppm by mass to 150 ppm by mass. In particular, the content of Na₂O is preferably from 30 ppm by mass to 600 ppm by mass, from 50 ppm by mass to 300 ppm by mass, or from 70 ppm by mass to 200 ppm by mass, particularly preferably from 80 ppm by mass to 150 ppm by mass. When the content of the alkali metal oxide is too small, the use of a high-purity raw material is essential, resulting in a rise in batch cost. In addition, an electrical conductivity is excessively reduced, and it becomes difficult to perform electric melting. Meanwhile, when the content of the alkali metal oxide is too large, an alkali ion may be diffused in a semiconductor film in a heat treatment step.

The alkali-free glass sheet of the present invention preferably has the following characteristics.

The thermal expansion coefficient is preferably 46×10⁻⁷/° C. or less, 42×10⁻⁷/° C. or less, 40×10⁻⁷/° C. or less, or 38×10⁻⁷/° C. or less, particularly preferably 26×10⁻⁷/° C. or more and 36×10⁻⁷/° C. or less. When the thermal expansion coefficient is too high, the glass sheet is liable to have a local dimensional change owing to temperature variations in the film forming process at high temperature.

The density is preferably 2.80 g/cm³ or less, 2.75 g/cm³ or less, 2.70 g/cm³ or less, 2.65 g/cm³ or less, 2.60 g/cm³ or less, or 2.55 g/cm³ or less, particularly preferably from 2.45 g/cm³ to 2.50 g/cm³. When the density is too high, the deflection amount of the glass sheet is liable to be increased, and hence pattern deviation caused by stress is liable to be promoted in, for example, manufacturing steps for a display.

The strain point is 750° C. or more, preferably 760° C. or more, 765° C. or more, 770° C. or more, 775° C. or more, 780° C. or more, 785° C. or more, 790° C. or more, 795° C. or more, or 800° C. or more. When the strain point is too low, thermal shrinkage is liable to occur in the glass sheet in the film forming process at high temperature.

The annealing point is preferably 800° C. or more, 805° C. or more, 810° C. or more, 820° C. or more, 830° C. or more, or 840° C. or more, particularly preferably 850° C. or more. When the annealing point is too low, thermal shrinkage is liable to occur in the glass sheet in the film forming process at high temperature.

The softening point is preferably 1,040° C. or more, 1,060° C. or more, or 1,080° C. or more, particularly preferably 1,100° C. or more. When the softening point is too low, thermal shrinkage is liable to occur in the glass sheet in the film forming process at high temperature.

The temperature at a viscosity at high temperature of 10^(2.5) dPa·s is preferably 1,750° C. or less, 1,720° C. or less, 1,700° C. or less, 1,690° C. or less, or 1,680° C. or less, particularly preferably 1,670° C. or less. When the temperature at 10^(2.5) dPa·s is high, the meltability and the fining property are liable to be reduced, resulting in a rise in manufacturing cost of the glass sheet.

The Young's modulus is preferably 80 GPa or more, 81 GPa or more, or 82 GPa or more, particularly preferably 83 GPa or more. When the Young's modulus is too low, the deflection amount of the glass sheet is liable to be increased, and hence pattern deviation caused by stress is liable to be promoted in, for example, manufacturing steps for a display.

The specific Young's modulus is preferably 30 GPa/g·cm⁻³ or more, 31 GPa/g·cm⁻³ or more, or 32 GPa/g·cm⁻³ or more, particularly preferably 33 GPa/g·cm⁻³ or more. When the specific Young's modulus is too low, the deflection amount of the glass sheet is liable to be increased, and hence pattern deviation caused by stress is liable to be promoted in, for example, manufacturing steps for a display.

The β-OH is an indicator of the amount of water in the glass. When the β-OH is reduced, the strain point can be increased. In addition, even with the same glass composition, a glass sheet having lower β-OH has a lower thermal shrinkage rate at a temperature equal to or lower than the strain point. The β-OH is preferably 0.30/mm or less, 0.25/mm or less, 0.20/mm or less, or 0.15/mm or less, particularly preferably 0.10/mm or less. When the β-OH is too low, the meltability is liable to be reduced. Accordingly, the β-OH is preferably 0.01/mm or more, particularly preferably 0.03/mm or more.

As a method of reducing the β-OH, the following methods are given: (1) a method involving selecting raw materials having low water contents; (2) a method involving adding a component (such as Cl or SO₃) which reduces the β-OH to the glass; (3) a method involving reducing the amount of water in a furnace atmosphere; (4) a method involving performing N₂ bubbling in molten glass; (5) a method involving adopting a small melting furnace; (6) a method involving increasing the flow rate of molten glass; and (7) a method involving adopting an electric melting method.

Herein, the “β-OH” refers to a value determined using the following mathematical formula by measuring the transmittances of the glass with an FT-IR.

β-OH=(1/X)log(T ₁ /T ₂)

X: Thickness (mm)

T₁: Transmittance (%) at a reference wavelength of 3,846 cm⁻¹

T₂: Minimum transmittance (%) at a wavelength around a hydroxyl group absorption wavelength of 3,600 cm⁻¹

It is preferred that the alkali-free glass sheet of the present invention have overflow-joined surfaces in a middle portion thereof in a sheet thickness direction. That is, it is preferred that the alkali-free glass sheet of the present invention be formed by an overflow down-draw method. The overflow down-draw method refers to a method in which molten glass is caused to overflow from both sides of a wedge-shaped refractory, and the overflowing molten glasses are subjected to down-draw downward at the lower end of the wedge-shaped refractory while being joined, to thereby form the glass into a flat sheet shape. By the overflow down-draw method, surfaces which are to serve as the surfaces of the glass sheet are formed in a state of free surfaces without being brought into contact with the refractory. As a result, a glass sheet having good surface quality can be manufactured without polishing at low cost. Further, an increase in area and a reduction in thickness are easily achieved as well.

The forming may be performed by, for example, a slot-down method, a redraw method, a float method, or a roll-out method as well as the overflow down-draw method.

The sheet thickness of the alkali-free glass sheet of the present invention is not particularly limited, but is preferably 1.0 mm or less, 0.7 mm or less, or 0.5 mm or less, particularly preferably from 0.05 mm to 0.4 mm. As the sheet thickness becomes smaller, weight saving of a liquid crystal panel or an OLED panel is more easily achieved. The sheet thickness may be adjusted based on, for example, a flow rate and a forming speed (sheet-drawing speed) at the time of glass production.

A method of manufacturing the alkali-free glass sheet of the present invention on an industrial scale preferably comprises a melting step of loading a glass batch to a melting furnace and heating the glass batch through application of a current with a heating electrode to obtain molten glass, the glass batch having been blended so as to comprise as a glass composition, in terms of mol %, 55% to 80% of SiO₂, 10% to 25% of Al₂O₃, 0% to 4% of B₂O₃, 0% to 30% of MgO, 0% to 25% of CaO, 0% to 15% of SrO, 0% to 15% of BaO, 0% to 5% of ZnO, and 0% to less than 1.0% of Y₂O₃+La₂O₃, and be substantially free of an alkali metal oxide, and a forming step of forming the obtained molten glass into an alkali-free glass sheet having a sheet thickness of from 0.1 mm to 0.7 mm by an overflow down-draw method.

In general, a manufacturing process for the glass sheet comprises a melting step, a fining step, a supplying step, a stirring step, and a forming step. The melting step is a step of melting a glass batch obtained by blending glass raw materials to provide molten glass. The fining step is a step of fining the molten glass obtained in the melting step by an action of a fining agent or the like. The supplying step is a step of transferring the molten glass from one step to another. The stirring step is a step of stirring the molten glass to homogenize the molten glass. The forming step is a step of forming the molten glass into a glass sheet. A step other than the above-mentioned steps, for example, a state adjusting step of adjusting the molten glass to be in a state suitable for forming may be introduced after the stirring step as required.

When the alkali-free glass sheet is manufactured on an industrial scale, the glass is generally melted by heating with a combustion flame of a burner. The burner is generally arranged at an upper portion of a melting kiln, and uses fossil fuel as its fuel, specifically, for example, liquid fuel, such as heavy oil, or gas fuel, such as LPG. The combustion flame may be obtained by mixing the fossil fuel and oxygen gas. However, such method is liable to entail an increase in β-OH because a large amount of water is mixed in the molten glass during the melting. Accordingly, in manufacturing the alkali-free glass sheet of the present invention, it is preferred to perform heating through application of a current with a heating electrode, and it is more preferred to melt the glass by heating through application of a current with a heating electrode without heating with the combustion flame of the burner, that is, perform full electric melting. With this configuration, water is less liable to be mixed in the molten glass during the melting, and hence the β-OH is easily controlled to 0.30/mm or less, 0.25/mm or less, 0.20/mm or less, or 0.15/mm or less, particularly 0.10/mm or less. Further, when the heating through application of a current with a heating electrode is performed, the amount of energy required for obtaining the molten glass per unit mass is reduced, and the amount of a melt volatile is reduced. As a result, an environmental load can be reduced.

Further, with regard to the heating through application of a current, as the amount of water in the glass batch becomes smaller, the β-OH in the glass sheet is reduced more easily. Moreover, a raw material for introducing B₂O₃ is liable to be a maximum water mixing source. Accordingly, from the viewpoint of manufacturing a glass sheet having low β-OH, it is preferred to reduce the content of B₂O₃ to the extent possible. In addition, as the amount of water in the glass batch becomes smaller, the glass batch spreads in a melting kiln more uniformly, and hence a homogeneous glass sheet with high quality is easily manufactured.

The heating through application of a current with a heating electrode is preferably performed by applying an alternating voltage to a heating electrode arranged at a bottom portion or a side portion of a melting kiln so as to be brought into contact with the molten glass in the melting kiln. A material having heat resistance and corrosion resistance to the molten glass is preferably used as a material for the heating electrode, and for example, tin oxide, molybdenum, platinum, or rhodium may be used. In particular, molybdenum is preferred from the viewpoint of the degree of freedom of installation in a furnace.

The alkali-free glass sheet of the present invention is substantially free of an alkali metal oxide, and hence has a high electrical resistivity. Accordingly, when the heating through application of a current with a heating electrode is performed, a current flows through not only the molten glass but also a refractory for forming the melting kiln, and the refractory for forming the melting kiln may be damaged early. In order to prevent such situation, it is preferred to use, as a furnace refractory, a zirconia-based refractory, particularly a zirconia electrocast brick, having a high electrical resistivity. In addition, it is preferred to introduce a small amount of a component (such as Fe₂O₃) which reduces the electrical resistivity into the molten glass (glass composition), and the content of Fe₂O₃ is preferably from 50 ppm by mass to 300 ppm by mass or from 80 ppm by mass to 250 ppm by mass, particularly preferably from 100 ppm by mass to 200 ppm by mass. Further, the content of ZrO₂ in the zirconia-based refractory is preferably 85 mass % or more, particularly preferably 90 mass % or more.

EXAMPLES Example 1

The present invention is hereinafter described by way of Examples. However, Examples below are merely examples, and the present invention is by no means limited to Examples below.

Examples (Sample Nos. 1 to 679) of the present invention are shown in Tables 1 to 49. The glass characteristics of Sample Nos. 281 to 679 are not actually measured values but calculation values calculated from composition factors.

TABLE 1 No. No. No. No. No. No. No. No. 1 2 3 4 5 6 7 8 mol % SiO₂ 72.9 58.8 64.1 71.7 75.1 59.8 59.8 59.8 Al₂O₃ 11.3 11.6 12.7 14.2 14.8 25.0 25.0 25.0 B₂O₃ 0.3 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 3.1 29.4 0.0 0.0 0.0 15.0 0.0 0.0 CaO 7.2 0.0 23.0 0.0 0.0 0.0 15.0 0.0 SrO 0.5 0.0 0.0 13.9 0.0 0.0 0.0 15.0 BaO 4.5 0.0 0.0 0.0 9.9 0.0 0.0 0.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 84.2 70.4 76.8 85.9 89.9 84.8 84.8 84.8 [MgO] + [CaO] + [SrO] + [BaO] 15.3 29.4 23.0 13.9 9.9 15.0 15.0 15.0 [SrO] + [BaO] 5.0 0.0 0.0 13.9 9.9 0.0 0.0 15.0 [B₂O₃]/([SrO] + [BaO]) 0.1 — — 0.0 0.0 — — 0.0 [Al₂O₃] + [B₂O₃] − −0.6 11.6 −10.4 0.2 5.0 25.0 10.0 10.0 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 331.4 397.7 264.4 464.9 440.4 499.8 424.8 619.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,776.5 1,694.4 1,758.6 1,819.5 1,827.4 1,835.4 1,853.4 1,874.4 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 39.8 42.0 50.7 42.9 36.0 32.0 38.2 40.9 (10⁻⁷/° C.) Density (g/cm³) 2.617 2.610 2.608 2.699 2.731 2.590 2.612 2.818 Strain point (° C.) 756 742 754 822 835 Unmea- 809 822 sured Annealing point (° C.) 813 787 802 886 904 Unmea- 858 875 sured Softening point (° C.) 1,058 960 988 1,165 Unmea- Unmea- 1,042 Unmea- sured sured sured 10^(4.5) dPa · s (° C.) 1,401 1,180 1,243 1,438 1,516 Unmea- Unmea- Unmea- sured sured sured 10^(4.0) dPa · s (° C.) 1,574 1,296 1,382 1,602 1,688 Unmea- Unmea- Unmea- sured sured sured 10^(3.0) dPa · s (° C.) 1,682 1,374 1,475 1,708 1,800 1,578 Unmea- Unmea- sured sured 10^(2.5) dPa · s (° C.) 1,335 1,138 1,193 1,379 1,458 Unmea- Unmea- Unmea- sured sured sured Young's modulus (GPa) 81.0 99.2 85.9 79.5 77.8 102.3 94.0 89.5 Specific Young's modulus 30.9 38.0 32.9 29.5 28.5 39.5 36.0 31.8 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.13 0.08 0.08 0.04 0.04 0.07 0.14 0.14 No. No. No. No. No. No. 9 10 11 12 13 14 mol % SiO₂ 59.8 64.8 64.8 64.8 64.8 69.8 Al₂O₃ 25.0 20.0 20.0 20.0 20.0 15.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 MgO 0.0 15.0 0.0 0.0 0.0 15.0 CaO 0.0 0.0 15.0 0.0 0.0 0.0 SrO 0.0 0.0 0.0 15.0 0.0 0.0 BaO 15.0 0.0 0.0 0.0 15.0 0.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 84.8 84.8 84.8 84.8 84.8 84.8 [MgO] + [CaO] + [SrO] + [BaO] 15.0 15.0 15.0 15.0 15.0 15.0 [SrO] + [BaO] 15.0 0.0 0.0 15.0 15.0 0.0 [B₂O₃]/([SrO] + [BaO]) 0.0 — — 0.0 0.0 — [Al₂O₃] + [B₂O₃] − 10.0 20.0 5.0 5.0 5.0 15.0 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 649.8 434.8 359.8 554.8 584.8 369.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,866.9 1,808.9 1,826.9 1,847.9 1,840.4 1,782.4 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 43.5 30.4 37.6 41.7 45.3 28.7 (10⁻⁷/° C.) Density (g/cm³) 3.015 2.537 2.566 2.778 2.977 2.482 Strain point (° C.) Unmea- Unmea- 808 824 832 Unmea- sured sured sured Annealing point (° C.) Unmea- Unmea- 861 880 894 Unmea- sured sured sured Softening point (° C.) Unmea- Unmea- 1,060 1,091 1,120 1,044 sured sured 10^(4.5) dPa · s (° C.) Unmea- Unmea- 1,327 1,365 1,413 1,330 sured sured 10^(4.0) dPa · s (° C.) Unmea- Unmea- 1,453 1,506 1,554 1,475 sured sured 10^(3.0) dPa · s (° C.) Unmea- Unmea- 1,538 1,595 1,645 1,568 sured sured 10^(2.5) dPa · s (° C.) Unmea- Unmea- 1,277 1,312 1,358 Unmea- sured sured sured Young's modulus (GPa) 84.5 97.2 89.5 84.8 80.3 91.9 Specific Young's modulus 28.0 38.3 34.9 30.5 27.0 37.0 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.07 0.11 0.05 0.07 0.05 0.12

TABLE 2 No. No. No. No. No. No. No. No. 15 16 17 18 19 20 21 22 mol % SiO₂ 69.8 69.8 69.8 69.8 69.8 69.8 69.8 64.8 Al₂O₃ 15.0 15.0 15.0 20.0 20.0 20.0 20.0 25.0 B₂O₃ 0..0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 0.0 0.0 0.0 10.0 0.0 0.0 0.0 10.0 CaO 15.0 0.0 0.0 0.0 10.0 0.0 0.0 0.0 SrO 0.0 15.0 0.0 0.0 0.0 10.0 0.0 0.0 BaO 0.0 0.0 15.0 0.0 0.0 0.0 10.0 0.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 84.8 84.8 84.8 89.8 89.8 89.8 89.8 89.8 [MgO] + [CaO] + [SrO] + [BaO] 15.0 15.0 15.0 10.0 10.0 10.0 10.0 10.0 [SrO] + [BaO] 0.0 15.0 15.0 0.0 0.0 10.0 10.0 0.0 [B₂O₃]/([SrO] + [BaO]) — 0.0 0.0 — — 0.0 0.0 — [Al₂O₃] + [B₂O₃] − 0.0 0.0 0.0 20.0 10.0 10.0 10.0 25.0 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 294.8 489.8 519.8 409.8 359.8 489.8 509.8 474.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,800.4 1,821.4 1,813.9 1,833.4 1,845.4 1,859.4 1,854.4 1,859.9 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 39.1 44.6 49.0 26.5 30.7 32.9 34.9 Unmea- (10⁻⁷/° C.) sured Density (g/cm³) 2.518 2.734 2.934 2.491 2.508 2.649 2.784 Unmea- sured Strain point (° C.) 808 823 832 Unmea- 809 823 824 Unmea- sured sured Annealing point (° C.) 862 882 896 Unmea- 870 881 888 Unmea- sured sured Softening point (° C.) 1,073 1,107 1,137 Unmea- 1,078 1,101 1,023 Unmea- sured sured 10^(4.5) dPa · s (° C.) 1,362 1,416 1,471 Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured 10^(4.0) dPa · s (° C.) 1,515 1,573 1,630 Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured 10^(3.0) dPa · s (° C.) 1,612 1,674 1,736 Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured 10^(2.5) dPa · s (° C.) 1,305 1,356 1,407 Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured Young's modulus (GPa) 84.8 79.8 75.0 94.2 89.1 86.0 82.6 Unmea- sured Specific Young's modulus 33.7 29.2 25.6 37.8 35.5 32.5 29.7 Unmea- (GPa/g · cm⁻³) sured β-OH (mm⁻¹) 0.07 0.13 0.13 0.15 0.15 0.15 0.07 0.04 No. No. No. No. No. No. 23 24 25 26 27 28 mol % SiO₂ 64.8 64.8 64.8 69.8 69.8 69.8 Al₂O₃ 25.0 25.0 25.0 15.0 15.0 15.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 MgO 0.0 0.0 0.0 7.5 7.5 7.5 CaO 10.0 0.0 0.0 7.5 0.0 0.0 SrO 0.0 10.0 0.0 0.0 7.5 0.0 BaO 0.0 0.0 10.0 0.0 0.0 7.5 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 89.8 89.8 89.8 84.8 84.8 84.8 [MgO] + [CaO] + [SrO] + [BaO] 10.0 10.0 10.0 15.0 15.0 15.0 [SrO] + [BaO] 0.0 10.0 10.0 0.0 7.5 7.5 [B₂O₃]/([SrO] + [BaO]) — 0.0 0.0 — 0.0 0.0 [Al₂O₃] + [B₂O₃] − 15.0 15.0 15.0 7.5 7.5 7.5 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 424.8 554.8 574.8 332.3 429.8 444.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,871.9 1,885.9 1,880.9 1,791.4 1,801.9 1,798.2 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient Unmea- Unmea- Unmea- 33.0 35.5 36.6 (10⁻⁷/° C.) sured sured sured Density (g/cm³) Unmea- Unmea- Unmea- 2.501 2.612 2.722 sured sured sured Strain point (° C.) Unmea- Unmea- Unmea- 773 776 780 sured sured sured Annealing point (° C.) Unmea- Unmea- Unmea- 828 833 839 sured sured sured Softening point (° C.) Unmea- Unmea- Unmea- 1,048 1,060 1,073 sured sured sured 10^(4.5) dPa · s (° C.) Unmea- Unmea- Unmea- 1,345 1,368 1,405 sured sured sured 10^(4.0) dPa · s (° C.) Unmea- Unmea- Unmea- 1,497 1,522 1,558 sured sured sured 10^(3.0) dPa · s (° C.) Unmea- Unmea- Unmea- 1,596 1,621 1,644 sured sured sured 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- 1,287 1,309 1,341 sured sured sured Young's modulus (GPa) Unmea- Unmea- Unmea- 89.1 86.5 83.9 sured sured sured Specific Young's modulus Unmea- Unmea- Unmea- 35.6 33.1 30.8 (GPa/g · cm⁻³) sured sured sured β-OH (mm⁻¹) 0.15 0.06 0.06 0.06 0.08 0.08

TABLE 3 No. No. No. No. No. No. No. No. 29 30 31 32 33 34 35 36 mol % SiO₂ 69.8 69.8 69.8 69.8 69.8 69.8 69.8 69.8 Al₂O₃ 15.0 15.0 15.0 13.0 13.0 13.0 13.0 13.0 B₂O₃ 0..0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 0.0 0.0 0.0 8.5 8.5 8.5 0.0 0.0 CaO 7.5 7.5 0.0 8.5 0.0 0.0 8.5 8.5 SrO 7.5 0.0 7.5 0.0 8.5 0.0 8.5 0.0 BaO 0.0 7.5 7.5 0.0 0.0 8.5 0.0 8.5 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 84.8 84.8 84.8 82.8 82.8 82.8 82.8 82.8 [MgO] + [CaO] + [SrO] + [BaO] 15.0 15.0 15.0 17.0 17.0 17.0 17.0 17.0 [SrO] + [BaO] 7.5 7.5 15.0 0.0 8.5 8.5 8.5 8.5 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 — 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − 0.0 0.0 0.0 4.5 4.5 4.5 −4.0 −4.0 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 392.3 407.3 504.8 311.3 421.8 438.3 379.3 396.3 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,810.9 1,807.2 1,817.7 1,772.2 1,784.1 1,779.9 1,794.3 1,790.1 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2 [ZnO] Thermal expansion coefficient 41.0 43.0 46.4 35.5 38.3 40.3 44.5 46.9 (10⁻⁷/° C.) Density (g/cm³) 2.623 2.736 2.838 2.503 2.631 2.757 2.654 2.782 Strain point (° C.) 806 798 816 760 767 770 774 762 Annealing point (° C.) 863 856 879 814 823 829 830 819 Softening point (° C.) 1,075 1,091 1,117 1,035 1,048 1,060 1,052 1,051 10^(4.5) dPa · s (° C.) 1,393 1,411 1,444 1,339 1,362 1,383 1,367 1,382 10^(4.0) dPa · s (° C.) 1,547 1,570 1,605 1,495 1,519 1,545 1,528 1,549 10^(3.0) dPa · s (° C.) 1,648 1,673 1,708 1,597 1,620 1,651 1,633 1,656 10^(2.5) dPa · s (° C.) 1,330 1,352 1,382 1,280 1,301 1,321 1,306 1,318 Young's modulus (GPa) 83.0 80.5 78.1 87.9 85.2 82.1 81.9 79.3 Specific Young's modulus 31.6 29.4 27.5 35.1 32.4 29.8 30.9 28.5 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.10 0.09 0.14 0.05 0.08 0.07 0.07 0.09 No. No. No. No. No. No. 37 38 39 40 41 42 mol % SiO₂ 69.8 63.8 63.8 63.8 63.8 63.8 Al₂O₃ 13.0 18.0 18.0 18.0 18.0 18.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 MgO 0.0 9.0 9.0 9.0 0.0 0.0 CaO 0.0 9.0 0.0 0.0 9.0 9.0 SrO 8.5 0.0 9.0 0.0 9.0 0.0 BaO 8.5 0.0 0.0 9.0 0.0 9.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 82.8 81.8 81.8 81.8 81.8 81.8 [MgO] + [CaO] + [SrO] + [BaO] 17.0 18.0 18.0 18.0 18.0 18.0 [SrO] + [BaO] 17.0 0.0 9.0 9.0 9.0 9.0 [B₂O₃]/([SrO] + [BaO]) 0.0 — 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − −4.0 9.0 9.0 9.0 0.0 0.0 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 506.8 378.8 495.8 513.8 450.8 468.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,802.0 1,794.4 1,807.0 1,802.5 1,817.8 1,813.3 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2 [ZnO] Thermal expansion coefficient 49.6 36.6 39.1 40.1 45.1 46.8 (10⁻⁷/° C.) Density (g/cm³) 2.901 2.565 2.695 2.825 2.708 2.838 Strain point (° C.) 768 766 771 777 802 797 Annealing point (° C.) 828 818 824 814 856 855 Softening point (° C.) 1,063 1,019 1,032 1,042 1,060 1,065 10^(4.5) dPa · s (° C.) 1,404 1,283 1,305 1,326 1,328 1,346 10^(4.0) dPa · s (° C.) 1,576 1,417 1,442 1,467 1,468 1,489 10^(3.0) dPa · s (° C.) 1,686 1,505 1,531 1,559 1,559 1,582 10^(2.5) dPa · s (° C.) 1,338 1,233 1,253 1,273 1,276 1,292 Young's modulus (GPa) 77.1 93.1 90.0 86.7 85.7 82.9 Specific Young's modulus 26.6 36.3 33.4 30.7 31.6 29.2 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.09 0.08 0.14 0.08 0.07 0.07

TABLE 4 No. No. No. No. No. No. No. No. 43 44 45 46 47 48 49 50 mol % SiO₂ 63.8 63.8 63.8 63.8 63.8 63.8 63.8 69.8 Al₂O₃ 18.0 16.0 16.0 16.0 16.0 16.0 16.0 15.0 B₂O₃ 0..0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 0.0 10.0 10.0 10.0 0.0 0.0 0.0 0.0 CaO 0.0 10.0 0.0 0.0 10.0 10.0 0.0 10.0 SrO 9.0 0.0 10.0 0.0 10.0 0.0 10.0 5.0 BaO 9.0 0.0 0.0 10.0 0.0 10.0 10.0 0.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 81.8 79.8 79.8 79.8 79.8 79.8 79.8 84.8 [MgO] + [CaO] + [SrO] + [BaO] 18.0 20.0 20.0 20.0 20.0 20.0 20.0 15.0 [SrO] + [BaO] 18.0 0.0 10.0 10.0 10.0 10.0 20.0 5.0 [B₂O₃]/([SrO] + [BaO]) 0.0 — 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − 0.0 6.0 6.0 6.0 −4.0 −4.0 −4.0 0.0 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 585.8 357.8 487.8 507.8 437.8 457.8 587.8 359.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,825.9 1,775.2 1,789.2 1,784.2 1,801.2 1,796.2 1,810.2 1,807.4 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 49.9 38.8 41.5 43.8 47.3 50.7 53.8 40.9 (10⁻⁷/° C.) Density (g/cm³) 2.959 2.568 2.716 2.863 2.736 2.880 3.024 2.591 Strain point (° C.) 817 756 761 766 779 768 777 804 Annealing point (° C.) 876 807 813 820 832 823 833 861 Softening point (° C.) 1,053 1,008 1,020 1,033 1,034 1,036 1,052 1,080 10^(4.5) dPa · s (° C.) 1,382 1,269 1,294 1,314 1,309 1,325 1,364 1,374 10^(4.0) dPa · s (° C.) 1,528 1,404 1,433 1,456 1,451 1,472 1,504 1,534 10^(3.0) dPa · s (° C.) 1,620 1,492 1,524 1,547 1,543 1,565 1,598 1,630 10^(2.5) dPa · s (° C.) 1,316 1,219 1,241 1,260 1,256 1,269 1,305 1,316 Young's modulus (GPa) 80.0 92.1 88.7 85.1 84.7 81.6 79.0 83.7 Specific Young's modulus 27.0 35.9 32.7 29.7 31.0 28.3 26.1 32.3 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.05 0.11 0.15 0.06 0.11 0.06 0.04 0.08 No. No. No. No. No. No. 51 52 53 54 55 56 mol % SiO₂ 69.8 69.8 69.8 66.5 69.8 69.8 Al₂O₃ 15.0 15.0 15.0 14.3 15.0 15.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 MgO 0.0 0.0 0.0 0.0 0.0 0.0 CaO 10.0 5.0 5.0 4.8 0.0 0.0 SrO 0.0 10.0 5.0 0.0 10.0 5.0 BaO 5.0 0.0 5.0 14.3 5.0 10.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 84.8 84.8 84.8 80.8 84.8 84.8 [MgO] + [CaO] + [SrO] + [BaO] 15.0 15.0 15.0 19.0 15.0 15.0 [SrO] + [BaO] 5.0 10.0 10.0 14.3 15.0 15.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − 0.0 0.0 0.0 −4.8 0.0 0.0 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 369.8 424.8 434.8 499.8 499.8 509.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,804.9 1,814.4 1,811.9 1,794.6 1,818.9 1,816.4 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 42.1 42.4 43.8 53.2 45.9 47.4 (10⁻⁷/° C.) Density (g/cm³) 2.665 2.662 2.734 2.989 2.804 2.875 Strain point (° C.) 798 808 800 758 818 818 Annealing point (° C.) 856 867 862 816 880 882 Softening point (° C.) 1,082 1,089 1,094 1,041 1,112 1,121 10^(4.5) dPa · s (° C.) 1,392 1,398 1,410 1,359 1,430 1,453 10^(4.0) dPa · s (° C.) 1,547 1,556 1,568 1,517 1,591 1,617 10^(3.0) dPa · s (° C.) 1,649 1,658 1,669 1,617 1,698 1,730 10^(2.5) dPa · s (° C.) 1,332 1,338 1,349 1,297 1,369 1,389 Young's modulus (GPa) 82.0 82.2 81.1 78.4 79.2 77.5 Specific Young's modulus 30.8 30.9 29.7 26.2 28.2 27.0 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.09 0.10 0.11 0.09 0.09 0.03

TABLE 5 No. No. No. No. No. No. No. No. 57 58 59 60 61 62 63 64 mol % SiO₂ 69.8 69.8 69.8 69.8 69.8 69.8 69.8 69.8 Al₂O₃ 15.0 15.0 15.0 15.0 15.0 15.0 15.0 15.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 5.0 5.0 5.0 5.0 5.0 5.0 10.0 10.0 CaO 10.0 5.0 5.0 0.0 0.0 0.0 5.0 0.0 SrO 0.0 5.0 0.0 10.0 5.0 0.0 0.0 5.0 BaO 0.0 0.0 5.0 0.0 5.0 10.0 0.0 0.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 84.8 84.8 84.8 84.8 84.8 84.8 84.8 84.8 [MgO] + [CaO] + [SrO] + [BaO] 15.0 15.0 15.0 15.0 15.0 15.0 15.0 15.0 [SrO] + [BaO] 0.0 5.0 5.0 10.0 10.0 10.0 0.0 5.0 [B₂O₃]/([SrO] + [BaO]) — 0.0 0.0 0.0 0.0 0.0 — 0.0 [Al₂O₃] + [B₂O₃] − 5.0 5.0 5.0 5.0 5.0 5.0 10.0 10.0 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 319.8 384.8 394.8 449.8 459.8 469.8 344.8 409.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,794.4 1,801.4 1,798.9 1,808.4 1,805.9 1,803.4 1,788.4 1,795.4 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 35.4 36.9 37.8 38.4 39.5 40.7 32.2 33.7 (10⁻⁷/° C.) Density (g/cm³) 2.505 2.582 2.656 2.654 2.725 2.796 2.492 2.569 Strain point (° C.) 776 776 773 782 782 788 771 773 Annealing point (° C.) 833 834 833 841 843 850 825 830 Softening point (° C.) 1,052 1,058 1,064 1,070 1,076 1,087 1,043 1,051 10^(4.5) dPa · s (° C.) 1,345 1,364 1,375 1,381 1,393 1,411 1,334 1,351 10^(4.0) dPa · s (° C.) 1,498 1,523 1,532 1,538 1,553 1,571 1,484 1,501 10^(3.0) dPa · s (° C.) 1,595 1,625 1,632 1,639 1,655 1,674 1,581 1,601 10^(2.5) dPa · s (° C.) 1,288 1,305 1,315 1,321 1,332 1,349 1,278 1,293 Young's modulus (GPa) 88.3 67.1 85.3 84.9 83.4 81.7 90.7 88.7 Specific Young's modulus 35.3 33.7 32.1 32.0 30.6 29.2 36.4 34.5 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.04 0.14 0.09 0.15 0.08 0.12 0.08 0.13 No. No. No. No. No. No. 65 66 67 68 69 70 mol % SiO₂ 69.8 69.8 69.8 69.8 69.8 69.8 Al₂O₃ 15.0 15.0 15.0 15.0 15.0 15.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 MgO 10.0 0.0 6.0 7.0 2.5 2.5 CaO 0.0 5.0 0.0 0.0 12.5 10.0 SrO 0.0 0.0 9.0 4.0 0.0 2.5 BaO 5.0 10.0 0.0 4.0 0.0 0.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 84.8 84.8 84.8 84.8 84.8 84.8 [MgO] + [CaO] + [SrO] + [BaO] 15.0 15.0 15.0 15.0 15.0 15.0 [SrO] + [BaO] 5.0 10.0 9.0 8.0 0.0 2.5 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 — 0.0 [Al₂O₃] + [B₂O₃] − 10.0 0.0 6.0 7.0 2.5 2.5 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 419.8 444.8 441.8 441.8 407.3 339.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,792.9 1,809.4 1,805.8 1,801.2 1,797.4 1,800.9 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 34.3 44.6 37.2 37.0 37.5 38.0 (10⁻⁷/° C.) Density (g/cm³) 2.644 2.790 2.637 2.671 2.513 2.550 Strain point (° C.) 774 798 777 774 786 784 Annealing point (° C.) 832 860 836 833 842 842 Softening point (° C.) 1,056 1,100 1,065 1,066 1,062 1,064 10^(4.5) dPa · s (° C.) 1,359 1,432 1,376 1,380 1,356 1,363 10^(4.0) dPa · s (° C.) 1,513 1,594 1,533 1,538 1,510 1,519 10^(3.0) dPa · s (° C.) 1,611 1,694 1,632 1,638 1,608 1,617 10^(2.5) dPa · s (° C.) 1,301 1,388 1,316 1,320 1,299 1,305 Young's modulus (GPa) 86.9 78.9 86.0 85.3 86.9 86.4 Specific Young's modulus 32.9 28.3 32.6 31.9 34.6 33.9 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.14 0.03 0.09 0.12 0.06 0.06

TABLE 6 No. No. No. No. No. No. No. No. 71 72 73 74 75 76 77 78 mol % SiO₂ 69.8 69.8 69.8 69.8 69.8 69.8 69.8 69.8 Al₂O₃ 15.0 15.0 15.0 15.0 15.0 15.0 15.0 15.0 B₂O₃ 0..0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 2.5 2.5 2.5 2.5 2.5 0.0 1.0 1.0 CaO 10.0 5.0 5.0 5.0 5.0 10.0 6.0 6.0 SrO 0.0 7.5 5.0 2.5 0.0 2.5 8.0 4.0 BaO 2.5 0.0 2.5 5.0 7.5 2.5 0.0 4.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 84.8 84.8 84.8 84.8 84.8 84.8 84.8 84.8 [MgO] + [CaO] + [SrO] + [BaO] 15.0 15.0 15.0 15.0 15.0 15.0 15.0 15.0 [SrO] + [BaO] 2.5 7.5 7.5 7.5 7.5 5.0 8.0 8.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − 2.5 2.5 2.5 2.5 2.5 0.0 1.0 1.0 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 344.8 404.8 409.8 414.8 419.8 364.8 403.8 411.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,799.7 1,807.9 1,806.7 1,805.4 1,804.2 1,806.2 1,810.4 1,808.4 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 38.5 39.5 39.9 40.5 41.0 41.2 41.0 41.6 (10⁻⁷/° C.) Density (g/cm³) 2.583 2.621 2.654 2.689 2.719 2.624 2.632 2.685 Strain point (° C.) 780 783 782 779 780 797 795 790 Annealing point (° C.) 838 842 841 839 840 856 854 850 Softening point (° C.) 1,066 1,072 1,074 1,076 1,080 1,080 1,080 1,082 10^(4.5) dPa · s (° C.) 1,368 1,381 1,388 1,392 1,403 1,387 1,390 1,400 10^(4.0) dPa · s (° C.) 1,522 1,539 1,546 1,552 1,565 1,545 1,548 1,560 10^(3.0) dPa · s (° C.) 1,621 1,638 1,646 1,654 1,667 1,646 1,649 1,661 10^(2.5) dPa · s (° C.) 1,310 1,321 1,328 1,331 1,341 1,327 1,330 1,339 Young's modulus (GPa) 85.6 85.0 84.3 83.3 82.5 83.3 83.9 82.7 Specific Young's modulus 33.2 32.4 31.8 31.0 30.4 31.7 31.9 30.8 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.03 0.13 0.14 0.14 0.11 0.11 0.15 0.04 No. No. No. No. No. No. 79 80 81 82 83 84 mol % SiO₂ 69.8 69.8 69.8 69.8 69.8 69.8 Al₂O₃ 15.0 15.0 15.0 15.0 15.0 15.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 MgO 1.0 2.5 2.5 2.5 2.5 7.5 CaO 6.0 0.0 0.0 0.0 0.0 2.5 SrO 0.0 12.5 7.5 5.0 0.0 0.0 BaO 8.0 0.0 5.0 7.5 12.5 5.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 84.8 84.8 84.8 84.8 84.8 84.8 [MgO] + [CaO] + [SrO] + [BaO] 15.0 15.0 15.0 15.0 15.0 15.0 [SrO] + [BaO] 8.0 12.5 12.5 12.5 12.5 5.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − 1.0 2.5 2.5 2.5 2.5 7.5 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 419.8 469.8 479.8 484.8 496.8 407.3 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,806.4 1,814.9 1,812.4 1,811.2 1,808.7 1,795.9 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 42.5 41.3 42.3 43.0 44.3 36.0 (10⁻⁷/° C.) Density (g/cm³) 2.736 2.693 2.748 2.785 2.844 2.649 Strain point (° C.) 788 793 790 788 795 774 Annealing point (° C.) 849 853 852 851 860 832 Softening point (° C.) 1,088 1,085 1,092 1,098 1,118 1,062 10^(4.5) dPa · s (° C.) 1,410 1,400 1,417 1,426 1,441 1,370 10^(4.0) dPa · s (° C.) 1,572 1,559 1,580 1,590 1,602 1,527 10^(3.0) dPa · s (° C.) 1,675 1,660 1,663 1,692 1,704 1,627 10^(2.5) dPa · s (° C.) 1,348 1,339 1,354 1,363 1,380 1,311 Young's modulus (GPa) 81.4 83.0 81.2 80.6 78.1 86.5 Specific Young's modulus 29.8 30.8 29.5 28.9 27.5 32.6 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.14 0.03 0.07 0.15 0.09 0.13

TABLE 7 No. No. No. No. No. No. No. No. 85 86 87 88 89 90 91 92 mol % SiO₂ 69.8 69.8 69.8 69.8 69.8 69.8 69.8 69.8 Al₂O₃ 15.0 15.0 15.0 15.0 15.0 15.0 15.0 15.0 B₂O₃ 0..0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 7.5 5.0 5.0 5.0 2.5 2.5 2.5 2.5 CaO 0.0 2.5 2.5 0.0 7.5 2.5 2.5 2.5 SrO 2.5 2.5 0.0 2.5 0.0 5.0 2.5 0.0 BaO 5.0 5.0 7.5 7.5 5.0 5.0 7.5 10.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 84.8 84.8 84.8 84.8 84.8 84.8 84.8 84.8 [MgO] + [CaO] + [SrO] + [BaO] 15.0 15.0 15.0 15.0 15.0 15.0 15.0 15.0 [SrO] + [BaO] 7.5 7.5 7.5 10.0 5.0 10.0 10.0 10.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − 7.5 5.0 5.0 5.0 2.5 2.5 2.5 2.5 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 439.8 427.3 432.3 464.8 382.3 447.3 452.3 457.3 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,799.4 1,802.4 1,801.2 1,804.7 1,801.9 1,808.9 1,807.7 1,806.4 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 36.9 39.1 38.9 40.1 39.7 41.3 42.0 42.7 (10⁻⁷/° C.) Density (g/cm³) 2.585 2.691 2.727 2.764 2.660 2.731 2.765 2.804 Strain point (° C.) 778 777 780 783 782 786 788 789 Annealing point (° C.) 837 837 840 844 841 846 849 852 Softening point (° C.) 1,068 1,072 1,075 1,081 1,072 1,084 1,088 1,094 10^(4.5) dPa · s (° C.) 1,379 1,385 1,393 1,401 1,384 1,404 1,414 1,420 10^(4.0) dPa · s (° C.) 1,537 1,544 1,551 1,562 1,544 1,563 1,576 1,580 10^(3.0) dPa · s (° C.) 1,639 1,644 1,651 1,664 1,646 1,664 1,678 1,680 10^(2.5) dPa · s (° C.) 1,319 1,325 1,332 1,340 1,324 1,343 1,351 1,358 Young's modulus (GPa) 85.4 84.6 83.5 82.6 83.9 82.5 81.3 80.7 Specific Young's modulus 31.8 31.4 30.6 29.9 31.5 30.2 29.4 28.8 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.05 0.12 0.12 0.08 0.15 0.04 0.11 0.07 No. No. No. No. No. No. 93 94 95 96 97 98 mol % SiO₂ 69.8 69.8 69.8 69.8 69.8 68.8 Al₂O₃ 15.0 15.0 15.0 15.0 15.0 15.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 1.0 MgO 2.5 3.5 3.5 3.5 3.5 2.5 CaO 0.0 4.0 5.0 3.0 3.5 5.0 SrO 2.5 0.0 0.0 0.0 1.5 0.0 BaO 10.0 7.5 6.5 8.5 6.5 7.5 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 84.8 84.8 84.8 84.8 84.8 83.8 [MgO] + [CaO] + [SrO] + [BaO] 15.0 15.0 15.0 15.0 15.0 15.0 [SrO] + [BaO] 12.5 7.5 6.5 8.5 8.0 7.5 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.1 [Al₂O₃] + [B₂O₃] − 2.5 3.5 3.5 3.5 3.5 3.5 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 489.8 424.8 409.8 439.8 429.3 403.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,809.9 1,803.0 1,802.1 1,803.9 1,804.2 1,790.1 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2 [ZnO] Thermal expansion coefficient 43.8 40.3 39.5 41.0 40.3 41.2 (10⁻⁷/° C.) Density (g/cm³) 2.834 2.731 2.701 2.760 2.723 2.725 Strain point (° C.) 797 780 779 782 780 767 Annealing point (° C.) 860 841 839 844 840 827 Softening point (° C.) 1,104 1,078 1,074 1,084 1,077 1,065 10^(4.5) dPa · s (° C.) 1,438 1,395 1,391 1,404 1,396 1,381 10^(4.0) dPa · s (° C.) 1,602 1,555 1,548 1,566 1,556 1,539 10^(3.0) dPa · s (° C.) 1,706 16.54 1,649 1,671 1,655 1,640 10^(2.5) dPa · s (° C.) 1,374 1,334 1,330 1,342 1,335 1,321 Young's modulus (GPa) 79.6 82.9 83.4 82.4 83.3 81.4 Specific Young's modulus 28.1 30.4 30.9 29.8 30.6 29.9 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.05 0.07 0.06 0.13 0.09 0.03

TABLE 8 No. No. No. No. No. No. No. No. 99 100 101 102 103 104 105 106 mol % SiO₂ 70.8 70.8 69.8 69.8 69.8 68.8 70.8 70.8 Al₂O₃ 15.0 14.0 16.0 14.0 16.0 15.0 15.0 14.0 B₂O₃ 0..0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 4.7 5.0 4.7 5.3 5.0 5.3 3.3 3.5 CaO 2.3 2.5 2.3 2.7 2.5 2.7 4.7 5.0 SrO 2.3 2.5 2.3 2.7 2.5 2.7 0.0 0.0 BaO 4.7 5.0 4.7 5.3 5.0 5.3 6.1 6.5 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 85.8 84.8 85.8 83.8 84.8 83.8 85.8 84.8 [MgO] + [CaO] + [SrO] + [BaO] 14.0 15.0 14.0 16.0 15.0 16.0 14.0 15.0 [SrO] + [BaO] 7.0 7.5 7.0 8.0 7.5 8.0 6.1 6.5 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − 5.7 4.0 6.7 3.3 6.0 4.3 4.3 2.5 [ CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 418.5 414.3 431.5 423.1 440.3 436.1 402.1 396.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,806.0 1,797.1 1,811.3 1,793.6 1,807.7 1,798.9 1,805.7 1,796.8 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 37.0 38.7 36.7 40.2 38.5 40.2 38.1 39.8 (10⁻⁷/° C.) Density (g/cm³) 2.667 2.682 2.676 2.706 2.700 2.716 2.677 2.692 Strain point (° C.) 781 774 782 769 779 773 784 777 Annealing point (° C.) 841 834 842 828 838 832 845 837 Softening point (° C.) 1,077 1,072 1,073 1,062 1,068 1,062 1,081 1,075 10^(4.5) dPa · s (° C.) 1,400 1,396 1,385 1,381 1,375 1,369 1,403 1,401 10^(4.0) dPa · s (° C.) 1,559 1,555 1,540 1,539 1,528 1,525 1,563 1,562 10^(3.0) dPa · s (° C.) 1,660 1,657 1,637 1,639 1,626 1,623 1,664 1,667 10^(2.5) dPa · s (° C.) 1,338 1,334 1,325 1,320 1,316 1,310 1,341 1,338 Young's modulus (GPa) 84.5 83.7 85.5 83.5 85.5 84.6 83.6 82.5 Specific Young's modulus 31.7 31.2 31.9 30.9 31.7 31.2 31.2 30.6 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.06 0.11 0.10 0.15 0.13 0.03 0.09 0.06 No. No. No. No. No. No. 107 108 109 110 111 112 mol % SiO₂ 69.8 69.8 68.8 68.8 71.8 71.8 Al₂O₃ 16.0 14.0 16.0 15.0 14.0 13.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 1.0 MgO 3.3 3.7 3.5 3.7 4.7 5.0 CaO 4.7 5.3 5.0 5.3 2.3 2.5 SrO 0.0 0.0 0.0 0.0 2.3 2.5 BaO 6.1 6.9 6.5 6.9 4.7 5.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 85.8 83.8 84.8 83.8 85.8 84.8 [MgO] + [CaO] + [SrO] + [BaO] 14.0 16.0 15.0 16.0 14.0 15.0 [SrO] + [BaO] 6.1 6.9 6.5 6.9 7.0 7.5 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − 5.3 1.7 4.5 2.7 4.7 3.0 [ CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 415.1 404.5 422.8 417.5 405.5 401.3 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,810.0 1,793.2 1,807.4 1,798.5 1,800.7 1,791.8 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2 [ZnO] Thermal expansion coefficient 37.7 41.5 39.3 41.4 37.0 38.8 (10⁻⁷/° C.) Density (g/cm³) 2.687 2.718 2.711 2.726 2.658 2.674 Strain point (° C.) 787 770 783 776 780 772 Annealing point (° C.) 846 831 843 835 841 833 Softening point (° C.) 1,078 1,065 1,071 1,064 1,081 1,073 10^(4.5) dPa · s (° C.) 1,392 1,386 1,378 1,375 1,412 1,412 10^(4.0) dPa · s (° C.) 1,548 1,545 1,531 1,532 1,577 1,578 10^(3.0) dPa · s (° C.) 1,648 1,648 1,627 1,632 1,681 1,678 10^(2.5) dPa · s (° C.) 1,332 1,324 1,319 1,315 1,348 1,347 Young's modulus (GPa) 84.7 82.9 84.6 83.6 83.6 82.7 Specific Young's modulus 31.5 30.5 31.2 30.7 31.4 30.9 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.15 0.05 0.09 0.11 0.15 0.15

TABLE 9 No. No. No. No. No. No. No. No. 113 114 115 116 117 118 119 120 mol % SiO₂ 70.8 69.8 71.8 71.8 70.8 71.8 70.8 69.8 Al₂O₃ 13.0 13.0 14.0 13.0 13.0 14.0 14.0 14.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 5.3 5.7 3.3 3.5 3.7 7.0 7.5 8.0 CaO 2.7 2.8 4.7 5.0 5.3 0.0 0.0 0.0 SrO 2.7 2.8 0.0 0.0 0.0 7.0 7.5 8.0 BaO 5.3 5.7 6.1 6.5 6.9 0.0 0.0 0.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 83.8 82.8 85.8 84.8 83.8 85.8 84.8 83.8 [MgO] + [CaO] + [SrO] + [BaO] 16.0 17.0 14.0 15.0 16.0 14.0 15.0 16.0 [SrO] + [BaO] 8.0 8.5 6.1 6.5 6.9 7.0 7.5 8.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − 2.3 1.7 3.3 1.5 0.7 7.0 6.5 6.0 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 410.1 419.0 389.1 383.8 391.5 407.8 416.8 425.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,788.3 1,784.7 1,800.4 1,791.5 1,787.9 1,800.2 1,796.6 1,793.0 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 40.3 41.5 37.9 39.9 41.5 34.4 35.7 36.5 (10⁻⁷/° C.) Density (g/cm³) 2.698 2.724 2.668 2.685 2.710 2.584 2.601 2.621 Strain point (° C.) 766 761 782 772 765 780 777 773 Annealing point (° C.) 826 820 844 833 826 839 835 830 Softening point (° C.) 1,063 1,052 1,084 1,075 1,064 1,071 1,063 1,054 10^(4.5) dPa · s (° C.) 1,392 1,375 1,418 1,414 1,396 1,394 1,377 1,364 10^(4.0) dPa · s (° C.) 1,558 1,538 1,585 1,583 1,561 1,556 1,537 1,520 10^(3.0) dPa · s (° C.) 1,659 1,641 1,688 1,692 1,668 1,662 1,641 1,622 10^(2.5) dPa · s (° C.) 1,328 1,312 1,353 1,348 1,332 1,332 1,316 1,304 Young's modulus (GPa) 82.9 83.1 82.7 82.0 81.9 85.9 86.1 86.4 Specific Young's modulus 30.7 30.5 31.0 30.5 30.2 33.2 33.1 33.0 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.14 0.15 0.09 0.07 0.09 0.06 0.08 0.10 No. No. No. No. No. No. 121 122 123 124 125 126 mol % SiO₂ 68.8 67.8 71.8 71.8 70.8 70.3 Al₂O₃ 15.0 16.0 13.0 12.0 13.0 14.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 MgO 8.0 8.0 7.5 8.0 8.0 7.8 CaO 0.0 0.0 0.0 0.0 0.0 0.0 SrO 8.0 8.0 7.5 8.0 8.0 7.8 BaO 0.0 0.0 0.0 0.0 0.0 0.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 83.8 83.8 84.8 83.8 83.8 84.3 [MgO] + [CaO] + [SrO] + [BaO] 16.0 16.0 15.0 16.0 16.0 15.5 [SrO] + [BaO] 8.0 8.0 7.5 8.0 8.0 7.8 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − 7.0 8.0 5.5 4.0 5.0 6.3 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 438.8 451.8 403.8 399.8 412.8 421.3 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,798.3 1,803.6 1,791.3 1,782.4 1,787.7 1,794.8 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 36.7 37.0 35.6 37.1 37.0 36.4 (10⁻⁷/° C.) Density (g/cm³) 2.630 2.640 2.592 2.602 2.611 2.612 Strain point (° C.) 775 777 772 764 767 772 Annealing point (° C.) 832 833 830 822 825 829 Softening point (° C.) 1,052 1,049 1,065 1,057 1,055 1,058 10^(4.5) dPa · s (° C.) 1,355 1,343 1,389 1,382 1,372 1,368 10^(4.0) dPa · s (° C.) 1,509 1,492 1,549 1,544 1,531 1,524 10^(3.0) dPa · s (° C.) 1,607 1,587 1,652 1,649 1,633 1,623 10^(2.5) dPa · s (° C.) 1,296 1,286 1,327 1,319 1,311 1,308 Young's modulus (GPa) 87.4 88.4 85.3 84.6 85.4 86.2 Specific Young's modulus 33.2 33.5 32.9 32.5 32.7 33.0 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.12 0.03 0.04 0.11 0.09 0.15

TABLE 10 No. No. No. No. No. No. No. No. 127 128 129 130 131 132 133 134 mol % SiO₂ 69.8 71.8 70.8 69.8 71.8 70.8 69.8 67.8 Al₂O₃ 14.5 13.5 14.5 14.5 13.5 14.5 15.5 15.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 7.8 4.8 4.8 5.2 3.4 3.4 3.4 7.5 CaO 0.0 2.4 2.4 2.6 4.8 4.8 4.8 0.0 SrO 7.8 2.4 2.4 2.6 0.0 0.0 0.0 7.5 BaO 0.0 4.8 4.8 5.2 6.3 6.3 6.3 0.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 2.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 84.3 85.3 85.3 84.3 85.3 85.3 85.3 82.8 [MgO] + [CaO] + [SrO] + [BaO] 15.5 14.5 14.5 15.5 14.5 14.5 14.5 15.0 [SrO] + [BaO] 7.8 7.3 7.3 7.8 6.3 6.3 6.3 7.5 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − 6.8 3.8 4.8 4.2 2.4 3.4 4.4 7.5 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 427.8 403.4 416.4 425.2 386.5 399.5 412.5 427.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,797.5 1,796.3 1,801.6 1,798.0 1,795.9 1,801.2 1,806.5 1,780.7 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 36.3 38.1 37.7 39.0 38.9 38.9 38.5 36.5 (10⁻⁷/° C.) Density (g/cm³) 2.617 2.665 2.675 2.699 2.676 2.686 2.694 2.662 Strain point (° C.) 773 774 776 772 776 779 780 757 Annealing point (° C.) 831 835 836 832 837 839 841 812 Softening point (° C.) 1,056 1,077 1,075 1,065 1,080 1,078 1,075 1,031 10^(4.5) dPa · s (° C.) 1,364 1,408 1,399 1,383 1,412 1,401 1,392 1,331 10^(4.0) dPa · s (° C.) 1,518 1,570 1,559 1,543 1,576 1,561 1,549 1,481 10^(3.0) dPa · s (° C.) 1,616 1,672 1,661 1,643 1,680 1,662 1,649 1,577 10^(2.5) dPa · s (° C.) 1,305 1,345 1,337 1,322 1,348 1,339 1,331 1,273 Young's modulus (GPa) 86.4 83.1 83.9 84.0 82.1 83.0 83.7 88.1 Specific Young's modulus 33.0 31.2 31.4 31.1 30.7 30.9 31.1 33.1 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.09 0.07 0.12 0.03 0.14 0.14 0.11 0.13 No. No. No. No. No. No. 135 136 137 138 139 140 mol % SiO₂ 65.8 69.8 69.8 67.8 65.8 69.8 Al₂O₃ 15.0 15.0 15.0 15.0 15.0 15.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 MgO 7.5 6.5 5.5 0.0 0.0 0.0 CaO 0.0 0.0 0.0 10.0 10.0 9.0 SrO 7.5 6.5 5.5 0.0 0.0 0.0 BaO 0.0 0.0 0.0 5.0 5.0 4.0 ZnO 4.0 2.0 4.0 2.0 4.0 2.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 80.8 84.8 84.8 82.8 80.8 84.8 [MgO] + [CaO] + [SrO] + [BaO] 15.0 13.0 11.0 15.0 15.0 13.0 [SrO] + [BaO] 7.5 6.5 5.5 5.0 5.0 4.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − 7.5 8.5 9.5 0.0 0.0 2.0 [CaO] − [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 425.8 409.8 389.8 367.8 365.8 352.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 3.7 1,759.5 1,787.9 1,773.9 1,783.7 1,762.5 1,790.2 [B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 37.5 33.6 31.9 42.2 43.0 38.7 (10⁻⁷/° C.) Density (g/cm³) 2.710 2.623 2.631 2.715 2.763 2.659 Strain point (° C.) 742 762 751 763 742 770 Annealing point (° C.) 796 820 808 820 796 830 Softening point (° C.) 1,008 1,046 1,035 1,045 1,015 1,061 10^(4.5) dPa · s (° C.) 1,295 1,354 1,346 1,349 1,311 1,373 10^(4.0) dPa · s (° C.) 1,440 1,509 1,500 1,501 1,459 1,529 10^(3.0) dPa · s (° C.) 1,536 1,607 1,599 1,600 1,555 1,629 10^(2.5) dPa · s (° C.) 1,240 1,295 1,286 1,291 1,254 1,313 Young's modulus (GPa) 88.9 87.6 88.2 83.8 85.3 84.1 Specific Young's modulus 32.8 33.4 33.5 30.9 30.9 31.6 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.06 0.07 0.08 0.10 0.09 0.07

TABLE 11 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 141 142 143 144 145 146 147 148 149 150 151 152 153 154 mol SiO₂ 69.8 69.8 70.8 70.8 69.8 69.8 68.8 68.8 68.9 68.9 68.9 68.9 70.5 69.5 % Al₂O₃ 15.0 11.4 11.4 10.4 12.4 10.4 12.4 11.4 13.6 13.6 14.1 14.6 13.1 13.1 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 3.4 2.4 3.4 2.4 0.3 0.3 MgO 0.0 9.3 8.3 9.3 8.3 10.3 9.3 10.3 1.7 1.7 1.7 1.7 6.1 7.1 CaO 8.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 9.4 10.4 8.4 8.4 3.8 3.8 SrO 0.0 9.3 9.3 9.3 9.3 9.3 9.3 9.3 1.6 1.6 1.6 1.6 2.1 2.1 BaO 3.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 1.2 1.2 1.7 2.2 3.9 3.9 ZnO 4.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 84.8 81.2 82.2 81.2 82.2 80.2 81.2 80.2 82.5 82.5 83.0 83.5 83.6 82.6 [MgO] + [CaO] + [SrO] + [BaO] 11.0 18.6 17.6 18.6 17.6 19.6 18.6 19.6 13.9 14.9 13.4 13.9 15.9 16.9 [SrO] + [BaO] 3.0 9.3 9.3 9.3 9.3 9.3 9.3 9.3 2.8 2.8 3.3 3.8 6.0 6.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 1.2 0.9 1.0 0.6 0.1 0.1 [Al₂O₃] + [B₂O₃] − [CaO] − 4.0 2.1 2.1 1.1 3.1 1.1 3.1 2.1 4.8 2.8 5.8 4.8 3.6 3.6 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 335.8 415.4 410.4 402.4 423.4 407.4 428.4 420.4 269.5 285.5 283.5 313.5 381.6 386.6 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,775.5 1,769.9 1,774.8 1,764.6 1,780.1 1,759.7 1,775.2 1,765.0 1,750.4 1,760.8 1,755.4 1,770.7 1,781.9 1,770.0 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 35.7 40.5 39.9 40.9 39.9 42.5 40.2 41.2 37.4 38.9 37.0 37.5 38.5 39.1 (10⁻⁷/° C.) Density (g/cm³) 2.653 2.649 2.638 2.644 2.670 2.671 2.659 2.662 2.528 2.546 2.543 2.572 2.644 2.655 Strain point (° C.) 754 754 758 750 761 743 757 749 736 745 740 752 761 755 Annealing point (° C.) 812 809 814 805 818 797 812 804 795 803 799 812 819 812 Softening point (° C.) 1,043 1,033 1,042 1,031 1,043 1,015 1,032 1,023 1,028 1,032 1,033 1,043 1,054 1,043 10^(4.5) dPa · s (° C.) 1,355 1,343 1,361 1,348 1,356 1,318 1,338 1,326 1,339 1,341 1,346 1,354 1,377 1,356 10^(4.0) dPa · s (° C.) 1,512 1,503 1,524 1,510 1,516 1,476 1,494 1,483 1,499 1,498 1,504 1,510 1,540 1,515 10^(3.0) dPa · s (° C.) 1,613 1,607 1,627 1,616 1,619 1,580 1,594 1,585 1,602 1,598 1,606 1,610 1,643 1,617 10^(2.5) dPa · s (° C.) 1,295 1,283 1,299 1,286 1,295 1,259 1,278 1,267 1,279 1,281 1,286 1,294 1,315 1,296 Young's modulus (GPa) 85.6 84.7 84.0 83.8 85.0 84.8 85.6 85.5 85.9 81.9 80.7 81.9 83.9 84.6 Specific Young's modulus 32.3 32.0 31.8 31.7 31.8 31.8 32.2 32.1 34.0 32.2 31.7 31.9 30.7 31.9 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.05 0.08 0.04 0.08 0.14 0.05 0.11 0.09 0.14 0.04 0.05 0.09 0.11 0.13

TABLE 12 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 155 156 157 158 159 160 161 162 163 164 165 166 167 168 mol SiO₂ 68.5 69.5 68.5 69.8 68.8 69.8 69.8 69.8 69.8 69.8 68.8 68.8 68.8 68.8 % Al₂O₃ 13.1 14.1 14.1 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 B₂O₃ 0.3 0.3 0.3 1.0 2.0 1.0 1.0 1.0 1.0 1.0 2.0 2.0 2.0 2.0 MgO 8.1 6.1 7.1 7.5 7.5 7.5 7.5 7.5 7.5 7.5 7.5 7.5 7.5 7.5 CaO 3.8 3.8 3.8 0.0 0.0 1.0 0.0 2.0 1.0 0.0 1.0 0.0 2.0 1.0 SrO 2.1 2.1 2.1 7.5 7.5 6.5 6.5 5.5 5.5 5.5 6.5 6.5 5.5 5.5 BaO 3.9 3.9 3.9 0.0 0.0 0.0 1.0 0.0 1.0 2.0 0.0 1.0 0.0 1.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 81.6 83.6 82.6 83.8 82.8 83.8 83.8 83.8 83.8 83.8 82.8 82.8 82.8 82.8 [MgO] + [CaO] + [SrO] + [BaO] 17.9 15.9 16.9 15.0 15.0 15.0 15.0 15.0 15.0 15.0 15.0 15.0 15.0 15.0 [SrO] + [BaO] 6.0 6.0 6.0 7.5 7.5 6.5 7.5 5.5 6.5 7.5 6.5 7.5 5.5 6.5 [B₂O₃]/([SrO] + [BaO]) 0.1 0.1 0.1 0.1 0.3 0.2 0.1 0.2 0.2 0.1 0.3 0.3 0.4 0.3 [Al₂O₃] + [B₂O₃] − [CaO] − 3.6 4.6 7.5 8.5 7.5 7.5 7.5 7.5 7.5 7.5 8.5 8.5 8.5 8.5 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 391.6 394.6 399.6 400.8 384.8 387.8 402.8 374.8 389.8 404.8 371.8 386.8 358.8 373.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,772.1 1,787.2 1,782.3 1,782.5 1,768.4 1,781.1 1,782.0 1,779.7 1,780.6 1,781.5 1,767.0 1,767.9 1,765.6 1,766.5 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 39.6 37.9 38.8 35.4 35.8 35.3 35.3 35.1 35.5 36.4 35.7 36.2 35.3 35.6 (10⁻⁷/° C.) Density (g/cm³) 2.667 2.653 2.664 2.595 2.590 2.581 2.609 2.566 2.594 2.625 2.575 2.602 2.561 2.589 Strain point (° C.) 750 765 759 762 750 760 761 760 760 761 748 748 746 746 Annealing point (° C.) 807 822 816 820 807 817 819 816 817 819 805 806 803 804 Softening point (° C.) 1,033 1,052 1,042 1,047 1,032 1,045 1,048 1,043 1,047 1,050 1,031 1,033 1,029 1,032 10^(4.5) dPa · s (° C.) 1,337 1,364 1,347 1,365 1,341 1,357 1,364 1,355 1,361 1,370 1,343 1,345 1,339 1,340 10^(4.0) dPa · s (° C.) 1,492 1,522 1,503 1,527 1,496 1,512 1,523 1,513 1,519 1,528 1,497 1,501 1,494 1,497 10^(3.0) dPa · s (° C.) 1,590 1,623 1,602 1,629 1,595 1,610 1,622 1,612 1,617 1,627 1,596 1,602 1,592 1,596 10^(2.5) dPa · s (° C.) 1,278 1,304 1,288 1,303 1,281 1,297 1,303 1,295 1,301 1,308 1,283 1,285 1,279 1,281 Young's modulus (GPa) 85.4 84.9 85.6 85.0 84.0 85.5 84.7 85.9 85.2 84.4 84.5 83.8 84.9 84.6 Specific Young's modulus 32.0 32.0 32.1 32.7 32.4 33.1 32.5 33.5 32.8 32.1 32.8 32.2 33.1 32.5 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.12 0.06 0.07 0.09 0.03 0.11 0.13 0.03 0.08 0.06 0.09 0.15 0.08 0.12

TABLE 13 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 169 170 171 172 173 174 175 176 177 178 179 180 181 182 mol SiO₂ 68.8 70.2 69.8 69.8 69.8 68.9 68.9 68.9 68.9 70.0 69.5 70.2 69.7 68.9 % Al₂O₃ 14.0 12.9 12.9 12.9 12.9 13.6 13.6 13.6 13.6 13.1 13.1 12.9 12.9 13.6 B₂O₃ 2.0 0.3 0.3 0.3 0.3 3.4 2.4 3.4 2.4 0.3 0.3 0.0 0.0 3.9 MgO 7.5 6.3 6.5 7.0 6.5 2.2 2.7 2.7 3.2 6.1 6.4 6.4 6.4 1.7 CaO 0.0 3.9 4.0 4.0 4.5 8.4 8.4 7.4 7.4 3.8 3.8 3.8 3.8 8.4 SrO 5.5 2.2 2.2 1.7 1.7 1.6 1.6 1.6 1.6 2.1 2.1 2.1 2.1 1.6 BaO 2.0 4.0 4.1 4.1 4.1 1.7 2.2 2.2 2.7 3.9 3.9 3.9 3.9 1.2 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.5 1.0 0.5 1.0 0.5 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 82.8 83.1 82.7 82.7 82.7 82.5 82.5 82.5 82.5 83.1 82.6 83.1 82.6 82.5 [MgO] + [CaO] + [SrO] + [BaO] 15.0 16.4 16.8 16.8 16.8 13.9 14.9 13.9 14.9 15.9 15.9 16.2 16.2 12.9 [SrO] + [BaO] 7.5 6.2 6.3 5.8 5.8 3.3 3.8 3.8 4.3 6.0 6.0 6.0 6.0 2.8 [B₂O₃]/([SrO] + [BaO]) 0.3 0.0 0.0 0.1 0.1 1.0 0.6 0.9 0.6 0.1 0.1 0.0 0.0 1.4 [Al₂O₃] + [B₂O₃] − [CaO] − 8.5 3.1 2.9 3.4 2.9 5.3 3.8 5.8 4.3 3.6 3.6 3.1 3.1 6.3 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 388.8 382.8 385.3 381.3 378.8 279.5 305.5 289.5 315.5 381.1 380.6 384.8 384.3 261.0 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,767.4 1,779.0 1,777.4 1,776.1 1,776.7 1,750.3 1,760.5 1,750.1 1,760.4 1,776.6 1,771.3 1,778.3 1,773.0 1,741.8 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 36.4 39.2 39.9 39.3 39.7 37.4 38.6 37.4 38.7 39.0 38.9 39.2 39.2 36.1 (10⁻⁷/° C.) Density (g/cm³) 2.618 2.654 2.661 2.653 2.653 2.540 2.571 2.552 2.586 2.657 2.668 2.659 2.672 2.523 Strain point (° C.) 748 756 753 754 754 734 741 733 740 754 750 757 752 726 Annealing point (° C.) 806 814 812 812 812 793 800 792 799 813 807 814 809 785 Softening point (° C.) 1,035 1,048 1,043 1,043 1,043 1,027 1,031 1,027 1,032 1,045 1,038 1,046 1,039 1,022 10^(4.5) dPa · s (° C.) 1,347 1,367 1,361 1,359 1,358 1,342 1,343 1,344 1,344 1,364 1,354 1,366 1,356 1,342 10^(4.0) dPa · s (° C.) 1,503 1,529 1,524 1,519 1,518 1,499 1,503 1,503 1,504 1,525 1,512 1,525 1,513 1,502 10^(3.0) dPa · s (° C.) 1,602 1,633 1,629 1,622 1,620 1,599 1,604 1,605 1,606 1,629 1,613 1,627 1,616 1,605 10^(2.5) dPa · s (° C.) 1,287 1,305 1,299 1,298 1,297 1,282 1,283 1,283 1,284 1,302 1,293 1,304 1,295 1,281 Young's modulus (GPa) Unmea- 84.1 84.1 84.4 84.1 80.7 81.9 80.8 81.8 84.2 84.6 84.6 84.9 80.3 sured Specific Young's modulus Unmea- 31.7 31.6 31.8 31.7 31.8 31.9 31.7 31.6 31.7 31.7 31.8 31.8 31.8 (GPa/g · cm⁻³) sured β-OH (mm⁻¹) 0.12 0.10 0.10 0.06 0.08 0.14 0.07 0.09 0.11 0.07 0.14 0.03 0.08 0.05

TABLE 14 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 183 184 185 186 187 188 189 190 191 192 193 194 195 196 mol SiO₂ 68.9 70.0 69.5 69.8 69.8 69.8 69.8 69.4 69.9 68.9 68.9 68.9 68.9 70.1 % Al₂O₃ 13.6 13.4 13.7 13.1 13.1 13.1 13.1 13.6 13.6 14.0 14.0 14.0 14.0 12.8 B₂O₃ 3.4 0.5 0.7 1.0 1.0 1.0 1.0 3.4 3.4 3.0 3.0 3.0 3.0 0.5 MgO 1.7 6.1 6.1 6.1 6.1 6.1 6.6 2.7 2.7 3.2 3.7 2.7 3.2 6.1 CaO 8.4 3.8 3.8 4.3 4.3 4.8 4.3 6.9 6.4 6.9 6.4 6.9 6.4 4.8 SrO 1.6 2.1 2.1 2.1 1.6 1.6 1.6 1.6 1.6 1.6 1.6 2.1 2.1 1.6 BaO 1.2 3.9 3.9 3.4 3.9 3.4 3.4 2.2 2.2 2.2 2.2 2.2 2.2 3.9 ZnO 1.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 82.5 83.4 83.2 82.9 82.9 82.9 82.9 83.0 83.5 82.9 82.9 82.9 82.9 82.9 [MgO] + [CaO] + [SrO] + [BaO] 12.9 15.9 15.9 15.9 15.9 15.9 15.9 13.4 12.9 13.9 13.9 13.9 13.9 16.4 [SrO] + [BaO] 2.8 6.0 6.0 5.5 5.5 5.0 5.0 3.8 3.8 3.8 3.8 4.3 4.3 5.5 [B₂O₃]/([SrO] + [BaO]) 1.2 0.1 0.1 0.2 0.2 0.2 0.2 0.9 0.9 0.8 0.8 0.7 0.7 0.1 [Al₂O₃] + [B₂O₃] − [CaO] − 5.8 4.1 4.6 4.3 4.3 4.3 4.8 6.3 6.8 6.3 6.8 5.8 6.3 3.0 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 268.5 382.3 383.3 362.9 363.9 356.4 358.9 289.5 289.5 303.6 306.1 307.6 310.1 368.0 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,743.5 1,780.7 1,779.5 1,771.6 1,771.4 1,770.9 1,770.3 1,752.0 1,753.8 1,757.3 1,756.7 1,758.6 1,758.0 1,775.0 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 36.3 38.4 38.5 38.1 38.3 38.0 37.6 36.2 35.4 36.7 36.2 37.2 37.0 39.1 (10⁻⁷/° C.) Density (g/cm³) 2.539 2.644 2.648 2.624 2.632 2.617 2.616 2.549 2.542 2.558 2.559 2.568 2.568 2.640 Strain point (° C.) 725 758 756 750 750 750 750 734 737 738 737 740 738 753 Annealing point (° C.) 784 816 814 808 809 808 808 794 797 797 796 799 797 810 Softening point (° C.) 1,020 1,049 1,046 1,041 1,042 1,040 1,040 1,031 1,035 1,031 1,029 1,033 1,031 1,043 10^(4.5) dPa · s (° C.) 1,340 1,368 1,363 1,358 1,361 1,360 1,355 1,350 Unmea- Unmea- 1,340 1,346 1,341 1,363 sured sured 10^(4.0) dPa · s (° C.) 1,498 1,528 1,520 1,517 1,523 1,522 1,513 1,508 Unmea- Unmea- 1,499 1,506 1,498 1,526 sured sured 10^(3.0) dPa · s (° C.) 1,599 1,630 1,619 1,622 1,628 1,626 1,614 1,612 Unmea- Unmea- 1,599 1,605 1,600 1,630 sured sured 10^(2.5) dPa · s (° C.) 1,279 1,307 1,302 1,297 1,299 1,298 1,294 1,289 Unmea- Unmea- 1,280 1,280 1,282 1,301 sured sured Young's modulus (GPa) 81.2 84.1 84.4 83.6 83.3 83.8 83.9 80.4 80.2 81.6 82.0 81.3 81.4 84.0 Specific Young's modulus 32.0 31.8 31.9 31.9 31.7 32.0 32.1 31.5 31.6 31.9 32.0 31.7 31.7 31.8 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.13 0.06 0.05 0.12 0.07 0.11 0.12 0.10 0.13 0.04 0.03 0.06 0.06 0.10

TABLE 15 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 197 198 199 200 201 202 203 204 205 206 207 208 209 210 mol SiO₂ 70.1 70.1 70.1 70.1 69.6 70.1 70.1 70.1 70.1 701 70.1 70.1 69.3 69.7 % Al₂O₃ 12.8 12.8 12.8 12.8 12.8 12.8 12.8 12.8 12.8 12.8 12.8 12.8 13.6 13.6 B₂O₃ 0.0 0.0 0.0 0.0 0.5 0.7 0.4 1.0 0.7 0.7 0.7 0.6 3.0 2.6 MgO 6.1 5.6 5.1 4.6 5.1 5.9 5.7 5.6 5.7 5.3 5.7 5.9 3.2 3.7 CaO 5.3 6.3 7.3 8.3 7.3 4.6 4.6 5.5 5.6 6.0 5.7 5.3 6.9 6.4 SrO 1.6 1.1 0.6 0.0 0.6 1.3 1.3 0.9 1.0 0.4 1.2 1.4 1.1 0.6 BaO 3.9 3.9 3.9 4.0 3.9 3.9 3.9 3.9 3.9 4.5 3.6 3.7 2.7 3.2 ZnO 0.0 0.0 0.0 0.0 0.0 0.5 1.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 82.9 82.9 82.9 82.9 82.4 82.9 82.9 82.9 82.9 82.9 82.9 82.9 82.9 83.3 [MgO] + [CaO] + [SrO] + [BaO] 16.9 16.9 16.9 16.9 16.9 15.7 15.5 15.9 16.2 16.2 16.2 16.3 13.9 13.9 [SrO] + [BaO] 5.5 5.0 4.5 4.0 4.5 5.2 5.2 4.8 4.9 4.9 4.8 5.1 3.8 3.8 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.1 0.1 0.1 0.2 0.1 0.1 0.1 0.1 0.8 0.7 [Al₂O₃] + [B₂O₃] − [CaO] − 2.0 1.5 1.0 0.5 1.5 3.7 3.4 3.5 3.0 2.6 3.0 3.0 5.9 6.0 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 376.0 367.0 358.0 349.2 350.0 359.4 362.7 348.4 355.0 354.2 353.1 359.8 299.4 309.3 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,780.2 1,780.1 1,780.0 1,779.8 1,772.9 1,769.3 1,769.2 1,769.4 1,772.5 1,772.7 1,772.6 1,773.7 1,754.9 1,759.7 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 39.5 39.9 40.2 40.4 40.1 38.0 38.2 38.4 39.2 39.2 39.1 38.8 37.3 36.9 (10⁻⁷/° C.) Density (g/cm³) 2.649 2.643 2.636 2.632 2.634 2.637 2.649 2.618 2.627 2.638 2.621 2.628 2.561 2.572 Strain point (° C.) 758 758 758 759 749 748 746 745 750 750 750 750 736 740 Annealing point (° C.) 816 815 815 816 806 806 804 804 808 809 808 808 794 799 Softening point (° C.) 1,045 1,045 1,044 1,045 1,036 1,040 1,040 1,039 1,041 1,042 1,041 1,042 1,030 1,035 10^(4.5) dPa · s (° C.) 1,365 1,362 1,361 1,362 1,355 1,363 1,356 1,358 1,357 1,360 1,357 1,359 1,358 1,358 10^(4.0) dPa · s (° C.) 1,526 1,522 1,521 1,523 1,515 1,525 1,516 1,518 1,519 1,521 1,520 1,518 1,518 1,524 10^(3.0) dPa · s (° C.) 1,629 1,625 1,623 1,625 1,618 1,628 1,618 1,621 1,622 1,623 1,625 1,620 1,625 1,631 10^(2.5) dPa · s (° C.) 1,303 1,301 1,300 1,301 1,293 1,301 1,295 1,297 1,296 1,299 1,296 1,298 1,295 1,295 Young's modulus (GPa) 84.5 84.6 84.4 84.2 84.0 84.0 84.4 83.3 83.4 83.4 83.6 84.0 80.9 81.5 Specific Young's modulus 31.9 32.0 32.0 32.0 31.9 31.9 31.9 31.8 31.7 31.6 31.9 31.9 31.6 31.7 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.12 0.07 0.03 0.11 0.12 0.13 0.10 0.08 0.07 0.06 0.09 0.12 0.14 0.03

TABLE 16 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 211 212 213 214 215 216 217 218 219 220 221 222 223 224 mol SiO₂ 70.1 69.7 70.3 70.3 63.7 72.9 63.1 70.3 70.5 70.4 72.9 70.4 70.5 70.3 % Al₂O₃ 13.6 13.6 12.8 12.8 18.0 11.3 18.0 12.8 12.5 12.5 11.6 12.6 12.4 12.6 B₂O₃ 2.2 2.1 0.7 0.7 1.1 0.3 1.7 0.7 0.7 1.0 0.3 0.7 0.7 0.8 MgO 4.2 3.7 5.3 5.3 6.0 3.1 6.0 5.1 5.7 3.3 2.8 5.1 5.1 5.7 CaO 5.9 6.4 6.0 6.0 9.0 7.2 9.0 6.2 4.4 7.6 7.2 6.2 6.2 4.4 SrO 0.1 1.1 0.4 0.2 0.0 0.5 0.0 0.4 2.1 0.4 0.5 0.4 0.4 2.1 BaO 3.7 3.2 4.3 4.5 2.0 4.5 2.0 4.3 3.9 4.6 4.5 4.4 4.5 3.9 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 83.7 83.3 83.1 83.1 81.7 84.2 81.1 83.1 83.0 82.9 84.5 83.0 82.9 82.9 [MgO] + [CaO] + [SrO] + [BaO] 13.9 14.4 16.0 16.0 17.0 15.3 17.0 16.0 16.1 15.9 15.0 16.1 16.2 16.1 [SrO] + [BaO] 3.8 4.3 4.7 4.7 2.0 5.0 2.0 4.7 6.0 5.0 5.0 4.8. 4.9 6.0 [B₂O₃]/([SrO] + [BaO]) 0.6 0.5 0.1 0.1 0.6 0.1 0.9 0.1 0.1 0.2 0.1 0.1 0.1 0.1 [Al₂O₃] + [B₂O₃] − [CaO] − 6.1 5.0 2.8 2.8 8.1 −0.6 8.7 2.6 2.8 0.9 −0.3 2.3 2.0 3.0 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 319.2 323.8 351.2 351.6 376.2 331.4 366.6 350.2 365.4 337.0 333.8 349.1 348.0 365.1 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,764.5 1,765.6 1,773.3 1,773.2 1,788.0 1,776.5 1,779.6 1,773.5 1,772.9 1,770.5 1,779.6 1,772.2 1,770.8 1,772.0 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 35.6 37.7 39.0 39.1 Unmea- Unmea- Unmea- 39.5 39.3 40.5 Unmea- 39.1 39.9 39.2 (10⁻⁷/° C.) sured sured sured sured Density (g/cm³) 2.580 2.589 2.629 2.631 Unmea- Unmea- Unmea- 2.629 2.939 2.637 Unmea- 2.632 2.635 2.640 sured sured sured sured Strain point (° C.) 744 744 750 751 761 753 752 749 748 742 754 744 744 744 Annealing point (° C.) 804 804 809 809 815 814 805 807 805 801 815 804 803 803 Softening point (° C.) 1,041 1,039 1,043 1,044 1,021 1,059 1,011 1,043 1,044 1,040 1,062 1,042 1,041 1,041 10^(4.5) dPa · s (° C.) 1,363 1,361 1,362 1,362 1,285 1,393 1,278 1,364 1,367 1,366 1,405 1,363 1,365 1,365 10^(4.0) dPa · s (° C.) 1,524 1,521 1,524 1,524 1,423 1,566 1,412 1,525 1,530 1,531 1,578 1,527 1,528 1,528 10^(3.0) dPa · s (° C.) 1,629 1,624 1,628 1,628 1,511 1,675 1,500 1,627 1,633 1,636 1,693 1,632 1,633 1,633 10^(2.5) dPa · s (° C.) 1,301 1,299 1,300 1,301 1,234 1,328 1,277 1,302 1,305 1,303 1,339 1,301 1,303 1,303 Young's modulus (GPa) 81.7 81.7 83.1 83.0 Unmea- Unmea- Unmea- 83.1 93.0 91.5 Unmea- 83.1 82.9 83.3 sured sured sured sured Specific Young's modulus 31.7 31.6 31.6 31.5 Unmea- Unmea- Unmea- 31.6 31.5 30.9 Unmea- 31.6 31.5 31.5 (GPa/g · cm⁻³) sured sured sured sured β-OH (mm⁻¹) 0.03 0.15 0.11 0.13 0.03 0.15 0.12 0.04 0.10 0.15 0.15 0.08 0.13 0.10

TABLE 17 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 225 226 227 228 229 230 231 232 233 234 235 236 237 238 mol SiO₂ 70.1 70.1 70.2 70.1 70.0 69.6 70.2 69.4 69.4 69.4 69.4 69.4 69.4 69.4 % Al₂O₃ 12.7 12.7 12.8 12.7 12.6 12.8 12.0 13.6 13.6 13.1 13.1 13.6 13.6 13.6 B₂O₃ 0.9 0.7 0.7 0.8 0.7 0.9 0.8 2.4 2.4 2.4 2.4 2.4 1.9 1.9 MgO 5.7 5.1 5.0 5.6 5.7 4.9 3.0 2.7 2.7 2.7 2.2 2.7 3.2 3.2 CaO 4.4 6.2 6.2 4.6 4.4 6.3 7.6 7.2 7.2 7.2 7.7 6.7 7.2 6.7 SrO 2.1 0.5 0.3 2.1 2.2 0.3 1.0 1.6 0.3 0.3 0.3 0.3 0.3 0.3 BaO 3.9 4.5 4.6 3.9 4.2 5.0 5.2 2.9 4.2 4.7 4.7 4.7 4.2 4.7 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 82.8 82.8 83.0 82.8 82.6 82.4 82.2 83.0 83.0 82.5 82.5 83.0 83.0 83.0 [MgO] + [CaO] + [SrO] + [BaO] 16.1 15.3 16.1 16.2 16.5 16.5 16.8 14.4 14.4 14.9 14.9 14.4 14.9 14.9 [SrO] + [BaO] 6.0 5.0 4.9 6.0 6.4 5.3 6.2 4.5 4.5 5.0 5.0 5.0 4.5 5.0 [B₂O₃]/([SrO] + [BaO]) 0.2 0.1 0.1 0.1 0.1 0.2 0.1 0.5 0.5 0.5 0.5 0.5 0.4 0.4 [Al₂O₃] + [B₂O₃] − [CaO] − 3.2 2.2 2.4 2.9 2.5 2.1 −1.0 4.3 4.3 3.3 2.8 4.3 3.8 3.8 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 364.8 353.2 352.9 365.9 372.5 355.2 349.0 316.0 318.6 319.6 317.1 326.1 329.1 336.6 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,771.1 1,772.2 1,773.4 1,772.3 1,772.3 1,769.6 1,769.1 1,763.0 1,762.4 1,758.3 1,758.9 1,762.8 1,767.0 1,767.4 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 39.4 39.5 39.2 39.3 40.0 40.5 42.8 38.1 38.4 39.6 40.0 38.7 38.8 38.9 (10⁻⁷/° C.) Density (g/cm³) 2.640 2.640 2.639 2.642 2.656 2.655 2.675 2.586 2.607 2.624 2.624 2.620 2.615 2.630 Strain point (° C.) 744 746 748 745 745 743 738 741 742 734 734 740 743 742 Annealing point (° C.) 803 804 806 804 803 802 796 800 802 794 794 800 802 802 Softening point (° C.) 1,040 1,040 1,042 1,041 1,040 1,035 1,032 1,037 1,038 1,033 1,033 1,038 1,038 1,039 10^(4.5) dPa · s (° C.) 1,362 1,361 1,361 1,362 1,363 1,356 1,360 1,358 1,363 1,356 1,357 1,360 1,361 1,363 10^(4.0) dPa · s (° C.) 1,524 1,524 1,524 1,524 1,526 1,518 1,527 1,519 1,525 1,521 1,522 1,522 1,526 1,525 10^(3.0) dPa · s (° C.) 1,629 1,627 1,627 1,628 1,631 1,618 1,632 1,625 1,629 1,624 1,627 1,628 1,640 1,628 10^(2.5) dPa · s (° C.) 1,300 1,299 1,299 1,300 1,301 1,294 1,296 1,296 1,300 1,294 1,294 1,298 1,298 1,301 Young's modulus (GPa) 83.3 83.2 83.1 83.2 83.0 82.5 81.2 81.2 80.7 80.1 79.9 80.5 81.6 81.3 Specific Young's modulus 31.6 31.5 31.5 31.5 31.3 31.1 30.4 31.4 31.0 30.5 30.4 30.7 31.2 30.9 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.05 0.08 0.07 0.09 0.03 0.08 0.09 0.09 0.10 0.08 0.15 0.08 0.14 0.07

TABLE 18 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 239 240 241 242 243 244 245 246 247 248 249 250 251 252 mol SiO₂ 69.4 71.3 72.3 72.3 72.3 72.3 72.3 72.3 72.3 71.3 71.3 71.3 71.8 71.3 % Al₂O₃ 13.1 10.7 10.7 10.7 10.7 10.7 11.7 11.7 11.7 11.7 11.7 11.7 10.7 10.7 B₂O₃ 1.9 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 3.7 0.0 0.0 1.0 1.0 2.0 1.0 2.0 3.0 1.0 2.0 3.0 1.0 1.0 CaO 6.7 11.5 11.5 11.5 10.5 9.5 10.5 9.5 8.5 10.5 9.5 8.5 11.5 11.5 SrO 0.3 1.3 0.3 0.3 0.3 0..3 0.3 0.3 0.3 0.3 0.3 0.3 0.8 1.3 BaO 4.7 5.0 5.0 4.0 5.0 5.0 4.0 4.0 4.0 5.0 5.0 5.0 4.0 4.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 82.5 82.0 83.0 83.0 83.0 83.0 84.0 84.0 84.0 83.0 83.0 83.0 82.5 82.0 [MgO] + [CaO] + [SrO] + [BaO] 15.4 17.8 16.8 16.8 16.8 16.8 15.8 15.8 15.8 16.8 16.8 16.8 17.3 17.8 [SrO] + [BaO] 5.0 6.3 5.3 4.3 5.3 5.3 4.3 4.3 4.3 5.3 5.3 5.3 4.8 5.3 [B₂O₃]/([SrO] + [BaO]) 0.4 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 3.3 −7.1 −6.1 −5.1 −5.1 −4.1 −3.1 −2.1 −1.1 −4.1 −3.1 −2.1 −5.6 −6.1 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 332.6 330.8 317.8 307.8 322.8 327.8 320.8 325.8 330.8 335.8 340.8 345.8 314.3 320.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,762.3 1,773.6 1,775.9 1,773.8 1,774.7 1,773.5 1,782.8 1,781.6 1,780.4 1,780.0 1,776.8 1,777.6 1,772.7 1,771.5 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 39.4 46.5 45.0 43.5 44.0 43.3 42.0 41.0 40.3 44.0 43.0 42.3 44.8 45.5 (10⁻⁷/° C.) Density (g/cm³) 2.630 2.697 2.666 2.631 2.661 2.659 2.623 2.620 2.616 2.668 2.665 2.662 2.645 2.661 Strain point (° C.) 736 744 750 750 747 746 764 760 759 755 753 752 743 743 Annealing point (° C.) 796 799 807 807 805 804 822 820 818 813 811 810 800 799 Softening point (° C.) 1,033 1,023 1,037 1,038 1,037 1,039 1,057 1,056 1,056 1,043 1,044 1,044 1,031 1,026 10^(4.5) dPa · s (° C.) 1,356 1,347 1,369 1,370 1,374 1,384 1,393 1,389 1,379 1,372 1,375 1,378 1,358 1,348 10^(4.0) dPa · s (° C.) 1,520 1,517 1,542 1,543 1,547 1,556 1,564 1,561 1,551 1,541 1,544 1,546 1,529 1,517 10^(3.0) dPa · s (° C.) 1,628 1,628 1,655 1,654 1,661 1,667 1,673 1,675 1,664 1,650 1,652 1,653 1,642 1,626 10^(2.5) dPa · s (° C.) 1,294 1,283 1,303 1,305 1,308 1,317 1,327 1,324 1,316 1,308 1,310 1,313 1,294 1,285 Young's modulus (GPa) 81.3 80.3 80.2 81.1 80.3 80.8 81.2 81.6 82.1 80.9 81.3 81.7 80.6 80.7 Specific Young's modulus 30.9 29.8 30.1 30.8 30.2 30.4 31.0 31.1 31.4 30.3 30.5 30.7 30.5 30.3 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.07 0.11 0.14 0.14 0.04 0.06 0.12 0.12 0.10 0.04 0.15 0.12 0.13 0.10

TABLE 19 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 253 254 255 256 257 258 259 260 261 262 263 264 265 266 mol SiO₂ 71.8 71.8 71.8 71.8 71.3 71.3 71.5 71.5 71.5 71.5 71.7 72.0 71.7 72.0 % Al₂O₃ 10.7 10.7 10.9 11.1 11.1 11.3 11.0 11.0 11.0 11.0 10.7 10.7 10.7 10.7 B₂O₃ 0.0 0.0 0.3 0.6 0.3 0.6 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 0.0 0.0 1.0 1.0 CaO 11.0 10.5 11.0 10.5 11.0 10.5 11.0 10.5 10.5 10.0 11.1 10.8 10.1 9.8 SrO 1.3 1.8 0.8 0.8 1.1 1.1 0.3 1.8 1.3 1.8 1.3 1.3 1.3 1.3 BaO 4.0 4.0 4.0 4.0 4.0 4.0 5.0 4.0 4.5 4.5 5.0 5.0 5.0 5.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 82.5 82.5 82.7 82.9 82.4 82.6 82.5 82.5 82.5 82.5 82.4 82.7 82.4 82.7 [MgO] + [CaO] + [SrO] + [BaO] 17.3 17.3 16.8 16.3 17.1 16.6 17.3 17.3 17.3 17.3 17.4 17.1 17.4 17.1 [SrO] + [BaO] 5.3 5.8 4.8 4.8 5.1 5.1 5.3 5.8 5.8 6.3 6.3 6.3 6.3 6.3 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.1 0.1 0.1 0.1 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − −5.6 −5.6 −4.6 −3.6 −4.7 −3.7 −5.3 −5.3 −5.3 −5.3 −6.7 −6.4 −5.7 −5.4 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 320.8 327.3 312.3 309.9 318.6 316.4 326.7 331.2 332.2 338.7 330.8 330.8 335.8 335.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,773.4 1,774.1 1,771.3 1,770.0 1,771.7 1,770.4 1,774.5 1,775.7 1,775.4 1,776.1 1,775.1 1,776.2 1,773.9 1,775.0 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 44.6 44.8 44.1 43.4 44.2 43.4 45.3 44.8 45.0 45.1 46.3 45.7 45.4 44.8 (10⁻⁷/° C.) Density (g/cm³) 2.654 2.661 2.638 2.631 2.650 2.641 2.672 2.662 2.671 2.679 2.690 2.686 2.686 2.681 Strain point (° C.) 745 744 743 740 741 740 747 746 744 747 745 746 742 742 Annealing point (° C.) 802 801 800 799 799 798 803 803 801 804 801 802 799 800 Softening point (° C.) 1,032 1,032 1,034 1,036 1,031 1,034 1,034 1,033 1,032 1,034 1,029 1,032 1,031 1,034 10^(4.5) dPa · s (° C.) 1,360 1,359 1,363 1,368 1,357 1,361 1,360 1,362 1,362 1,362 1,357 1,363 1,360 1,366 10^(4.0) dPa · s (° C.) 1,531 1,530 1,535 1,540 1,527 1,531 1,530 1,533 1,532 1,533 1,528 1,537 1,533 1,539 10^(3.0) dPa · s (° C.) 1,642 1,641 1,646 1,652 1,636 1,639 1,641 1,644 1,642 1,643 1,640 1,647 1,646 1,651 10^(2.5) dPa · s (° C.) 1,296 1,295 1,298 1,303 1,293 1,297 1,296 1,297 1,297 1,298 1,292 1,298 1,295 1,301 Young's modulus (GPa) 80.6 80.6 80.4 80.2 80.6 80.4 80.6 80.6 80.5 80.5 79.9 80.0 80.3 80.4 Specific Young's modulus 30.4 30.3 30.5 30.5 30.4 30.5 30.1 30.3 30.1 30.1 29.7 29.8 29.9 30.0 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.10 0.05 0.05 0.08 0.04 0.13 0.14 0.15 0.03 0.03 0.04 0.13 0.09 0.08

TABLE 20 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 267 268 269 270 271 272 273 274 275 276 277 278 279 280 mol SiO₂ 72.2 69.6 71.2 69.4 71.5 72.0 72.0 72.0 72.0 71.8 71.6 69.8 71.8 71.6 % Al₂O₃ 10.7 10.7 10.7 11.3 10.4 11.3 11.9 12.4 12.1 11.2 11.9 14.0 11.9 12.4 B₂O₃ 0.0 0.4 0.1 2.4 0.8 0.5 1.0 1.5 1.8 0.2 0.2 0.0 1.2 1.9 MgO 0.0 2.0 0.7 1.6 0.6 0.0 0.0 0.0 0.0 2.0 4.0 2.0 0.0 0.0 CaO 10.6 10.8 10.8 10.2 10.4 10.1 9.4 8.8 8.8 8.8 6.8 6.0 9.4 8.8 SrO 1.3 1.3 1.3 0.4 0.5 1.2 1.1 1.0 1.0 0.8 0.3 8.0 1.1 1.0 BaO 5.0 5.0 5.0 4.4 5.6 4.7 4.4 4.1 4.1 5.0 5.0 0.0 4.4 4.1 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 [SiO₂] + [Al₂O₃] 82.9 80.3 81.9 80.8 81.9 83.3 83.9 84.4 84.1 83.0 82.5 83.8 83.7 84.0 [MgO] + [CaO] + [SrO] + [BaO] 16.9 19.1 17.8 16.6 17.1 16.0 14.9 13.9 13.9 16.6 16.1 16.0 14.9 13.9 [SrO] + [BaO] 6.3 6.3 6.3 4.8 6.1 5.9 5.5 5.1 5.1 5.8 5.3 8.0 5.5 5.1 [B₂O₃]/([SrO] + [BaO]) 0.0 0.1 0.0 0.5 0.1 0.1 0.2 0.3 0.4 0.0 0.0 0.0 0.2 0.4 [Al₂O₃] + [B₂O₃] − [CaO] − −6.2 −6.0 −6.3 −1.3 −5.3 −4.2 −2.0 0.0 0.0 −3.2 0.0 0.0 −1.8 0.4 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 330.8 334.4 332.7 288.4 315.7 324.8 318.8 311.5 302.8 337.6 360.2 395.8 315.6 305.1 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,776.9 1,760.8 1,771.4 1,743.7 1,762.0 1,776.0 1,775.8 1,774.7 1,768.9 1,774.8 1,777.2 1,800.2 1,773.0 1,769.0 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- (10⁻⁷/° C.) sured sured sured sured sured sured sured sured sured sured sured sured sured sured Density (g/cm³) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Strain point (° C.) Unmea- 727 740 713 727 747 751 756 749 745 749 777 751 746 sured Annealing point (° C.) Unmea- 782 797 771 784 806 Unmea- Unmea- 812 804 809 835 813 803 sured sured sured Softening point (° C.) Unmea- 1,005 1,024 1,004 1,016 1,043 Unmea- Unmea- 1,058 1,043 1,051 1,062 1,058 1,031 sured sured sured 10^(4.5) dPa · s (° C.) Unmea- 1,318 1,349 1,327 1,350 1,384 Unmea- Unmea- 1,399 1,380 1,387 1,377 1,395 1,345 sured sured sured 10^(4.0) dPa · s (° C.) Unmea- 1,483 1,519 1,494 1,524 1,559 Unmea- Unmea- 1,572 1,552 1,557 1,536 1,565 1,503 sured sured sured 10^(3.0) dPa · s (° C.) Unmea- 1,589 1,630 1,600 1,636 1,670 Unmea- Unmea- 1,682 1,662 1,667 1,638 1,674 1,604 sured sured sured 10^(2.5) dPa · s (° C.) Unmea- 1,256 1,285 1,264 1,284 1,317 Unmea- Unmea- 1,333 1,314 1,322 1,316 1,330 1,284 sured sured sured Young's modulus (GPa) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Specific Young's modulus Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- (GPa/g · cm⁻³) sured sured sured sured sured sured sured sured sured sured sured sured sured sured β-OH (mm⁻¹) 0.08 0.05 0.10 0.04 0.10 0.03 0.11 0.06 0.09 0.03 0.15 0.12 0.07 0.15

TABLE 21 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 281 282 283 284 285 286 287 288 289 290 291 292 293 294 mol SiO₂ 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 % Al₂O₃ 13.5 13.5 13.5 13.5 13.5 13.0 13.0 13.0 13.0 13.0 13.0 13.0 13.0 13.0 B₂O₃ 0.0 0.0 0.0 0.0 0.5 0.0 0.0 0.0 0.0 1.0 0.0 0.0 0.0 0.5 MgO 3.3 3.3 3.3 3.8 3.3 3.3 3.3 3.3 4.3 3.3 3.3 3.3 3.8 3.3 CaO 4.7 4.7 5.2 4.7 4.7 4.7 4.7 5.7 4.7 4.7 4.7 5.2 4.7 4.7 SrO 0.0 0.5 0.0 0.0 0.0 0.0 1.0 0.0 0.0 0.0 0.5 0.0 0.0 0.0 BaO 6.6 6.1 6.1 6.1 6.1 7.1 6.1 6.1 6.1 6.1 6.6 6.6 6.6 6.6 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 85.4 85.4 85.4 85.4 85.4 84.9 84.9 84.9 84.9 84.9 84.9 84.9 84.9 84.9 [MgO] + [CaO] + [SrO] + [BaO] 14.5 14.5 14.5 14.6 14.0 15.0 15.0 15.0 15.1 14.0 15.0 15.1 15.1 14.6 [SrO] + [BaO] 6.6 6.6 6.1 6.1 6.1 7.1 7.1 6.1 6.1 6.1 7.1 6.6 6.6 6.6 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.2 0.0 0.0 0.0 0.1 [Al₂O₃] + [B₂O₃] − [CaO] − 2.2 2.3 2.2 2.7 3.3 1.2 1.3 1.2 2.2 3.3 1.2 1.2 1.7 2.2 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 390.8 389.2 382.8 386.0 374.7 391.8 389.2 376.3 382.0 360.2 390.8 384.3 387.0 376.5 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,798.6 1,798.4 1,798.1 1,798.0 1,792.5 1,794.6 1,794.6 1,793.6 1,792.9 1,782.8 1,794.8 1,794.6 1,794.4 1,789.3 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 39.1 39.0 38.8 38.4 38.1 40.3 40.0 39.7 38.9 38.2 40.2 40.0 39.6 39.2 (10⁻⁷/° C.) Density (g/cm³) 2.687 2.679 2.672 2.672 2.662 2.703 2.688 2.675 2.673 2.655 2.696 2.689 2.688 2.679 Strain point (° C.) 776 776 775 774 768 770 771 770 768 756 770 770 769 763 Annealing point (° C.) 838 838 837 836 832 833 833 831 829 821 833 832 831 827 Softening point (° C.) 1,082 1,081 1,079 1,078 1,076 1,077 1,075 1,072 1,071 1,066 1,076 1,074 1,074 1,071 10^(4.5) dPa · s (° C.) 1,415 1,413 1,411 1,411 1,411 1,411 1,409 1,405 1,404 1,405 1,410 1,408 1,408 1,408 10^(4.0) dPa · s (° C.) 1,581 1,580 1,577 1,576 1,578 1,581 1,578 1,573 1,571 1,574 1,579 1,577 1,575 1,578 10^(3.0) dPa · s (° C.) 1,686 1,685 1,682 1,681 1,684 1,687 1,684 1,679 1,677 1,681 1,685 1,683 1,681 1,683 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 82.0 82.1 82.3 82.6 81.7 81.4 81.6 82.0 82.5 80.8 81.5 81.7 82.0 81.2 Specific Young's modulus 30.5 30.6 30.8 30.9 30.7 30.1 30.4 30.7 30.9 30.4 30.2 30.4 30.5 30.3 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.14 0.14 0.06 0.13 0.15 0.15 0.15 0.08 0.07 0.03 0.15 0.11 0.13 0.08

TABLE 22 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 295 296 297 298 299 300 301 302 303 304 305 306 307 308 mol SiO₂ 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 % Al₂O₃ 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 B₂O₃ 0.0 0.0 0.0 0.0 1.5 0.0 0.0 0.0 0.5 0.0 0.0 0.0 1.0 0.0 MgO 3.3 3.3 3.3 4.8 3.3 3.3 3.3 3.8 3.3 3.3 3.3 4.3 3.3 3.3 CaO 4.7 4.7 6.2 4.7 4.7 4.7 5.2 4.7 4.7 4.7 5.7 4.7 4.7 5.2 SrO 0.0 1.5 0.0 0.0 0.0 0.5 0.0 0.0 0.0 1.0 0.0 0.0 0.0 0.5 BaO 7.6 6.1 6.1 6.1 6.1 7.1 7.1 7.1 7.1 6.6 6.6 6.6 6.6 6.6 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 84.4 84.4 84.4 84.4 84.4 84.4 84.4 84.4 84.4 84.4 84.4 84.4 84.4 84.4 [MgO] + [CaO] + [SrO] + [BaO] 15.5 15.5 15.5 15.5 14.0 15.5 15.6 15.6 15.0 15.5 15.6 15.6 14.5 15.6 [SrO] + [BaO] 7.6 7.6 6.1 6.1 6.1 7.6 7.1 7.1 7.1 7.6 6.6 6.6 6.6 7.1 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.2 0.0 0.0 0.0 0.1 0.0 0.0 0.0 0.2 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 0.2 0.3 0.2 1.8 3.3 0.2 0.2 0.7 1.2 0.2 0.2 1.2 2.2 0.2 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 392.8 389.2 369.8 377.4 345.7 391.8 385.3 388.0 377.3 390.8 377.8 383.0 361.8 384.3 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,790.5 1,790.8 1,789.1 1,787.3 1,773.1 1,790.8 1,790.5 1,789.9 1,784.9 1,791.0 1,790.1 1,788.8 1,779.2 1,790.8 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 41.4 41.1 10.5 39.3 38.3 41.3 41.1 40.7 40.4 41.2 40.9 40.0 39.3 41.0 (10⁻⁷/° C.) Density (g/cm³) 2.719 2.697 2.677 2.674 2.647 2.712 2.705 2.704 2.696 2.705 2.692 2.689 2.672 2.698 Strain point (° C.) 764 765 764 763 745 764 764 763 757 764 764 763 751 764 Annealing point (° C.) 826 826 824 823 811 826 825 824 821 826 824 823 815 825 Softening point (° C.) 1,072 1,069 1,064 1,064 1,056 1,071 1,069 1,069 1,066 1,070 1,067 1,067 1,061 1,068 10^(4.5) dPa · s (° C.) 1,407 1,404 1,398 1,398 1,398 1,406 1,404 1,404 1,404 1,405 1,401 1,401 1,401 1,403 10^(4.0) dPa · s (° C.) 1,578 1,575 1,568 1,565 1,571 1,577 1,575 1,574 1,577 1,576 1,571 1,569 1,575 1,573 10^(3.0) dPa · s (° C.) 1,686 1,682 1,675 1,672 1,677 1,684 1,682 1,681 1,683 1,683 1,678 1,677 1,680 1,680 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 80.8 81.2 81.7 82.4 79.9 80.9 81.1 81.4 80.5 81.1 81.4 81.9 80.2 81.3 Specific Young's modulus 29.7 30.1 30.5 30.8 30.2 29.8 30.0 30.1 29.9 30.0 30.3 30.5 30.0 30.1 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.06 0.14 0.05 0.04 0.05 0.13 0.07 0.13 0.05 0.06 0.12 0.08 0.03 0.08

TABLE 23 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 309 310 311 312 313 314 315 316 317 318 319 320 321 322 mol SiO₂ 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 % Al₂O₃ 12.5 12.5 12.5 12.5 12.5 12.0 12.0 12.0 12.0 12.0 12.0 12.0 12.0 12.0 B₂O₃ 0.0 0.5 0.0 0.5 0.5 0.0 0.0 0.0 0.0 2.0 0.0 0.0 0.0 1.0 MgO 3.8 3.3 3.8 3.3 3.8 3.3 3.3 3.3 5.3 3.3 3.3 3.3 4.3 3.3 CaO 4.7 4.7 5.2 5.2 4.7 4.7 4.7 6.7 4.7 4.7 4.7 5.7 4.7 4.7 SrO 0.5 0.5 0.0 0.0 0.0 0.0 2.0 0.0 0.0 0.0 1.0 0.0 0.0 0.0 BaO 6.6 6.6 6.6 6.6 6.6 8.1 6.1 6.1 6.1 6.1 7.1 7.1 7.1 7.1 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 84.4 84.4 84.4 84.4 84.4 83.9 83.9 83.9 83.9 83.9 83.9 83.9 83.9 83.9 [MgO] + [CaO] + [SrO] + [BaO] 15.6 15.1 15.6 15.1 15.1 16.0 16.0 16.0 16.0 14.0 16.0 16.1 16.1 15.0 [SrO] + [BaO] 7.1 7.1 6.6 6.6 6.6 8.1 8.1 6.1 6.1 6.1 8.1 7.1 7.1 7.1 [B₂O₃]/([SrO] + [BaO]) 0.0 0.1 0.0 0.1 0.1 0.0 0.0 0.0 0.0 0.3 0.0 0.0 0.0 0.1 [Al₂O₃] + [B₂O₃] − [CaO] − 0.7 1.2 0.7 1.2 1.7 −0.8 −0.7 −0.8 1.3 3.3 −0.8 −0.8 0.2 1.2 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 387.0 376.5 380.5 370.0 372.5 393.8 389.2 363.3 373.4 331.2 391.8 378.8 384.0 362.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,790.6 1,786.0 1,789.9 1,785.3 1,784.7 1,786.5 1,787.0 1,784.6 1,782.2 1,763.4 1,787.0 1,786.0 1,784.8 1,775.2 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 40.6 40.2 40.4 40.1 39.7 42.6 42.1 41.4 39.8 38.4 42.4 42.0 41.2 40.5 (10⁻⁷/° C.) Density (g/cm³) 2.697 2.688 2.690 2.681 2.680 2.736 2.706 2.680 2.675 2.640 2.721 2.708 2.706 2.688 Strain point (° C.) 763 757 763 757 757 758 758 758 758 736 758 758 758 746 Annealing point (° C.) 824 820 823 819 819 818 818 816 817 800 818 817 817 809 Softening point (° C.) 1,068 1,065 1,066 1,064 1,063 1,065 1,062 1,057 1,058 1,045 1,063 1,061 1,061 1,054 10^(4.5) dPa · s (° C.) 1,403 1,403 1,401 1,401 1,401 1,402 1,399 1,391 1,391 1,390 1,401 1,397 1,397 1,396 10^(4.0) dPa · s (° C.) 1,572 1,575 1,570 1,573 1,572 1,575 1,570 1,561 1,558 1,568 1,572 1,567 1,566 1,574 10^(3.0) dPa · s (° C.) 1,679 1,680 1,677 1,678 1,678 1,683 1,678 1,670 1,667 1,671 1,681 1,676 1,675 1,677 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 81.6 80.7 81.7 80.9 81.1 80.1 80.7 81.4 82.4 79.0 80.4 80.8 81.3 79.6 Specific Young's modulus 30.2 30.0 30.4 30.2 30.3 29.3 29.8 30.4 30.8 29.9 29.6 29.8 30.0 29.6 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.06 0.04 0.06 0.15 0.03 0.05 0.03 0.11 0.05 0.11 0.13 0.14 0.08 0.14

TABLE 24 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 323 324 325 326 327 328 329 330 331 332 333 334 335 336 mol SiO₂ 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 % Al₂O₃ 12.0 12.0 12.0 12.0 12.0 12.0 14.5 14.5 14.5 15.0 15.0 15.0 15.0 15.0 B₂O₃ 0.0 0.0 1.0 0.0 1.0 1.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 3.3 4.3 3.3 4.3 3.3 4.3 3.3 3.3 2.8 3.3 3.3 2.3 3.3 2.8 CaO 5.7 4.7 4.7 5.7 5.7 4.7 4.7 4.2 4.7 4.7 3.7 4.7 4.2 4.7 SrO 1.0 1.0 1.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 BaO 6.1 6.1 6.1 6.1 6.1 6.1 5.6 6.1 6.1 5.1 6.1 6.1 5.6 5.6 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 83.9 83.9 83.9 83.9 83.9 83.9 86.4 86.4 86.4 86.9 86.9 86.9 86.9 86.9 [MgO] + [CaO] + [SrO] + [BaO] 16.0 16.0 15.0 16.1 15.0 15.0 13.5 13.5 13.6 13.0 13.0 13.1 13.1 13.1 [SrO] + [BaO] 7.1 7.1 7.1 6.1 6.1 6.1 5.6 6.1 6.1 5.1 6.1 6.1 5.6 5.6 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.1 0.0 0.2 0.2 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − −0.8 0.3 1.3 0.2 1.2 2.3 4.2 4.2 3.7 5.2 5.2 4.2 5.2 4.7 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 376.3 381.4 360.2 368.5 347.3 352.4 388.8 395.8 394.0 387.8 402.3 398.0 395.3 393.0 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,786.0 1,784.8 1,775.2 1,783.9 1,774.2 1,773.0 1,806.7 1,807.1 1,808.2 1,810.8 1,811.6 1,813.3 1,811.7 1,812.7 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 41.8 40.9 40.2 40.6 39.9 39.1 36.9 37.1 37.5 35.7 36.3 37.0 36.0 36.4 (10⁻⁷/° C.) Density (g/cm³) 2.693 2.691 2.673 2.677 2.660 2.657 2.654 2.667 2.669 2.638 2.664 2.667 2.651 2.652 Strain point (° C.) 758 758 746 757 746 747 785 785 787 788 790 794 789 791 Annealing point (° C.) 817 817 809 816 808 808 846 847 849 847 850 854 849 850 Softening point (° C.) 1,059 1,060 1,053 1,057 1,051 1,051 1,092 1,095 1,097 1,097 1,102 1,106 1,100 1,101 10^(4.5) dPa · s (° C.) 1,395 1,395 1,394 1,391 1,390 1,391 1,418 1,421 1,422 1,418 1,424 1,428 1,421 1,423 10^(4.0) dPa · s (° C.) 1,565 1,564 1,571 1,559 1,567 1,564 1,580 1,583 1,585 1,580 1,587 1,590 1,583 1,584 10^(3.0) dPa · s (° C.) 1,674 1,673 1,674 1,668 1,670 1,669 1,681 1,685 1,687 1,677 1,684 1,689 1,680 1,682 10^(2.5) dPa · s(° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 81.1 81.6 79.9 82.0 80.3 80.7 83.2 82.9 82.7 83.8 83.2 82.8 83.5 83.4 Specific Young's modulus 30.1 30.3 29.9 30.6 30.2 30.4 31.3 31.1 31.0 31.8 31.2 31.0 31.5 31.4 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.09 0.11 0.10 0.12 0.09 0.09 0.12 0.03 0.05 0.05 0.09 0.09 0.06 0.12

TABLE 25 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 337 338 339 340 341 342 343 344 345 346 347 348 349 350 mol SiO₂ 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 % Al₂O₃ 15.0 15.5 15.5 15.5 15.5 15.5 15.5 15.5 15.5 15.5 16.0 16.0 16.0 16.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 2.8 3.3 3.3 1.8 3.3 2.8 3.3 2.3 2.8 2.3 3.3 3.3 1.3 3.3 CaO 4.2 4.7 3.2 4.7 4.2 4.7 3.7 4.7 3.7 4.2 4.7 2.7 4.7 3.7 SrO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 BaO 6.1 4.6 6.1 6.1 5.1 5.1 5.6 5.6 6.1 6.1 4.1 6.1 6.1 5.1 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 86.9 87.4 87.4 87.4 87.4 87.4 87.4 87.4 87.4 87.4 87.9 87.9 87.9 87.9 [MgO] + [CaO] + [SrO] + [BaO] 13.1 12.5 12.5 12.5 12.6 12.6 12.6 12.6 12.6 12.6 12.0 12.0 12.0 12.1 [SrO] + [BaO] 6.1 4.6 6.1 6.1 5.1 5.1 5.6 5.6 6.1 6.1 4.1 6.1 6.1 5.1 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 4.7 6.2 6.2 4.8 6.2 5.7 6.2 5.2 5.7 5.2 7.2 7.2 5.3 7.2 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 400.5 386.8 408.8 401.4 394.3 392.0 401.8 397.0 406.5 404.0 385.8 415.3 405.4 400.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,813.2 1,814.8 1,816.1 1,817.9 1,815.7 1,816.3 1,816.2 1,817.3 1,817.2 1,817.8 1,818.9 1,820.6 1,823.0 1,820.2 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 36.7 34.7 35.5 36.6 34.9 35.3 35.2 35.9 35.8 36.2 33.6 34.7 36.1 34.2 (10⁻⁷/° C.) Density (g/cm³) 2.666 2.622 2.662 2.665 2.635 2.636 2.649 2.651 2.663 2.664 2.605 2.659 2.664 2.633 Strain point (° C.) 792 791 794 800 792 794 793 797 796 798 794 798 806 795 Annealing point (° C.) 852 848 853 860 849 851 851 856 855 857 848 854 865 850 Softening point (° C.) 1,104 1,102 1,109 1,114 1,104 1,106 1,106 1,110 1,110 1,112 1,106 1,114 1,119 1,110 10^(4.5) dPa · s (° C.) 1,426 1,417 1,427 1,432 1,421 1,422 1,424 1,427 1,429 1,430 1,416 1,428 1,437 1,422 10^(4.0) dPa · s (° C.) 1,588 1,582 1,593 1,596 1,585 1,586 1,589 1,591 1,594 1,595 1,585 1,601 1,603 1,593 10^(3.0) dPa · s (° C.) 1,686 1,672 1,683 1,690 1,675 1,678 1,679 1,684 1,685 1,687 1,666 1,681 1,691 1,673 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 83.0 84.4 83.5 82.8 84.1 83.9 83.8 83.4 83.3 83.1 85.0 83.8 82.9 84.4 Specific Young's modulus 31.1 32.2 31.4 31.1 31.9 31.8 31.6 31.5 31.3 31.2 32.6 31.5 31.1 32.1 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.08 0.03 0.08 0.03 0.04 0.09 0.15 0.15 0.04 0.11 0.05 0.07 0.06 0.03

TABLE 26 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 351 352 353 354 355 356 357 358 359 360 361 362 363 364 mol SiO₂ 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 % Al₂O₃ 16.0 16.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 2.3 2.3 10.0 10.0 10.0 8.0 8.0 8.0 6.0 6.0 6.0 6.0 6.0 6.0 CaO 4.7 3.7 4.0 0.0 0.0 6.0 0.0 0.0 8.0 0.0 0.0 4.0 4.0 0.0 SrO 0.0 0.0 0.0 4.0 0.0 0.0 6.0 0.0 0.0 8.0 0.0 4.0 0.0 4.0 BaO 5.1 6.1 0.0 0.0 4.0 0.0 0.0 6.0 0.0 0.0 8.0 0.0 4.0 4.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 87.9 87.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 [MgO] + [CaO] + [SrO] + [BaO] 12.1 12.1 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 [SrO] + [BaO] 5.1 6.1 0.0 4.0 4.0 0.0 6.0 6.0 0.0 8.0 8.0 4.0 4.0 8.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 — 0.0 0.0 — 0.0 0.0 — 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 6.2 6.2 10.0 10.0 10.0 8.0 8.0 8.0 6.0 6.0 6.0 6.0 6.0 6.0 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 396.0 410.5 331.9 383.9 391.9 321.9 399.9 411.9 311.9 415.9 431.9 363.9 371.9 423.9 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,821.4 1,822.3 1,788.6 1,794.2 1,792.2 1,791.0 1,799.4 1,796.4 1,793.4 1,804.6 1,800.6 1,799.0 1,797.0 1,802.6 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 34.9 35.4 30.1 31.2 31.9 31.3 33.1 34.4 32.6 35.2 37.0 33.9 34.7 36.1 (10⁻⁷/° C.) Density (g/cm³) 2.635 3.661 2.488 2.541 2.597 2.493 2.572 2.657 2.497 2.603 2.717 2.550 2.606 2.660 Strain point (° C.) 800 802 771 780 782 770 778 780 773 780 779 774 773 779 Annealing point (° C.) 856 859 830 836 839 828 837 841 831 841 847 834 833 843 Softening point (° C.) 1,113 1,116 1,048 1,057 1,063 1,053 1,065 1,077 1,058 1,076 1,093 1,066 1,069 1,084 10^(4.5) dPa · s (° C.) 1,426 1,433 1,358 1,370 1,381 1,364 1,385 1,402 1,370 1,399 1,422 1,385 1,396 1,411 10^(4.0) dPa · s (° C.) 1,594 1,601 1,517 1,534 1,546 1,521 1,548 1,566 1,527 1,563 1,587 1,544 1,557 1,575 10^(3.0) dPa · s (° C.) 1,678 1,685 1,613 1,629 1,641 1,619 1,646 1,664 1,626 1,664 1,689 1,645 1,658 1,677 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 84.0 83.4 89.5 88.2 87.0 88.6 86.6 84.8 87.7 85.0 82.6 86.3 85.1 83.8 Specific Young's modulus 31.9 31.3 36.0 34.7 33.5 35.5 33.7 31.9 35.1 32.7 30.4 33.9 32.7 31.5 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.11 0.11 0.12 0.14 0.12 0.04 0.04 0.08 0.08 0.15 0.11 0.05 0.04 0.09

TABLE 27 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 365 366 367 368 369 370 371 372 373 374 375 376 377 378 mol SiO₂ 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 % Al₂O₃ 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 6.0 6.0 6.0 6.0 6.0 6.0 4.0 4.0 4.0 4.0 4.0 4.0 4.0 4.0 CaO 6.0 6.0 2.0 2.0 0.0 0.0 10.0 0.0 0.0 8.0 8.0 6.0 6.0 6.0 SrO 2.0 0.0 6.0 0.0 2.0 6.0 0.0 10.0 0.0 2.0 0.0 4.0 0.0 2.0 BaO 0.0 2.0 0.0 6.0 6.0 2.0 0.0 0.0 10.0 0.0 2.0 0.0 4.0 2.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 [MgO] + [CaO] + [SrO] + [BaO] 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 [SrO] + [BaO] 2.0 2.0 6.0 6.0 8.0 8.0 0.0 10.0 10.0 2.0 2.0 4.0 4.0 4.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 — 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 6.0 6.0 6.0 6.0 6.0 6.0 4.0 4.0 4.0 4.0 4.0 4.0 4.0 4.0 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 337.9 341.9 389.9 401.9 427.9 419.9 301.9 431.9 451.9 327.9 331.9 353.9 361.9 357.9 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,796.2 1,795.2 1,801.8 1,798.8 1,801.6 1,803.6 1,795.8 1,809.8 1,804.8 1,798.6 1,797.6 1,801.4 1,799.4 1,800.4 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 33.3 33.7 34.6 35.8 36.5 35.7 34.0 37.4 39.7 34.7 35.1 35.4 36.2 35.8 (10⁻⁷/° C.) Density (g/cm³) 2.524 2.552 2.576 2.661 2.688 2.631 2.502 2.634 2.776 2.528 2.556 2.554 2.611 2.583 Strain point (° C.) 773 772 776 776 779 780 781 788 785 779 778 779 777 778 Annealing point (° C.) 832 830 837 839 845 842 838 849 855 838 836 839 837 837 Softening point (° C.) 1,062 1,063 1,070 1,080 1,069 1,060 1,064 1,090 1,111 1,068 1,069 1,072 1,075 1,074 10^(4.5) dPa · s (° C.) 1,377 1,383 1,392 1,409 1,416 1,405 1,375 1,413 1,440 1,383 1,389 1,391 1,402 1,396 10^(4.0) dPa · s (° C.) 1,535 1,541 1,553 1,572 1,581 1,569 1,533 1,578 1,609 1,541 1,547 1,550 1,563 1,556 10^(3.0) dPa · s (° C.) 1,636 1,642 1,654 1,673 1,683 1,670 1,634 1,681 1,712 1,643 1,650 1,653 1,665 1,659 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 87.0 86.4 85.7 83.9 83.2 84.4 86.7 83.4 80.4 86.1 85.5 85.4 84.2 84.8 Specific Young's modulus 34.5 33.9 33.2 31.5 30.9 32.1 34.7 31.7 29.0 34.0 33.4 33.4 32.2 32.8 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.14 0.03 0.15 0.12 0.05 0.07 0.11 0.06 0.07 0.05 0.04 0.03 0.05 0.15

TABLE 28 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 379 380 381 382 383 384 385 386 387 388 389 390 391 392 mol SiO₂ 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 % Al₂O₃ 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 4.0 4.0 4.0 4.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 CaO 4.0 4.0 4.0 4.0 10.0 10.0 8.0 8.0 8.0 6.0 6.0 6.0 6.0 4.0 SrO 6.0 0.0 2.0 4.0 2.0 0.0 4.0 0.0 2.0 6.0 0.0 2.0 4.0 8.0 BaO 0.0 6.0 4.0 2.0 0.0 2.0 0.0 4.0 2.0 0.0 6.0 4.0 2.0 0.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 [MgO] + [CaO] + [SrO] + [BaO] 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 [SrO] + [BaO] 6.0 6.0 6.0 6.0 2.0 2.0 4.0 4.0 4.0 6.0 6.0 6.0 6.0 8.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 4.0 4.0 4.0 4.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 379.9 391.9 387.9 383.9 317.9 321.9 343.9 351.9 347.9 369.9 381.9 377.9 373.9 395.9 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,804.2 1,801.2 1,802.2 1,803.2 1,801.0 1,800.0 1,803.8 1,801.8 1,802.8 1,806.6 1,803.6 1,804.6 1,805.6 1,809.4 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 36.0 37.4 36.9 36.5 36.2 36.5 36.9 37.8 37.3 37.6 38.9 38.5 38.0 38.3 (10⁻⁷/° C.) Density (g/cm³) 2.581 2.666 2.638 2.609 2.533 2.561 2.559 2.616 2.587 2.586 2.671 2.642 2.614 2.612 Strain point (° C.) 780 778 779 780 788 786 787 785 786 788 786 786 787 791 Annealing point (° C.) 841 841 840 841 847 845 848 844 846 850 847 847 848 852 Softening point (° C.) 1,077 1,084 1,081 1,079 1,076 1,077 1,081 1,083 1,082 1,085 1,091 1,089 1,087 1,091 10^(4.5) dPa · s (° C.) 1,398 1,415 1,409 1,404 1,388 1,393 1,396 1,406 1,401 1,403 1,418 1,413 1,408 1,411 10^(4.0) dPa · s (° C.) 1,559 1,578 1,572 1,565 1,548 1,554 1,556 1,569 1,563 1,565 1,584 1,578 1,572 1,574 10^(3.0) dPa · s (° C.) 1,662 1,682 1,675 1,669 1,650 1,657 1,660 1,673 1,666 1,669 1,688 1,682 1,676 1,679 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 84.7 82.9 83.5 84.1 85.2 84.6 84.5 83.3 83.9 83.8 82.0 82.6 83.2 83.2 Specific Young's modulus 32.8 31.1 31.7 32.2 33.6 33.0 33.0 31.8 32.4 32.4 30.7 31.3 31.8 31.8 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.06 0.13 0.12 0.06 0.13 0.13 0.15 0.11 0.09 0.05 0.12 0.14 0.10 0.06

TABLE 29 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 393 394 395 396 397 398 399 400 401 402 403 404 405 406 mol SiO₂ 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 71.9 % Al₂O₃ 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 0.0 0.0 0.0 0.0 CaO 4.0 4.0 4.0 4.0 2.0 2.0 2.0 2.0 2.0 2.0 0.0 0.0 0.0 0.0 SrO 0.0 6.0 4.0 2.0 10.0 0.0 8.0 6.0 4.0 2.0 10.0 8.0 6.0 4.0 BaO 8.0 2.0 4.0 6.0 0.0 10.0 2.0 4.0 6.0 8.0 4.0 6.0 8.0 10.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 85.9 [MgO] + [CaO] + [SrO] + [BaO] 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 [SrO] + [BaO] 8.0 8.0 8.0 8.0 10.0 10.0 10.0 10.0 10.0 10.0 14.0 14.0 14.0 14.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 0.0 0.0 0.0 0.0 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 411.9 399.9 403.9 407.9 421.9 441.9 425.9 429.9 433.9 437.9 471.9 475.9 479.9 483.9 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,805.4 1,808.4 1,807.4 1,806.4 1,812.2 1,807.2 1,811.2 1,810.2 1,809.2 1,808.2 1,812.2 1,817.2 1,816.2 1,815.2 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 40.1 38.7 39.2 39.6 39.0 41.2 39.5 39.9 40.4 40.8 42.9 43.4 43.8 44.3 (10⁻⁷/° C.) Density (g/cm³) 2.726 2.640 2.669 2.697 2.639 2.781 2.667 2.696 2.724 2.752 2.753 2.782 2.810 2.838 Strain point (° C.) 798 791 790 789 796 793 795 795 794 794 817 816 816 816 Annealing point (° C.) 852 852 851 852 856 859 856 856 857 858 876 877 878 879 Softening point (° C.) 1,103 1,093 1,096 1,099 1,097 1,117 1,100 1,104 1,109 1,113 1,123 1,127 1,130 1,132 10^(4.5) dPa · s (° C.) 1,431 1,416 1,421 1,426 1,419 1,443 1,424 1,429 1,434 1,438 1,445 1,449 1,453 1,457 10^(4.0) dPa · s (° C.) 1,599 1,581 1,587 1,593 1,584 1,615 1,590 1,596 1,602 1,609 1,621 1,627 1,633 1,639 10^(3.0) dPa · s (° C.) 1,703 1,685 1,691 1,697 1,688 1,717 1,694 1,700 1,706 1,712 1,720 1,725 1,730 1,735 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 80.8 82.6 82.0 81.4 82.5 79.5 81.9 81.3 80.7 80.1 79.0 78.4 77.8 77.2 Specific Young's modulus 29.6 31.3 30.7 30.2 31.3 28.6 30.7 30.2 29.6 29.1 28.7 28.2 27.7 27.2 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.12 0.04 0.04 0.14 0.07 0.08 0.15 0.07 0.15 0.05 0.05 0.05 0.05 0.14

TABLE 30 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 407 408 409 410 411 412 413 414 415 416 417 418 419 420 mol SiO₂ 71.7 71.5 71.3 71.1 70.9 70.7 70.5 70.3 70.1 69.9 69.7 69.5 69.3 69.1 % Al₂O₃ 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 B₂O₃ 0.2 0.4 0.6 0.8 1.0 1.2 1.4 1.6 1.8 2.0 2.2 2.4 2.6 2.8 MgO 3.3 3.3 3.3 3.3 3.3 3.3 3.3 3.3 3.3 3.3 3.3 3.3 3.3 3.3 CaO 4.7 4.7 4.7 4.7 4.7 4.7 4.7 4.7 4.7 4.7 4.7 4.7 4.7 4.7 SrO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 BaO 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 85.7 85.5 85.3 85.1 84.9 84.7 84.5 84.3 84.1 83.9 83.7 83.5 83.3 83.1 [MgO] + [CaO] + [SrO] + [BaO] 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 14.0 [SrO] + [BaO] 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 6.1 [B₂O₃]/([SrO] + [BaO]) 0.0 0.1 0.1 0.1 0.2 0.2 0.2 0.3 0.3 0.3 0.4 0.4 0.4 0.5 [Al₂O₃] + [B₂O₃] − [CaO] − 3.5 3.7 3.9 4.1 4.3 4.5 4.7 4.9 5.1 5.3 5.5 5.7 5.9 6.1 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 386.0 382.8 379.6 376.4 373.2 370.0 366.8 363.6 360.4 357.2 354.0 350.8 347.6 344.4 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,799.3 1,796.5 1,793.7 1,790.9 1,788.1 1,785.2 1,782.4 1,779.6 1,776.8 1,774.0 1,771.1 1,768.3 1,765.5 1,762.7 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 38.0 38.0 38.1 38.1 38.1 38.2 38.2 38.2 38.3 38.3 38.3 38.4 38.4 38.4 (10⁻⁷/° C.) Density (g/cm³) 2.668 2.667 2.666 2.664 2.663 2.662 2.660 2.659 2.657 2.656 2.655 2.653 2.652 2.651 Strain point (° C.) 776 772 768 764 760 757 753 750 747 744 741 739 736 734 Annealing point (° C.) 839 835 832 828 825 821 818 815 811 808 805 802 799 796 Softening point (° C.) 1,082 1,078 1,074 1,070 1,066 1,063 1,059 1,056 1,053 1,050 1,047 1,043 1,040 1,036 10^(4.5) dPa · s (° C.) 1,413 1,410 1,406 1,403 1,399 1,396 1,392 1,389 1,385 1,382 1,378 1,374 1,371 1,367 10^(4.0) dPa · s (° C.) 1,577 1,573 1,569 1,565 1,561 1,557 1,553 1,549 1,545 1,541 1,537 1,533 1,530 1,526 10^(3.0) dPa · s (° C.) 1,682 1,678 1,675 1,671 1,668 1,664 1,660 1,656 1,652 1,648 1,644 1,640 1,636 1,632 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 82.4 82.2 82.0 81.8 81.6 81.4 81.2 81.0 80.8 80.6 80.5 80.3 80.1 79.9 Specific Young's modulus 30.9 30.8 30.8 30.7 30.6 30.6 30.5 30.5 30.4 30.4 30.3 30.2 30.2 30.1 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.12 0.03 0.10 0.11 0.08 0.10 0.05 0.13 0.04 0.10 0.04 0.05 0.07 0.12

TABLE 31 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 421 422 423 424 425 426 427 428 429 430 431 432 433 434 mol SiO₂ 68.9 68.9 69.4 69.9 70.4 70.9 71.4 72.4 72.9 73.4 73.9 74.4 74.9 73.6 % Al₂O₃ 14.0 15.5 15.3 15.0 14.8 14.5 14.3 13.8 13.5 13.3 13.0 12.8 12.5 12.0 B₂O₃ 3.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 3.3 3.6 3.6 3.5 3.4 3.4 3.3 3.2 3.2 3.1 3.0 3.0 2.9 3.3 CaO 4.7 5.2 5.1 5.0 4.9 4.8 4.8 4.6 4.5 4.4 4.3 4.3 4.2 4.8 SrO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 BaO 6.1 6.7 6.6 6.5 6.4 6.3 6.2 6.0 5.9 5.7 5.6 5.5 5.4 6.2 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 82.9 84.4 84.7 84.9 85.2 85.4 85.7 86.2 86.4 86.7 86.9 87.2 87.4 85.6 [MgO] + [CaO] + [SrO] + [BaO] 14.0 15.5 15.3 15.0 14.8 14.5 14.3 13.8 13.5 13.3 13.0 12.8 12.5 14.3 [SrO] + [BaO] 6.1 6.7 6.6 6.5 6.4 6.3 6.2 6.0 5.9 5.7 5.6 5.5 5.4 6.2 [B₂O₃]/([SrO] + [BaO]) 0.5 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 6.3 3.6 3.6 3.5 3.4 3.4 3.3 3.2 3.2 3.1 3.0 3.0 2.9 1.0 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 341.2 420.2 415.1 409.9 404.7 399.6 394.4 384.1 378.9 373.7 368.6 363.4 358.2 365.7 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,759.9 1,804.7 1,804.3 1,803.9 1,803.4 1,803.0 1,802.6 1,801.7 1,801.3 1,800.9 1,800.5 1,800.0 1,799.6 1,790.4 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 38.5 40.6 40.2 39.7 39.3 38.8 38.4 37.5 37.1 36.7 36.3 36.0 35.6 38.6 (10⁻⁷/° C.) Density (g/cm³) 2.649 2.719 2.710 2.702 2.694 2.686 2.678 2.662 2.653 2.645 2.637 2.629 2.621 2.662 Strain point (° C.) 732 777 778 778 779 779 780 781 782 782 783 783 784 769 Annealing point (° C.) 793 836 837 838 839 840 842 844 845 846 847 848 849 832 Softening point (° C.) 1,032 1,066 1,069 1,072 1,075 1,079 1,083 1,092 1,096 1,101 1,106 1,111 1,116 1,085 10^(4.5) dPa · s (° C.) 1,363 1,383 1,388 1,394 1,400 1,406 1,411 1,422 1,427 1,433 1,438 1,443 1,447 1,422 10^(4.0) dPa · s (° C.) 1,522 1,536 1,543 1,551 1,558 1,565 1,573 1,588 1,596 1,604 1,612 1,620 1,628 1,601 10^(3.0) dPa · s (° C.) 1,628 1,635 1,643 1,652 1,660 1,668 1,677 1,693 1,701 1,708 1,716 1,723 1,730 1,707 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 79.7 83.9 83.6 83.4 83.2 83.0 82.8 82.3 82.1 81.9 81.7 81.5 81.3 81.0 Specific Young's modulus 30.1 30.8 30.9 30.9 30.9 30.9 30.9 30.9 31.0 31.0 31.0 31.0 31.0 30.4 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.14 0.07 0.06 0.09 0.15 0.10 0.05 0.03 0.08 0.09 0.04 0.08 0.08 0.14

TABLE 32 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 435 436 437 438 439 440 441 442 443 444 445 446 447 448 mol SiO₂ 73.2 72.7 72.3 71.1 70.6 70.2 69.8 69.4 71.8 71.6 71.5 71.3 71.2 71.0 % Al₂O₃ 12.5 13.0 13.5 15.0 15.5 16.0 16.5 17.0 14.0 13.9 13.9 13.9 13.9 13.8 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.2 0.4 06 0.8 1.0 1.2 MgO 3.3 3.3 3.3 3.2 3.2 3.2 3.2 3.2 3.3 3.3 3.2 3.2 3.2 3.2 CaO 4.7 4.7 4.7 4.6 4.6 4.6 4.5 4.5 4.7 4.6 4.6 4.6 4.6 4.6 SrO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 BaO 6.2 6.1 6.1 6.0 6.0 5.9 5.9 5.9 6.1 6.0 6.0 6.0 6.0 6.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 85.7 85.7 85.8 86.1 86.1 86.2 86.3 86.4 85.7 85.6 85.4 85.2 85.0 84.9 [MgO] + [CaO] + [SrO] + [BaO] 14.2 14.2 14.1 13.8 13.8 13.7 13.6 13.5 14.0 13.9 13.9 13.9 13.9 13.8 [SrO] + [BaO] 6.2 6.1 6.1 6.0 6.0 5.9 5.9 5.9 6.1 6.0 6.0 6.0 6.0 6.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.1 0.1 0.1 0.2 0.2 [Al₂O₃] + [B₂O₃] − [CaO] − 1.6 2.1 2.7 4.4 5.0 5.5 6.1 6.6 3.5 3.7 3.8 4.0 4.2 4.4 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 371.6 377.5 383.4 401.0 406.9 412.7 418.6 424.5 385.5 381.7 377.9 374.1 370.3 366.6 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,793.3 1,796.3 1,799.2 1,808.0 1,811.0 1,813.9 1,816.9 1,819.8 1,799.3 1,796.4 1,793.6 1,790.7 1,787.8 1,785.0 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 38.4 38.3 38.1 37.7 37.5 37.4 37.3 37.2 37.9 37.9 37.9 37.9 37.9 37.9 (10⁻⁷/° C.) Density (g/cm³) 2.664 2.666 2.668 2.674 2.676 2.678 2.680 2.682 2.667 2.665 2.663 2.661 2.658 2.656 Strain point (° C.) 772 775 778 785 787 789 791 793 776 772 768 764 761 757 Annealing point (° C.) 835 838 841 845 846 846 846 846 839 836 832 829 825 822 Softening point (° C.) 1,086 1,086 1,087 1,088 1,088 1,088 1,088 1,088 1,083 1,079 1,075 1,071 1,068 1,065 10^(4.5) dPa · s (° C.) 1,421 1,420 1,419 1,411 1,407 1,403 1,399 1,395 1,414 1,411 1,408 1,405 1,402 1,399 10^(4.0) dPa · s (° C.) 1,596 1,591 1,586 1,570 1,564 1,559 1,555 1,550 1,578 1,574 1,571 1,568 1,565 1,562 10^(3.0) dPa · s (° C.) 1,702 1,697 1,671 1,670 1,663 1,655 1,648 1,640 1,682 1,680 1,678 1,675 1,672 1,670 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 81.4 81.8 82.2 83.4 83.8 84.2 84.6 85.0 82.3 82.1 81.9 81.7 81.5 81.3 Specific Young's modulus 30.5 30.7 30.8 31.2 31.3 31.4 31.6 31.7 30.9 30.8 30.8 30.7 30.7 30.6 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.04 0.09 0.14 0.13 0.10 0.15 0.04 0.04 0.05 0.05 0.09 0.11 0.09 0.15

TABLE 33 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 449 450 451 452 453 454 455 456 457 458 459 460 461 462 mol SiO₂ 70.9 70.7 70.6 70.5 70.3 70.2 70.0 69.9 69.7 74.1 73.7 73.4 73.0 72.6 % Al₂O₃ 13.8 13.8 13.7 13.7 13.7 13.7 13.6 13.6 13.6 14.4 14.4 14.3 14.2 14.1 B₂O₃ 1.4 1.6 1.8 2.0 2.2 2.4 2.6 2.8 3.0 0.0 0.0 0.0 0.0 0.0 MgO 3.2 3.2 3.2 3.2 3.2 3.2 3.2 3.2 3.2 0.3 0.8 1.3 1.8 2.3 CaO 4.6 4.6 4.6 4.6 4.6 4.6 4.5 4.5 4.5 4.8 4.8 4.8 4.7 4.7 SrO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 BaO 6.0 6.0 6.0 5.9 5.9 5.9 5.9 5.9 5.9 6.3 6.2 6.2 6.2 6.1 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 84.7 84.5 84.4 84.2 84.0 83.8 83.7 83.5 83.3 88.5 88.1 87.6 87.2 86.8 [MgO] + [CaO] + [SrO] + [BaO] 13.8 13.8 13.7 13.7 13.7 13.7 13.6 13.6 13.6 11.4 11.8 12.3 12.7 13.1 [SrO] + [BaO] 6.0 6.0 6.0 5.9 5.9 5.9 5.9 5.9 5.9 6.3 6.2 6.2 6.2 6.1 [B₂O₃]/([SrO] + [BaO]) 0.2 0.3 0.3 0.3 0.4 0.4 0.4 0.5 0.5 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 4.6 4.8 5.0 5.2 5.4 5.6 5.8 6.0 6.2 3.4 3.4 3.3 3.3 3.3 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 362.8 359.0 355.2 351.4 347.7 343.9 340.1 336.3 332.5 382.8 383.9 385.0 386.0 387.1 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,782.1 1,779.2 1,776.3 1,773.5 1,770.6 1,767.7 1,764.9 1,762.0 1,759.1 1,817.9 1,815.3 1,812.6 1,810.0 1,807.3 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 37.9 37.8 37.8 37.8 37.8 37.8 37.8 37.8 37.7 36.0 36.3 36.6 37.0 37.3 (10⁻⁷/° C.) Density (g/cm³) 2.654 2.652 2.649 2.647 2.645 2.642 2.640 2.638 2.636 2.651 2.654 2.657 2.660 2.663 Strain point (° C.) 754 750 747 744 741 739 736 734 732 809 805 801 795 790 Annealing point (° C.) 819 815 812 809 806 803 800 797 794 876 870 864 858 853 Softening point (° C.) 1,062 1,058 1,055 1,052 1,049 1,046 1,043 1,039 1,036 1,128 1,125 1,121 1,115 1,106 10^(4.5) dPa · s (° C.) 1,396 1,394 1,391 1,387 1,384 1,381 1,378 1,375 1,372 1,464 1,456 1,448 1,440 1,432 10^(4.0) dPa · s (° C.) 1,559 1,556 1,553 1,550 1,547 1,543 1,540 1,537 1,534 1,642 1,631 1,620 1,610 1,600 10^(3.0) dPa · s (° C.) 1,667 1,664 1,661 1,658 1,654 1,651 1,648 1,645 1,641 1,735 1,727 1,719 1,710 1,702 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 81.0 80.8 80.6 80.4 80.2 80.0 79.8 79.5 79.3 80.8 81.1 81.4 81.7 82.0 Specific Young's modulus 30.5 30.5 30.4 30.4 30.3 30.3 30.2 30.2 30.1 30.5 30.6 30.6 30.7 30.8 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.05 0.11 0.08 0.15 0.13 0.13 0.15 0.05 0.07 0.12 0.07 0.06 0.12 0.07

TABLE 34 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 463 464 465 466 467 468 469 470 471 472 473 474 475 476 mol SiO₂ 72.2 71.5 71.1 70.8 70.4 70.0 69.6 74.1 73.8 73.4 73.0 72.6 72.3 71.5 % Al₂O₃ 14.1 13.9 13.9 13.8 13.7 13.6 13.6 14.4 14.4 14.3 14.2 14.1 14.1 13.9 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 2.8 3.8 4.3 4.8 5.3 5.8 6.3 3.4 3.4 3.3 3.3 3.3 3.3 3.2 CaO 4.7 4.6 4.6 4.6 4.6 4.5 4.5 1.7 2.2 2.7 3.2 3.7 4.2 5.2 SrO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 BaO 6.1 6.0 6.0 6.0 5.9 5.9 5.9 6.3 6.2 6.2 62 6.1 96.1 6.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 86.3 85.4 85.0 84.5 84.1 83.6 83.2 88.6 88.1 87.7 87.2 86.6 86.3 85.4 [MgO] + [CaO] + [SrO] + [BaO] 13.6 14.5 14.9 15.4 15.8 16.3 16.7 11.3 11.8 12.2 12.7 13.1 13.6 14.5 [SrO] + [BaO] 6.1 6.0 6.0 6.0 5.9 5.9 5.9 6.3 6.2 6.2 6.2 6.1 6.1 6.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 3.3 3.2 3.2 3.2 3.2 3.2 3.2 6.5 5.9 5.4 4.9 4.3 3.8 2.7 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 388.2 390.4 391.5 392.6 393.7 394.7 395.8 398.2 396.7 395.2 393.7 392.2 390.7 387.6 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,804.6 1,799.3 1,796.7 1,794.0 1,791.4 1,788.7 1,786.0 1,814.4 1,812.4 1,810.3 1,808.0 1,806.2 1,804.1 1,800.0 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 37.6 38.3 38.7 39.0 39.4 39.7 40.1 33.7 34.4 35.1 35.8 36.5 37.3 38.8 (10⁻⁷/° C.) Density (g/cm³) 2.667 2.673 2.676 2.680 2.683 2.686 2.689 2.643 2.648 2.652 2.657 2.661 2.666 2.675 Strain point (° C.) 785 776 772 769 766 764 762 798 795 792 789 786 783 777 Annealing point (° C.) 847 838 833 829 825 822 819 861 858 856 852 849 846 839 Softening point (° C.) 1,096 1,078 1,071 1,065 1,060 1,056 1,052 1,128 1,124 1,118 1,111 1,103 1,095 1,079 10^(4.5) dPa · s (° C.) 1,424 1,408 1,400 1,391 1,383 1,374 1,366 1,457 1,450 1,444 1,437 1,430 1,423 1,409 10^(4.0) dPa · s (° C.) 1,590 1,571 1,561 1,552 1,543 1,534 1,525 1,637 1,626 1,616 1,606 1,597 1,588 1,572 10^(3.0) dPa · s (° C.) 1,693 1,675 1,665 1,656 1,646 1,636 1,626 1,721 1,716 1,710 1,705 1,698 1,691 1,677 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 82.3 82.9 83.2 83.5 83.7 84.0 84.3 82.2 82.3 82.4 82.4 82.5 82.5 82.6 Specific Young's modulus 30.9 31.0 31.1 31.1 31.2 31.3 31.4 31.1 31.1 31.1 31.0 31.0 31.0 30.9 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.10 0.06 0.05 0.03 0.14 0.11 0.04 0.06 0.10 0.015 0.05 0.05 0.11 0.13

TABLE 35 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 477 478 479 480 481 482 483 484 485 486 487 488 489 490 mol SiO₂ 71.7 70.7 70.4 70.0 69.6 71.8 71.6 71.5 71.3 71.2 71.0 70.9 70.7 70.6 % Al₂O₃ 13.8 13.8 13.7 13.6 13.6 14.0 13.9 13.9 13.9 13.9 13.8 13.8 13.8 13.7 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 3.2 3.2 3.2 3.2 3.2 3.3 3.3 3.2 3.2 3.2 3.2 3.2 3.2 3.2 CaO 5.7 6.2 6.7 7.2 7.7 4.7 4.6 4.6 4.6 4.6 4.6 4.6 4.6 4.6 SrO 0.0 0.0 0.0 0.0 0.0 0.2 0.4 0.6 0.8 1.0 1.2 1.4 1.6 1.8 BaO 6.0 6.0 5.9 5.9 5.9 6.1 6.0 6.0 6.0 6.0 6.0 6.0 6.0 6.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 85.0 84.5 84.1 83.6 83.2 85.7 85.6 85.4 85.2 85.0 84.9 84.7 84.5 84.4 [MgO] + [CaO] + [SrO] + [BaO] 14.9 15.4 15.8 16.3 16.7 14.2 14.3 14.5 14.7 14.9 15.0 15.2 15.4 15.5 [SrO] + [BaO] 6.0 6.0 5.9 5.9 5.9 6.3 6.4 6.6 6.8 7.0 7.2 7.4 7.6 7.8 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 2.1 1.6 1.1 0.5 0.0 3.1 2.9 2.6 2.4 2.2 2.0 1.8 1.6 1.4 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 386.1 384.6 383.1 381.5 380.0 391.3 393.3 395.3 397.3 399.3 401.4 403.4 405.4 407.4 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,797.9 1,795.8 1,793.8 1,791.7 1,789.6 1,801.7 1,801.1 1,800.6 1,800.1 1,799.6 1,799.1 1,798.6 1,798.1 1,797.6 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 39.5 40.3 41.1 41.9 42.6 38.3 38.7 39.0 39.4 39.8 40.1 40.5 40.9 41.2 (10⁻⁷/° C.) Density (g/cm³) 2.679 2.684 2.688 2.693 2.697 2.674 2.678 2.683 2.687 2.692 2.696 2.700 2.705 2.709 Strain point (° C.) 774 771 769 766 762 780 779 778 777 776 775 774 773 772 Annealing point (° C.) 835 831 828 824 820 842 841 840 839 838 837 835 834 833 Softening point (° C.) 1,072 1,066 1,061 1,056 1,052 1,085 1,083 1,081 1,079 1,077 1,075 1,073 1,071 1,069 10^(4.5) dPa · s (° C.) 1,401 1,394 1,386 1,378 1,370 1,415 1,413 1,411 1,409 1,406 1,404 1,402 1,400 1,398 10^(4.0) dPa · s (° C.) 1,564 1,556 1,547 1,538 1,529 1,579 1,576 1,574 1,572 1,570 1,568 1,565 1,563 1,560 10^(3.0) dPa · s (° C.) 1,669 1,660 1,652 1,643 1,634 1,683 1,681 1,679 1,677 1,675 1,672 1,670 1,668 1,665 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 82.7 82.7 82.8 82.8 82.9 82.5 82.5 82.4 82.4 82.3 82.3 82.2 82.2 82.1 Specific Young's modulus 30.9 30.8 30.8 30.8 30.7 30.9 30.8 32.7 30.7 30.6 30.5 30.5 30.4 30.3 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.14 0.09 0.12 0.11 0.11 0.10 0.07 0.05 0.07 0.10 0.07 0.03 0.08 0.04

TABLE 36 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 491 492 493 494 495 496 497 498 499 500 501 502 503 504 mol SiO₂ 70.5 70.3 70.2 70.0 69.9 69.7 74.2 73.8 73.4 73.0 72.6 72.3 71.5 71.1 % Al₂O₃ 13.7 13.7 13.7 13.6 13.6 13.6 14.4 14.4 14.3 14.2 14.1 14.1 13.9 13.8 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 3.2 3.2 3.2 3.2 3.2 3.2 3.4 3.4 3.3 3.3 3.3 3.3 3.2 3.2 CaO 4.6 4.6 4.6 4.5 4.5 4.5 4.8 4.8 4.8 4.7 4.7 4.7 4.6 4.6 SrO 2.0 2.2 2.4 2.6 2.8 3.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 BaO 5.9 5.9 5.9 5.9 5.9 5.9 3.1 3.6 4.1 4.6 5.1 5.6 6.6 7.1 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 84.2 84.0 83.8 83.7 83.5 83.3 88.6 88.2 87.7 87.2 86.8 86.3 85.4 85.0 [MgO] + [CaO] + [SrO] + [BaO] 15.7 15.9 16.1 16.2 16.4 16.6 11.3 11.7 12.2 12.7 13.1 13.6 14.5 14.9 [SrO] + [BaO] 7.9 8.1 8.3 8.5 8.7 8.9 3.1 3.6 4.1 4.6 5.1 5.6 6.6 7.1 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 1.2 1.0 0.8 0.6 0.4 0.2 6.5 6.0 5.4 4.9 4.3 3.8 2.7 2.1 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 409.4 411.5 413.5 415.5 417.5 419.5 351.0 357.4 363.9 370.3 376.8 383.2 396.1 402.5 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,797.1 1,796.6 1,796.1 1,795.6 1,795.0 1,794.5 1,811.8 1,810.1 1,808.5 1,806.9 1,805.3 1,803.7 1,800.4 1,798.8 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 41.6 42.0 42.3 42.7 43.1 43.4 32.0 32.9 33.9 34.9 35.9 37.0 39.1 40.2 (10⁻⁷/° C.) Density (g/cm³) 2.713 2.718 2.722 2.727 2.731 2.735 2.556 2.575 2.594 2.613 2.633 2.652 2.690 2.709 Strain point (° C.) 771 770 769 767 766 765 792 790 788 787 758 783 778 775 Annealing point (° C.) 832 830 829 827 826 824 850 850 849 848 846 845 840 837 Softening point (° C.) 1,067 1,065 1,063 1,062 1,060 1,058 1,114 1,111 1,107 1,102 1,097 1,092 1,082 1,077 10^(4.5) dPa · s (° C.) 1,396 1,394 1,391 1,389 1,387 1,385 1,437 1,434 1,431 1,428 1,424 1,420 1,412 1,408 10^(4.0) dPa · s (° C.) 1,558 1,555 1,553 1,550 1,548 1,545 1,613 1,606 1,600 1,594 1,589 1,585 1,576 1,572 10^(3.0) dPa · s (° C.) 1,663 1,661 1,658 1,656 1,653 1,650 1,698 1,696 1,695 1,693 1,690 1,688 1,681 1,677 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 82.1 82.1 82.0 82.0 81.9 81.9 84.2 84.0 83.7 83.4 83.1 82.8 82.3 82.0 Specific Young's modulus 30.3 30.2 30.1 30.1 30.0 29.9 33.0 32.6 32.3 31.9 31.6 31.2 30.6 30.3 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.10 0.04 0.12 0.14 0.10 0.10 0.11 0.09 0.15 0.13 0.04 0.03 0.04 0.14

TABLE 37 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 505 506 507 508 509 510 511 512 513 514 515 516 517 518 mol SiO₂ 70.7 70.3 70.0 69.6 68.9 69.4 69.9 70.4 70.9 71.4 72.4 72.9 73.4 73.9 % Al₂O₃ 13.8 13.7 13.6 13.5 14.4 14.2 13.9 13.7 13.5 13.2 12.8 12.5 12.3 12.1 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 3.2 3.2 3.2 3.2 5.5 5.4 5.4 5.3 5.2 5.1 4.9 4.8 4.7 4.6 CaO 4.6 4.6 4.5 4.5 2.8 2.7 2.7 2.6 2.6 2.5 2.5 2.4 2.4 2.3 SrO 0.0 0.0 0.0 0.0 2.8 2.7 2.7 2.6 2.6 2.5 2.5 2.4 2.4 2.3 BaO 7.6 8.1 8.6 9.1 5.5 5.4 5.4 5.3 5.2 5.1 4.9 4.8 4.7 4.6 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 84.5 84.0 83.6 83.1 83.3 83.6 83.8 84.1 84.4 84.6 85.2 85.4 85.7 86.0 [MgO] + [CaO] + [SrO] + [BaO] 15.4 15.9 16.3 16.8 16.6 16.3 16.1 15.8 15.5 15.3 14.7 14.5 14.2 13.9 [SrO] + [BaO] 7.6 8.1 8.6 9.1 8.3 8.2 8.0 7.9 7.8 7.6 7.4 7.2 7.1 7.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 1.6 1.0 0.5 −0.1 3.3 3.3 3.2 3.2 3.1 3.1 2.9 2.9 2.8 2.8 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 409.0 415.4 421.9 428.3 433.7 428.3 422.9 417.6 412.2 406.8 396.0 390.6 385.2 379.9 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,797.2 1,795.6 1,794.0 1,792.3 1,795.3 1,795.0 1,794.7 1,794.4 1,794.2 1,793.9 1,793.3 1,793.1 1,792.8 1,792.5 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 41.3 42.4 43.5 44.6 41.2 40.7 40.3 39.8 39.3 38.9 38.0 37.6 37.2 36.8 (10⁻⁷/° C.) Density (g/cm³) 2.729 2.748 2.767 2.786 2.721 2.713 2.705 2.696 2.688 2.680 2.664 2.655 2.647 2.639 Strain point (° C.) 772 769 766 762 756 767 767 768 768 769 770 770 771 771 Annealing point (° C.) 834 831 827 823 825 826 827 828 829 830 832 833 835 836 Softening point (° C.) 1,073 1,069 1,065 1,060 1,058 1,061 1,063 1,065 1,068 1,071 1,078 1,083 1,087 1,092 10^(4.5) dPa · s (° C.) 1,404 1,399 1,395 1,390 1,372 1,378 1,384 1,390 1,396 1,402 1,413 1,418 1,424 1,429 10^(4.0) dPa · s (° C.) 1,567 1,562 1,556 1,550 1,529 1,536 1,543 1,551 1,558 1,566 1,581 1,589 1,597 1,605 10^(3.0) dPa · s (° C.) 1,673 1,668 1,663 1,658 1,628 1,637 1,646 1,654 1,663 1,671 1,687 1,695 1,703 1,710 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 81.7 81.4 81.1 80.8 83.9 83.7 83.5 83.2 83.0 82.8 82.4 82.2 81.9 81.7 Specific Young's modulus 29.9 29.6 29.3 29.0 30.8 30.8 30.9 30.9 30.9 30.9 30.9 30.9 31.0 31.0 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.14 0.04 0.04 0.05 0.12 0.05 0.05 0.09 0.13 0.13 0.13 0.12 0.10 0.12

TABLE 38 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 519 520 521 522 523 524 525 526 527 528 529 530 531 532 mol SiO₂ 74.4 74.9 74.4 74.0 73.6 73.1 72.7 72.3 71.5 71.1 70.7 70.2 69.8 69.4 % Al₂O₃ 11.8 11.6 10.0 10.5 11.0 11.5 12.0 12.5 13.5 14.0 14.5 15.0 15.5 16.0 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 4.6 4.5 5.2 5.1 5.1 5.1 5.1 5.0 5.0 4.9 4.9 4.9 4.9 4.8 CaO 2.3 2.2 2.6 2.6 2.6 2.5 2.5 2.5 2.5 2.5 2.5 2.4 2.4 2.4 SrO 2.3 2.2 2.6 2.6 2.6 2.5 2.5 2.5 2.5 2.5 2.5 2.4 2.4 2.4 BaO 4.6 4.5 5.2 5.1 5.1 5.1 5.1 5.0 5.0 4.9 4.9 4.9 4.9 4.8 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 86.2 86.5 84.4 84.5 84.6 84.6 84.7 84.8 85.0 85.1 85.2 85.2 85.3 85.4 [MgO] + [CaO] + [SrO] + [BaO] 13.7 13.4 15.5 15.4 15.3 15.3 15.2 15.1 14.9 14.8 14.7 14.7 14.6 14.5 [SrO] + [BaO] 6.8 6.7 7.8 7.7 7.7 7.6 7.6 7.5 7.5 7.4 7.4 7.3 7.3 7.2 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 2.7 2.7 −0.3 0.2 0.8 1.3 1.9 2.4 3.6 4.1 4.7 5.2 5.8 6.3 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 374.5 369.1 367.0 372.7 378.4 384.2 389.9 395.7 407.1 412.9 418.6 424.4 430.1 435.8 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,792.2 1,792.0 1,775.9 1,778.8 1,781.8 1,784.7 1,787.7 1,790.7 1,796.6 1,799.5 1,802.5 1,805.5 1,808.4 1,811.4 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 36.4 36.1 39.6 39.4 39.2 39.0 38.8 38.6 38.3 38.1 38.0 37.9 37.7 37.6 (10⁻⁷/° C.) Density (g/cm³) 2.631 2.622 2.660 2.662 2.664 2.666 2.668 2.670 2.674 2.676 2.678 2.680 2.682 2.684 Strain point (° C.) 772 772 751 754 757 760 763 766 772 774 776 778 779 781 Annealing point (° C.) 837 738 811 814 818 821 825 828 834 836 837 839 839 839 Softening point (° C.) 1,097 1,102 1,062 1,066 1,069 1,071 1,073 1,074 1,075 1,075 1,074 1,074 1,073 1,072 10^(4.5) dPa · s (° C.) 1,434 1,439 1,410 1,411 1,411 1,411 1,410 1,409 1,405 1,402 1,399 1,396 1,392 1,388 10^(4.0) dPa · s (° C.) 1,613 1,621 1,595 1,592 1,589 1,586 1,582 1,578 1,568 1,563 1,558 1,552 1,547 1,542 10^(3.0) dPa · s (° C.) 1,718 1,725 1,700 1,699 1,696 1,693 1,689 1,685 1,673 1,667 1,660 1,653 1,645 1,638 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 81.5 81.3 80.2 80.6 81.0 81.4 81.8 82.2 83.0 83.4 83.8 84.2 84.6 84.9 Specific Young's modulus 31.0 31.0 30.2 30.3 30.4 30.5 30.7 30.8 31.0 31.2 31.3 31.4 31.5 31.7 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.03 0.15 0.08 0.05 0.15 0.03 0.05 0.12 0.08 0.12 0.09 0.05 0.15 0.10

TABLE 39 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 533 534 535 536 537 538 539 540 541 542 543 544 545 546 mol SiO₂ 71.8 71.6 71.5 71.3 71.2 71.0 10.9 70.7 70.6 70.5 70.3 70.2 70.0 69.9 % Al₂O₃ 13.0 12.9 12.9 12.9 12.9 12.8 12.8 12.8 12.8 12.7 12.7 12.7 12.7 12.6 B₂O₃ 0.2 0.4 0.6 0.8 1.0 1.2 1.4 1.6 1.8 2.0 2.2 2.4 2.6 2.8 MgO 5.0 5.0 5.0 5.0 4.9 4.9 4.9 4.9 4.9 4.9 4.9 4.9 4.9 4.9 CaO 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.4 2.4 2.4 2.4 2.4 SrO 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.5 2.4 2.4 2.4 2.4 2.4 BaO 5.0 5.0 5.0 5.0 4.9 4.9 4.9 4.9 4.9 4.9 4.9 4.9 4.9 4.9 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 84.7 84.6 84.4 84.2 84.1 83.9 83.7 83.5 83.4 83.2 83.0 82.9 82.7 82.5 [MgO] + [CaO] + [SrO] + [BaO] 15.0 14.9 14.9 14.9 14.9 14.8 14.8 14.8 14.7 14.7 14.7 14.6 14.6 14.6 [SrO] + [BaO] 7.5 7.5 7.5 7.4 7.4 7.4 7.4 7.4 7.4 7.3 7.3 7.3 7.3 7.3 [B₂O₃]/([SrO] + [BaO]) 0.0 0.1 0.1 0.1 0.1 0.2 0.2 0.2 0.2 0.3 0.3 0.3 0.4 0.4 [Al₂O₃] + [B₂O₃] − [CaO] − 3.2 3.4 3.6 3.8 4.0 4.2 4.4 4.6 4.7 4.9 5.1 5.3 5.5 5.7 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 397.6 393.8 390.0 386.2 382.4 378.6 374.8 371.0 367.2 363.4 359.6 355.8 352.0 348.1 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,790.8 1,787.9 1,785.1 1,782.2 1,779.4 1,776.5 1,773.7 1,770.8 1,768.0 1,765.1 1,762.3 1,759.4 1,756.6 1,753.7 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 38.4 38.4 38.4 38.4 38.4 38.3 38.3 38.3 38.3 38.3 38.3 38.3 38.2 38.2 (10⁻⁷/° C.) Density (g/cm³) 2.669 2.667 2.665 2.663 2.660 2.658 2.656 2.653 2.651 2.649 2.647 2.644 2.642 2.640 Strain point (° C.) 766 762 759 756 753 750 747 744 741 739 736 734 731 729 Annealing point (° C.) 828 825 821 818 815 812 809 806 803 800 797 794 791 788 Softening point (° C.) 1,071 1,098 1,064 1,061 1,057 1,054 1,051 1,047 1,044 1,040 1,037 1,033 1,029 1,025 10^(4.5) dPa · s (° C.) 1,405 1,402 1,399 1,396 1,393 1,390 1,387 1,384 1,381 1,378 1,375 1,372 1,369 1,366 10^(4.0) dPa · s (° C.) 1,571 1,568 1,565 1,562 1,559 1,556 1,553 1,550 1,547 1,544 1,541 1,538 1,535 1,531 10^(3.0) dPa · s (° C.) 1,676 1,674 1,671 1,668 1,665 1,662 1,658 1,655 1,652 1,648 1,645 1,642 1,638 1,635 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 82.4 82.2 81.9 81.7 81.5 81.3 81.1 80.9 80.6 80.4 80.2 80.0 79.8 79.6 Specific Young's modulus 30.9 30.8 30.7 30.7 30.6 30.6 30.5 30.5 30.4 30.4 30.3 30.3 30.2 30.1 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.10 0.03 0.06 0.09 0.07 0.12 0.13 0.12 0.06 0.06 0.04 0.10 0.05 0.04

TABLE 40 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 547 548 549 550 551 552 553 554 555 556 557 558 559 560 mol SiO₂ 69.7 74.2 73.8 73.4 73.0 72.7 72.3 71.5 71.1 70.8 70.4 70.0 69.6 73.7 % Al₂O₃ 12.6 13.4 13.3 13.3 13.2 13.1 13.1 12.9 12.9 12.8 12.7 12.7 12.6 13.3 B₂O₃ 3.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 4.8 2.0 2.5 3.0 3.5 4.0 4.5 5.5 6.0 6.5 7.0 7.5 8.0 5.1 CaO 2.4 2.6 2.6 2.6 2.5 2.5 2.5 2.5 2.5 2.5 2.4 2.4 2.4 0.0 SrO 2.4 2.6 2.6 2.6 2.5 2.5 2.5 2.5 2.5 2.4 2.4 2.4 2.4 2.6 BaO 4.8 5.2 5.1 5.1 5.1 5.1 5.0 5.0 4.9 4.9 4.9 4.9 4.8 5.1 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 82.4 87.6 87.1 86.7 86.2 85.8 85.3 84.5 84.0 83.6 83.1 82.7 82.2 87.1 [MgO] + [CaO] + [SrO] + [BaO] 14.5 12.3 12.8 13.2 13.7 14.1 14.6 15.4 15.9 16.3 16.8 17.2 17.7 12.8 [SrO] + [BaO] 7.3 7.7 7.7 7.7 7.6 7.6 7.5 7.5 7.4 7.4 7.3 7.3 7.3 7.7 [B₂O₃]/([SrO] + [BaO]) 0.4 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 5.9 3.1 3.1 3.1 3.0 3.0 3.0 3.0 3.0 3.0 2.9 2.9 2.9 5.6 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 344.3 395.1 396.2 397.2 398.3 399.3 400.4 402.4 403.5 404.5 405.6 406.6 407.7 409.1 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,750.9 1,809.6 1,806.9 1,804.3 1,801.6 1,798.9 1,796.3 1,791.0 1,788.3 1,785.6 1,783.0 1,780.3 1,777.7 1,803.5 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 38.2 36.4 36.8 37.1 37.4 37.8 38.1 38.8 39.1 39.5 39.8 40.2 40.6 34.9 (10⁻⁷/° C.) Density (g/cm³) 2.637 2.652 2.656 2.659 2.662 2.665 2.669 2.675 2.678 2.682 2.685 2.688 2.691 2.650 Strain point (° C.) 727 798 792 786 781 776 772 767 764 763 761 760 758 784 Annealing point (° C.) 786 863 857 851 846 841 836 827 823 820 817 814 812 851 Softening point (° C.) 1,021 1,127 1,121 1,112 1,102 1,091 1,082 1,069 1,064 1,059 1,054 1,049 1,044 1,114 10^(4.5) dPa · s (° C.) 1,363 1,456 1,448 1,440 1,432 1,424 1,416 1,399 1,391 1,382 1,374 1,365 1,356 1,442 10^(4.0) dPa · s (° C.) 1,528 1,634 1,623 1,613 1,603 1,593 1,583 1,564 1,554 1,544 1,535 1,525 1,515 1,615 10^(3.0) dPa · s (° C.) 1,631 1,733 1,724 1,716 1,707 1,698 1,689 1,669 1,659 1,649 1,639 1,629 1,618 1,714 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 79.3 80.8 81.1 81.4 81.7 82.0 82.3 82.9 83.2 83.5 83.8 84.1 84.4 82.3 Specific Young's modulus 30.1 30.5 30.5 30.6 30.7 30.8 30.8 31.0 31.1 31.1 31.2 31.3 31.3 31.1 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.07 0.11 0.09 0.06 0.12 0.11 0.10 0.14 0.05 0.07 0.06 0.11 0.11 0.14

TABLE 41 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 561 562 563 564 565 566 567 568 569 570 571 572 573 574 mol SiO₂ 73.4 73.0 72.6 72.3 71.5 71.2 70.8 70.4 70.1 69.7 73.7 73.4 73.0 72.6 % Al₂O₃ 13.3 13.2 13.1 13.1 12.9 12.9 12.8 12.7 12.7 12.6 13.3 13.3 13.2 13.1 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 5.1 5.1 5.1 5.0 5.0 4.9 4.9 4.9 4.9 4.8 5.1 5.1 5.1 5.1 CaO 0.5 1.0 1.5 2.0 3.0 3.5 4.0 4.5 5.0 5.5 2.6 2.6 2.5 2.5 SrO 2.6 2.5 2.5 2.5 2.5 2.5 2.5 2.4 2.4 2.4 0.0 0.5 1.0 1.5 BaO 5.1 5.1 5.1 5.0 5.0 4.9 4.9 4.9 4.9 4.8 5.1 5.1 5.1 5.1 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 86.6 86.2 85.8 85.3 84.5 84.0 83.6 83.2 82.7 82.3 87.1 86.6 86.2 85.8 [MgO] + [CaO] + [SrO] + [BaO] 13.3 13.7 14.1 14.6 15.4 15.9 16.3 16.7 17.2 17.6 12.8 13.3 13.7 14.1 [SrO] + [BaO] 7.7 7.6 7.6 7.5 7.5 7.4 7.4 7.3 7.3 7.3 5.1 5.6 6.1 6.6 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 5.1 4.6 4.1 3.5 2.5 1.9 1.4 0.9 0.4 −0.2 5.6 5.1 4.6 4.1 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 407.6 406.0 404.5 402.9 399.9 398.3 396.8 395.2 393.7 392.1 375.8 380.9 386.0 391.2 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,801.5 1,799.5 1,797.6 1,795.6 1,791.6 1,789.7 1,787.7 1,785.7 1,783.7 1,781.8 1,799.9 1,798.7 1,797.4 1,796.1 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 35.6 36.3 37.0 37.7 39.2 39.9 40.7 41.4 42.2 42.9 34.1 34.9 35.8 36.6 (10⁻⁷/° C.) Density (g/cm³) 2.654 2.659 2.663 2.667 2.676 2.681 2.685 2.689 2.694 22.698 2.616 2.627 2.638 2.649 Strain point (° C.) 781 778 775 772 766 763 760 757 754 751 779 777 775 774 Annealing point (° C.) 847 843 839 835 827 823 819 815 810 806 844 842 840 837 Softening point (° C.) 1,105 1,097 1,089 1,081 1,069 1,063 1,058 1,052 1,047 1,041 1,100 1,094 1,089 1,084 10^(4.5) dPa · s (° C.) 1,435 1,429 1,422 1,415 1,400 1,393 1,385 1,378 1,370 1,362 1,432 1,428 1,423 1,418 10^(4.0) dPa · s (° C.) 1,606 1,598 1,590 1,582 1,565 1,557 1,548 1,539 1,529 1,520 1,602 1,596 1,590 1,585 10^(3.0) dPa · s (° C.) 1,708 1,701 1,694 1,687 1,671 1,663 1,654 1,645 1,636 1,627 1,703 1,699 1,695 1,690 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 82.4 82.4 82.5 82.5 82.6 82.7 82.7 82.8 82.8 82.9 83.2 83.1 82.9 82.8 Specific Young's modulus 31.0 31.0 31.0 30.9 30.9 30.8 30.8 30.8 30.8 30.7 31.8 31.6 31.4 31.3 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.12 0.08 0.14 0.03 0.15 0.15 0.06 0.09 0.13 0.06 0.15 0.15 0.03 0.13

TABLE 42 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 575 576 577 578 579 580 581 582 583 584 585 586 587 588 mol SiO₂ 72.3 71.5 71.2 70.8 70.4 70.1 69.7 74.2 73.8 73.4 73.0 72.7 72.3 71.5 % Al₂O₃ 13.1 12.9 12.9 12.8 12.7 12.7 12.6 13.4 13.3 13.3 13.2 13.1 13.1 12.9 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 MgO 5.0 5.0 4.9 4.9 4.9 4.9 4.8 5.2 5.1 5.1 5.1 5.1 5.0 5.0 CaO 2.5 2.5 2.5 2.5 2.4 2.4 2.4 2.6 2.6 2.6 2.5 2.5 2.5 2.5 SrO 2.0 3.0 3.5 4.0 4.5 5.0 5.5 2.6 2.6 2.6 2.5 2.5 2.5 2.5 BaO 5.0 5.0 4.9 4.9 4.9 4.9 4.8 2.0 2.5 3.0 3.5 4.0 4.5 5.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 85.3 84.5 84.0 83.6 83.2 82.7 82.3 87.6 87.1 86.7 86.2 85.8 85.3 84.5 [MgO] + [CaO] + [SrO] + [BaO] 14.6 15.4 15.9 16.3 16.7 17.2 17.6 12.3 12.8 13.2 13.7 14.1 14.6 15.4 [SrO] + [BaO] 7.0 8.0 8.4 8.9 9.4 9.9 10.3 4.6 5.1 5.6 6.0 6.5 7.0 8.0 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 3.5 2.5 1.9 1.4 0.9 0.4 −0.2 6.3 5.7 5.2 4.6 4.1 3.5 2.5 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 396.3 406.5 411.6 416.8 421.9 427.0 432.1 363.6 369.9 376.2 382.5 388.8 395.1 407.7 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,794.9 1,792.4 1,791.1 1,789.8 1,788.6 1,787.3 1,786.1 1,802.9 1,801.4 1,799.8 1,798.3 1,796.7 1,795.2 1,792.1 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 37.5 39.4 40.3 41.2 42.2 43.1 44.0 32.5 33.4 34.4 35.4 36.4 37.4 39.5 (10⁻⁷/° C.) Density (g/cm³) 2.661 2.683 2.694 2.705 2.717 2.728 2.739 2.558 2.577 2.596 2.615 2.634 2.653 2.691 Strain point (° C.) 771 767 764 761 758 755 752 781 779 778 776 774 772 766 Annealing point (° C.) 834 828 824 821 817 813 809 844 843 841 839 837 834 828 Softening point (° C.) 1,079 1,070 1,066 1,061 1,056 1,051 1,046 1,100 1,095 1,091 1,086 1,082 1,078 1,071 10^(4.5) dPa · s (° C.) 1,413 1,402 1,397 1,391 1,386 1,380 1,374 1,429 1,426 1,422 1,419 1,415 1,411 1,403 10^(4.0) dPa · s (° C.) 1,579 1,567 1,561 1,554 1,547 1,540 1,532 1,600 1,595 1,590 1,586 1,582 1,578 1,569 10^(3.0) dPa · s (° C.) 1,685 1,673 1,667 1,661 1,654 1,647 1,640 1,697 1,695 1,693 1,690 1,687 1,683 1,675 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 82.7 82.5 82.3 82.2 82.1 82.0 81.9 84.3 84.0 83.7 83.4 83.1 82.9 82.3 Specific Young's modulus 31.1 30.7 30.6 30.4 30.2 30.1 29.9 32.9 32.6 32.2 31.9 31.6 31.2 30.6 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.11 0.14 0.08 0.11 0.12 0.15 0.05 0.13 0.03 0.05 0.04 0.04 0.07 0.12

TABLE 43 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 589 590 591 592 593 594 595 596 597 598 599 600 601 602 mol SiO₂ 71.1 70.8 70.4 70.0 69.6 67.6 68.1 68.6 69.1 69.6 70.1 71.1 71.6 72.1 % Al₂O₃ 12.9 12.8 12.7 12.7 12.6 14.4 14.2 14.0 13.8 13.5 13.3 12.9 12.7 12.4 B₂O₃ 0.0 0.0 0.0 0.0 0.0 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 MgO 4.9 4.9 4.9 4.9 4.8 6.7 6.6 6.5 6.4 6.3 6.2 6.0 5.9 5.8 CaO 2.5 2.5 2.4 2.4 2.4 4.2 4.1 4.1 4.0 3.9 3.9 3.7 3.7 3.6 SrO 2.5 2.5 2.4 2.4 2.4 2.3 2.3 2.2 2.2 2.2 2.1 2.1 2.0 2.0 BaO 6.0 6.5 7.0 7.5 8.0 4.3 4.2 4.2 4.1 4.0 4.0 3.8 3.8 3.7 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 84.0 83.6 83.1 82.7 82.2 82.0 82.3 82.6 82.9 83.1 83.4 84.0 84.3 84.5 [MgO] + [CaO] + [SrO] + [BaO] 15.9 16.3 16.8 17.2 17.7 17.5 17.3 17.0 16.7 16.4 16.2 15.6 15.4 15.1 [SrO] + [BaO] 8.5 9.0 9.4 9.9 10.4 6.6 6.5 6.4 6.3 6.2 6.1 5.9 5.8 5.7 [B₂O₃]/([SrO] + [BaO]) 0.0 0.0 0.0 0.0 0.0 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [Al₂O₃] + [B₂O₃] − [CaO] − 1.9 1.4 0.8 0.3 −0.3 4.0 3.9 3.8 3.8 3.7 3.7 3.5 3.5 3.4 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 414.0 420.3 426.6 432.9 439.2 410.6 405.7 400.9 396.1 391.3 386.5 376.9 372.1 367.3 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,790.5 1,789.0 1,787.4 1,785.8 1,784.3 1,784.3 1,784.2 1,784.1 1,784.0 1,783.9 1,783.8 1,783.6 1,783.5 1,783.4 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 40.6 41.7 42.7 43.8 44.9 41.0 40.5 40.1 39.7 39.2 38.8 37.9 37.5 37.1 (10⁻⁷/° C.) Density (g/cm³) 2.710 2.729 2.748 2.766 2.785 2.689 2.681 2.674 2.666 2.659 2.652 2.637 2.629 2.622 Strain point (° C.) 764 761 757 754 751 757 757 758 758 759 759 760 760 761 Annealing point (° C.) 824 821 817 813 808 811 812 813 814 815 817 819 820 821 Softening point (° C.) 1,067 1,063 1,059 1,054 1,050 1,041 1,043 1,045 1,047 1,049 1,052 1,056 1,059 1,061 10^(4.5) dPa · s (° C.) 1,399 1,395 1,390 1,386 1,381 1,338 1,344 1,350 1,356 1,363 1,369 1,381 1,387 1,393 10^(4.0) dPa · s (° C.) 1,564 1,558 1,552 1,545 1,538 1,494 1,500 1,507 1,514 1,522 1,529 1,544 1,552 1,560 10^(3.0) dPa · s (° C.) 1,670 1,665 1,660 1,655 1,649 1,585 1,594 1,603 1,612 1,622 1,631 1,649 1,657 1,666 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 82.0 81.7 81.5 81.2 80.9 85.3 85.1 84.8 84.6 84.4 84.1 83.7 83.5 83.2 Specific Young's modulus 30.3 30.0 29.6 29.3 29.0 31.7 31.7 31.7 31.7 31.7 31.7 31.7 31.7 31.7 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.10 0.10 0.03 0.07 0.09 0.04 0.15 0.09 0.14 0.12 0.06 0.10 0.06 0.13

TABLE 44 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 603 604 605 606 607 608 609 610 611 612 613 614 615 616 mol SiO₂ 72.6 73.1 73.6 73.0 72.6 72.2 71.8 71.4 71.0 70.2 69.8 69.4 69.0 68.6 % Al₂O₃ 12.2 12.0 11.8 10.1 10.6 11.1 11.6 12.1 12.6 13.6 14.1 14.6 15.1 15.6 B₂O₃ 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 MgO 5.7 5.6 5.5 6.3 6.3 6.2 6.2 6.2 6.1 6.1 6.0 6.0 6.0 5.9 CaO 3.5 3.5 3.4 3.9 3.9 3.9 3.9 3.8 3.8 3.8 3.8 3.7 3.7 3.7 SrO 2.0 1.9 1.9 2.2 2.2 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.0 BaO 3.6 3.6 3.5 4.0 4.0 4.0 4.0 3.9 3.9 3.9 3.9 3.8 3.8 3.8 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 84.8 85.1 85.4 83.1 83.2 83.3 83.4 83.5 83.6 83.8 83.9 84.0 84.1 84.2 [MgO] + [CaO] + [SrO] + [BaO] 14.8 14.5 14.3 16.4 16.4 16.3 16.2 16.1 16.0 15.8 15.7 15.6 15.5 15.4 [SrO] + [BaO] 5.6 5.5 5.4 6.2 6.2 6.1 6.1 6.1 6.0 6.0 5.9 5.9 5.9 5.8 [B₂O₃]/([SrO] + [BaO]) 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [Al₂O₃] + [B₂O₃] − [CaO] − 3.4 3.3 3.2 0.3 0.8 1.4 1.9 2.5 3.0 4.2 4.7 5.3 5.8 6.4 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 362.5 357.7 352.8 346.6 352.4 358.3 364.1 370.0 375.8 387.6 393.4 399.3 405.1 411.0 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,783.3 1,783.3 1,783.2 1,765.6 1,768.6 1,771.6 1,774.7 1,777.7 1,780.7 1,786.7 1,789.8 1,792.8 1,795.8 1,798.8 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 36.7 36.4 36.0 39.4 39.2 39.0 38.9 38.7 38.5 38.2 38.1 38.0 37.8 37.7 (10⁻⁷/° C.) Density (g/cm³) 2.615 2.607 2.600 2.631 2.633 2.636 2.638 2.640 2.642 2.646 2.648 2.651 2.653 2.655 Strain point (° C.) 761 762 762 745 747 750 752 755 757 761 763 764 766 767 Annealing point (° C.) 822 823 825 802 804 807 810 812 815 820 822 823 824 824 Softening point (° C.) 1,064 1,067 1,071 1,041 1,044 1,046 1,049 1,051 1,053 1,055 1,055 1,055 1,055 1,054 10^(4.5) dPa · s (° C.) 1,399 1,405 1,410 1,381 1,381 1,381 1,380 1,379 1,377 1,373 1,370 1,367 1,364 1,361 10^(4.0) dPa · s (° C.) 1,568 1,576 1,584 1,555 1,553 1,550 1,548 1,544 1,541 1,532 1,527 1,522 1,517 1,512 10^(3.0) dPa · s (° C.) 1,674 1,683 1,691 1,664 1,662 1,659 1,655 1,650 1,645 1,634 1,628 1,621 1,615 1,609 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 83.0 82.8 82.5 81.6 82.0 82.4 82.8 83.1 83.5 84.3 84.7 85.1 85.5 85.8 Specific Young's modulus 31.7 31.7 31.7 31.0 31.1 31.3 31.4 31.5 31.6 31.9 32.0 32.1 32.2 32.3 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.13 0.10 0.10 0.14 0.11 0.10 0.05 0.07 0.07 0.14 0.09 0.03 0.09 0.09

TABLE 45 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 617 618 619 620 621 622 623 624 625 626 627 628 629 630 mol SiO₂ 68.2 70.7 70.5 70.3 70.2 70.0 69.9 69.7 69.6 69.5 69.3 69.2 69.0 68.9 % Al₂O₃ 16.1 13.1 13.1 13.0 13.0 13.0 13.0 12.9 12.9 12.9 12.9 12.8 12.8 12.8 B₂O₃ 0.3 0.1 0.5 0.7 0.9 1.1 1.3 1.5 1.7 1.9 2.1 2.3 2.5 2.7 MgO 5.9 6.1 6.1 6.1 6.1 6.1 6.0 6.0 6.0 6.0 6.0 6.0 6.0 6.0 CaO 3.7 3.8 3.8 3.8 3.8 3.8 3.8 3.8 3.7 3.7 3.7 3.7 3.7 3.7 SrO 2.0 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.0 BaO 3.8 3.9 3.9 3.9 3.9 3.9 3.9 3.9 3.8 3.8 3.8 3.8 3.8 3.8 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 84.3 83.9 83.5 83.4 83.2 83.0 82.9 82.7 82.5 82.4 82.2 82.0 81.9 81.7 [MgO] + [CaO] + [SrO] + [BaO] 15.4 15.9 15.9 15.8 15.8 15.8 15.7 15.7 15.7 15.6 15.6 15.6 15.5 15.5 [SrO] + [BaO] 5.8 6.0 6.0 6.0 6.0 6.0 5.9 5.9 5.9 5.9 5.9 5.9 5.9 5.9 [B₂O₃]/([SrO] + [BaO]) 0.1 0.0 0.1 0.1 0.2 0.2 0.2 0.3 0.3 0.3 0.4 0.4 0.4 0.5 [Al₂O₃] + [B₂O₃] − [CaO] − 6.9 3.4 3.8 4.0 4.2 4.4 4.6 4.8 5.0 5.1 5.3 5.5 5.7 5.9 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 416.8 385.5 377.9 374.1 370.4 366.6 362.8 359.0 355.3 351.5 347.7 343.9 340.2 336.4 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,801.8 1,786.6 1,780.9 1,778.0 1,775.2 1,772.4 1,769.5 1,766.7 1,763.8 1,761.0 1,758.2 1,755.3 1,752.5 1,749.6 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 37.5 38.4 38.4 38.3 38.3 38.3 38.3 38.3 38.3 38.2 38.2 38.2 38.2 38.2 (10⁻⁷/° C.) Density (g/cm³) 2.657 2.646 2.642 2.640 2.637 2.635 2.633 2.631 2.629 2.626 2.624 2.622 2.620 2.617 Strain point (° C.) 768 763 757 754 751 748 745 743 740 738 735 733 730 728 Annealing point (° C.) 824 821 815 812 809 806 803 801 798 795 793 790 788 785 Softening point (° C.) 1,053 1,057 1,051 1,048 1,045 1,042 1,038 1,035 1,031 1,028 1,024 1,020 1,017 1,013 10^(4.5) dPa · s (° C.) 1,358 1,378 1,372 1,369 1,366 1,364 1,361 1,358 1,355 1,352 1,349 1,346 1,343 1,340 10^(4.0) dPa · s (° C.) 1,506 1,539 1,534 1,531 1,528 1,526 1,523 1,520 1,517 1,514 1,512 1,509 1,506 1,503 10^(3.0) dPa · s (° C.) 1,603 1,642 1,637 1,634 1,631 1,628 1,625 1,622 1,619 1,616 1,613 1,609 1,606 1,603 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 86.2 84.1 83.7 83.5 83.3 83.0 82.8 82.6 82.4 82.2 81.9 81.7 81.5 81.3 Specific Young's modulus 32.5 31.8 31.7 31.6 31.6 31.5 31.5 31.4 31.3 31.3 31.2 31.2 31.1 31.1 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.11 0.11 0.10 0.15 0.11 0.11 0.11 0.08 0.06 0.10 0.10 0.11 0.07 0.12

TABLE 46 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 631 632 633 634 635 636 637 638 639 640 641 642 643 644 mol SiO₂ 68.8 68.6 68.5 72.9 72.5 72.1 71.7 71.4 71.0 70.2 69.8 69.5 69.1 68.7 % Al₂O₃ 12.8 12.7 12.7 13.5 13.4 13.4 13.3 13.2 13.2 13.0 13.0 12.9 12.8 12.8 B₂O₃ 2.9 3.1 3.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 MgO 5.9 5.9 5.9 3.1 3.6 4.1 4.6 5.1 5.6 6.6 7.1 7.6 8.1 8.6 CaO 3.7 3.7 3.7 3.9 3.9 3.9 3.9 3.8 3.8 3.8 3.8 3.7 3.7 3.7 SrO 2.0 2.0 2.0 2.2 2.2 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.0 BaO 3.8 3.8 3.8 4.0 4.0 4.0 4.0 3.9 3.9 3.9 3.9 3.8 3.8 3.8 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 81.5 81.3 81.2 86.4 85.9 85.5 85.0 84.6 84.1 83.3 82.8 82.4 81.9 81.5 [MgO] + [CaO] + [SrO] + [BaO] 15.5 15.5 15.4 13.2 13.7 14.1 14.6 15.0 15.5 16.3 16.8 17.2 17.7 18.1 [SrO] + [BaO] 5.8 5.8 5.8 6.2 6.2 6.1 6.1 6.1 6.0 6.0 5.9 5.9 5.9 5.8 [B₂O₃]/([SrO] + [BaO]) 0.5 0.5 0.6 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [Al₂O₃] + [B₂O₃] − [CaO] − 6.1 6.3 6.5 3.7 3.7 3.7 3.7 3.6 3.6 3.6 3.6 3.5 3.5 3.5 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 332.6 328.8 325.1 374.7 375.9 377.1 378.2 379.4 380.5 382.9 394.0 385.2 386.3 387.5 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,746.8 1,744.0 1,741.1 1,799.6 1,796.9 1,794.3 1,791.6 1,789.0 1,786.4 1,781.1 1,778.4 1,775.8 1,773.2 1,770.5 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 38.2 38.1 38.1 36.3 36.6 37.0 37.3 37.7 38.0 38.7 39.1 39.4 39.8 40.2 (10⁻⁷/° C.) Density (g/cm³) 2.615 2.613 2.611 2.624 2.627 2.630 2.634 2.637 2.641 2.648 2.651 2.654 2.658 2.661 Strain point (° C.) 725 723 721 778 773 769 766 763 761 758 756 755 753 751 Annealing point (° C.) 783 780 778 842 837 832 828 824 821 815 812 810 808 806 Softening point (° C.) 1,009 1,006 1,002 1,094 1,084 1,075 1,068 1,063 1,058 1,049 1,045 1,039 1,034 1,027 10^(4.5) dPa · s (° C.) 1,337 1,334 1,331 1,425 1,417 1,409 1,400 1,392 1,383 1,366 1,358 1,349 1,341 1,332 10^(4.0) dPa · s (° C.) 1,500 1,498 1,495 1,593 1,583 1,573 1,564 1,555 1,546 1,528 1,519 1,510 1,501 1,492 10^(3.0) dPa · s (° C.) 1,600 1,597 1,594 1,698 1,688 1,679 1,669 1,660 1,650 1,629 1,619 1,609 1,598 1,587 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 81.1 80.8 80.6 82.2 82.5 82.7 83.0 83.3 83.6 84.2 84.5 84.8 85.1 85.4 Specific Young's modulus 31.0 30.9 30.9 31.3 31.4 31.5 31.5 31.6 31.7 31.8 31.9 31.9 32.0 32.1 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.14 0.11 0.08 0.10 0.15 0.11 0.09 0.06 0.06 0.09 0.03 0.07 0.09 0.14

TABLE 47 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 645 646 647 648 649 650 651 652 653 654 655 656 657 658 mol SiO₂ 68.3 72.8 72.4 72.1 71.7 71.3 71.0 70.2 69.9 69.5 69.1 68.8 68.4 72.0 % Al₂O₃ 12.7 13.5 13.4 13.4 13.3 13.2 13.2 13.0 13.0 12.9 12.8 12.8 12.7 13.4 B₂O₃ 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 MgO 9.1 6.3 6.3 6.2 6.2 6.2 6.1 6.1 6.0 6.0 6.0 5.9 5.9 6.2 CaO 3.7 0.8 1.3 1.8 2.3 2.8 3.3 4.3 4.8 5.3 5.8 6.3 6.8 3.9 SrO 2.0 2.2 2.2 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.1 2.0 2.0 0.1 BaO 3.8 4.0 4.0 4.0 4.0 3.9 3.9 3.9 3.9 3.8 3.8 3.8 3.8 4.0 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 81.0 86.3 85.9 85.4 85.0 84.6 84.1 83.3 82.8 82.4 82.0 81.5 81.1 85.4 [MgO] + [CaO] + [SrO] + [BaO] 18.6 13.3 13.7 14.2 14.6 15.0 15.5 16.3 16.8 17.2 17.6 18.1 18.5 14.2 [SrO] + [BaO] 5.8 6.2 6.2 6.1 6.1 6.1 6.0 6.0 5.9 5.9 5.9 5.8 5.8 4.1 [B₂O₃]/([SrO] + [BaO]) 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [Al₂O₃] + [B₂O₃] − [CaO] − 3.5 6.8 6.3 5.8 5.2 4.7 4.1 3.1 2.5 2.0 1.4 0.9 0.4 5.7 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 388.7 390.5 389.0 387.6 386.1 384.6 383.2 380.2 378.8 377.3 375.8 374.4 372.9 360.9 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,767.9 1,795.4 1,793.5 1,791.5 1,789.6 1,787.6 1,785.7 1,781.8 1,779.8 1,777.9 1,775.9 1,774.0 1,772.0 1,788.5 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 40.5 34.1 34.8 35.4 36.2 36.9 37.6 39.1 39.9 40.7 41.4 42.2 42.9 34.8 (10⁻⁷/° C.) Density (g/cm³) 2.665 2.617 2.621 2.626 2.630 2.635 2.640 2.649 2.653 2.658 2.662 2.667 2.672 2.599 Strain point (° C.) 749 773 771 769 767 764 762 757 754 751 748 745 742 766 Annealing point (° C.) 804 838 834 831 828 825 821 814 811 807 803 799 796 827 Softening point (° C.) 1,021 1,083 1,077 1,071 1,066 1,062 1,058 1,049 1,045 1,040 1,034 1,029 1,023 1,064 10^(4.5) dPa · s (° C.) 1,323 1,416 1,409 1,403 1,396 1,389 1,382 1,368 1,360 1,353 1,345 1,338 1,330 1,395 10^(4.0) dPa · s (° C.) 1,483 1,582 1,574 1,566 1,559 1,551 1,544 1,529 1,521 1,513 1,504 1,496 1,487 1,556 10^(3.0) dPa · s (° C.) 1,577 1,685 1,678 1,671 1,664 1,656 1,648 1,631 1,622 1,613 1,604 1,596 1,587 1,661 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 85.7 83.6 83.7 83.7 83.8 83.8 83.9 84.0 84.0 84.1 84.1 84.1 84.2 84.4 Specific Young's modulus 32.1 32.0 31.9 31.9 31.8 31.8 31.8 31.7 31.7 31.6 31.6 31.5 31.5 32.5 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.06 0.08 0.04 0.13 0.11 0.04 0.09 0.07 0.10 0.14 0.04 0.05 0.13 0.12

TABLE 48 No. No. No. No. No. No. No. No. No. No. No. No. No. No. 659 660 661 662 663 664 665 666 667 668 669 670 671 672 mol SiO₂ 71.7 71.3 71.0 70.2 69.9 69.5 69.2 68.8 68.4 72.8 72.4 72.1 71.7 71.3 % Al₂O₃ 13.3 13.2 13.2 13.0 13.0 12.9 12.8 12.8 12.7 13.5 13.4 13.4 13.3 13.2 B₂O₃ 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 MgO 6.2 6.2 6.1 6.1 6.0 6.0 6.0 5.9 5.9 6.3 6.3 6.2 6.2 6.2 CaO 3.9 3.8 3.8 3.8 3.8 3.7 3.7 3.7 3.7 3.9 3.9 3.9 3.9 3.8 SrO 0.6 1.1 1.6 2.6 3.1 3.6 4.1 4.6 5.1 2.2 2.2 2.1 2.1 2.1 BaO 4.0 3.9 3.9 3.9 3.9 3.8 3.8 3.8 3.8 0.9 1.4 1.9 2.4 2.9 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 85.0 84.6 84.1 83.3 82.8 82.4 82.0 81.6 81.1 86.3 85.9 85.4 85.0 84.6 [MgO] + [CaO] + [SrO] + [BaO] 14.6 15.0 15.5 16.3 16.8 17.2 17.6 18.0 18.5 13.3 13.7 14.2 14.6 15.0 [SrO] + [BaO] 4.6 5.0 5.5 6.5 7.0 7.4 7.9 8.4 8.9 3.1 3.6 4.0 4.5 5.0 [B₂O₃]/([SrO] + [BaO]) 0.1 0.1 0.1 0.0 0.0 0.0 0.0 0.0 0.0 0.1 0.1 0.1 0.1 0.1 [Al₂O₃] + [B₂O₃] − [CaO] − 5.2 4.7 4.1 3.1 2.5 2.0 1.5 1.0 0.4 6.8 6.3 5.8 5.2 4.7 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 366.1 371.3 376.5 386.9 392.1 397.3 402.5 407.7 412.9 343.7 350.0 356.4 362.7 369.0 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,787.3 1,786.1 1,784.9 1,782.5 1,781.3 1,780.1 1,778.9 1,777.7 1,776.5 1,792.6 1,791.1 1,789.7 1,788.2 1,786.7 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 35.7 36.6 37.5 39.3 40.2 41.2 42.1 43.0 43.9 32.5 33.4 34.3 35.3 36.3 (10⁻⁷/° C.) Density (g/cm³) 2.610 2.622 2.633 2.655 2.667 2.678 2.689 2.701 2.712 2.531 2.550 2.569 2.588 2.606 Strain point (° C.) 765 763 762 757 755 753 750 748 745 769 768 766 765 763 Annealing point (° C.) 825 823 820 815 811 808 805 801 797 830 829 827 825 823 Softening point (° C.) 1,062 1,059 1,057 1,051 1.047 1,043 1,038 1,033 1,029 1,067 1,065 1,063 1,061 1,059 10^(4.5) dPa · s (° C.) 1,390 1.385 1,380 1,370 1,365 1,359 1,354 1,349 1,343 1,395 1,392 1,389 1,386 1,382 10^(4.0) dPa · s (° C.) 1,551 1.547 1,542 1,531 1,525 1.519 1,513 1,506 1,499 1,558 1,554 1,550 1,547 1,544 10^(3.0) dPa · s (° C.) 1,656 1,651 1,645 1,634 1,628 1,621 1,615 1,608 1,602 1,660 1,657 1,654 1,651 1,648 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured sured sured sured sured sured sured sured Young's modulus (GPa) 84.3 84.2 84.0 83.8 83.7 83.5 83.4 83.3 83.2 85.6 85.3 85.0 84.8 84.5 Specific Young's modulus 32.3 32.1 31.9 31.6 31.4 31.2 31.0 30.8 30.7 33.8 33.5 33.1 32.8 32.4 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.08 0.07 0.13 0.08 0.05 0.12 0.15 0.08 0.08 0.04 0.13 0.13 0.06 0.14

TABLE 49 No. No. No. No. No. No. No. 673 674 675 676 677 678 679 mol SiO₂ 71.0 70.2 69.9 69.5 69.1 68.8 68.4 % Al₂O₃ 13.2 13.0 13.0 12.9 12.8 12.8 12.7 B₂O₃ 0.3 0.3 0.3 0.3 0.3 0.3 0.3 MgO 6.1 6.1 6.0 6.0 6.0 5.9 5.9 CaO 3.8 3.8 3.8 3.7 3.7 3.7 3.7 SrO 2.1 2.1 2.1 2.1 2.1 2.0 2.0 BaO 3.4 4.4 4.9 5.4 5.9 6.4 6.9 ZnO 0.0 0.0 0.0 0.0 0.0 0.0 0.0 SnO₂ 0.1 0.1 0.1 0.1 0.1 0.1 0.1 [SiO₂] + [Al₂O₃] 84.1 83.3 82.8 82.4 82.0 81.5 81.1 [MgO] + [CaO] + [SrO] + [BaO] 15.5 16.3 16.8 17.2 17.7 18.1 18.5 [SrO] + [BaO] 5.5 6.5 7.0 7.5 8.0 8.4 8.9 [B₂O₃]/([SrO] + [BaO]) 0.1 0.0 0.0 0.0 0.0 0.0 0.0 [Al₂O₃] + [B₂O₃] − [CaO] − 4.1 3.1 2.5 2.0 1.4 0.9 0.4 [SrO] − [BaO] [SiO₂] + 14[Al₂O₃] − 375.4 368.0 394.4 400.7 407.0 413.4 419.7 15[B₂O₃] + 6[MgO] + [CaO] + 14[SrO] + 16[BaO] 17.8[SiO₂] + 23.1[Al₂O₃] + 1,785.2 1,782.2 1,780.7 1,779.3 1,777.8 1,776.3 1,774.8 3.7[B₂O₃] + 12.9[MgO] + 14.1[CaO] + 15.5[SrO] + 15.0[BaO] + 7.2[ZnO] Thermal expansion coefficient 37.3 39.4 40.5 41.6 42.6 43.7 44.7 (10⁻⁷/° C.) Density (g/cm³) 2.625 2.663 2.682 2.701 2.720 2.739 2.757 Strain point (° C.) 762 757 755 753 750 748 746 Annealing point (° C.) 821 815 811 808 804 801 797 Softening point (° C.) 1,056 1,051 1,048 1,044 1,039 1,035 1,031 10^(4.5) dPa · s (° C.) 1,379 1,371 1,367 1,363 1,359 1,355 1,351 10^(4.0) dPa · s (° C.) 1,540 1,532 1,528 1,523 1,517 1,511 1,505 10^(3.0) dPa · s (° C.) 1,644 1,635 1,631 1,626 1,621 1,616 1,611 10^(2.5) dPa · s (° C.) Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- Unmea- sured sured sured sured sured sured sured Young's modulus (GPa) 84.2 83.6 83.3 83.1 82.8 82.5 82.2 Specific Young's modulus 32.1 31.4 31.1 30.8 30.4 30.1 29.8 (GPa/g · cm⁻³) β-OH (mm⁻¹) 0.08 0.08 0.05 0.13 0.09 0.15 0.12

First, a glass batch prepared by blending glass raw materials so as to achieve the glass composition shown in each Table was loaded in a platinum crucible, and then melted at from 1,600° C. to 1,650° C. for 24 hours. In melting the glass batch, molten glass was stirred to be homogenized by using a platinum stirrer. Next, the molten glass was poured on a carbon sheet and formed into a sheet shape, followed by being annealed at a temperature around an annealing point for 30 minutes. Each of the resultant samples was evaluated for its thermal expansion coefficient, density, strain point, annealing point, softening point, temperature at a viscosity at high temperature of 10^(4.5) dPa·s, temperature at a viscosity at high temperature of 10^(4.0) dPa·s, temperature at a viscosity at high temperature of 10³⁰ dPa·s, temperature at a viscosity at high temperature of 10^(2.5) dPa·s, Young's modulus, specific Young's modulus, and β-OH.

The thermal expansion coefficient is a value obtained by measuring an average thermal expansion coefficient within a temperature range of from 30° C. to 380° C. with a dilatometer.

The density is a value measured by a well-known Archimedes method.

The strain point, the annealing point, and the softening point are values measured in accordance with methods specified in ASTM C336 and C338.

The temperatures at viscosities at high temperature of 10^(4.5) dPa·s, 10^(4.0) dPa·s, 10^(3.0) dPa·s, and 10^(2.5) dPa·s are values measured by a platinum sphere pull up method.

The Young's modulus is a value measured by a flexural resonance method.

The specific Young's modulus is a value obtained by dividing the Young's modulus by the density.

The β-OH is a value measured by the above-mentioned method.

As apparent from Tables 1 to 49, each of Sample Nos. 1 to 679 has a high strain point, and is free of Y₂O₃ and La₂O₃ in the glass composition, and is hence considered to enable a reduction in manufacturing cost.

Example 2

Data on a relationship between β-OH and a thermal shrinkage rate are shown in Table 50. Sample A and Sample B each have the glass composition according to Sample No. 1, but have different β-OH values. Sample A and Sample B were each measured for its thermal shrinkage rate when held at 500° C. for 1 hour and its thermal shrinkage rate when held at 600° C. for 1 hour.

TABLE 50 A B Glass composition Sample No. 1 Sample No. 1 β-OH 0.13 mm⁻¹ 0.36 mm⁻¹ Thermal shrinkage rate at 500° C.-1 hr. 8 ppm 10 ppm Thermal shrinkage rate at 500° C.-2 hr. 31 ppm 39 ppm

The thermal shrinkage rate may be measured as described below. First, linear markings are engraved in parallel in two portions on the glass sheet. Then, the glass sheet is divided in a direction perpendicular to the markings to obtain two glass pieces. Next, one of the glass pieces is increased in temperature from normal temperature to 500° C. or 600° C. at a temperature increase rate of 5° C./min, held at 500° C. or 600° C. for 1 hour, and cooled to normal temperature at a temperature decrease rate of 5° C./min. Subsequently, the glass piece subjected to the heat treatment and the glass piece not subjected to the heat treatment are arranged so that divided surfaces are aligned with each other and fixed with an adhesive tape. After that, a deviation amount ΔL between the markings is measured. Finally, a value of ΔL/L₀ is measured as a thermal shrinkage rate. The “L₀” refers to the length of the glass piece before the heat treatment.

From Table 50, it is revealed that, even with the same glass composition, the thermal shrinkage rate can be reduced more at lower β-OH.

Example 3

Glasses having the glass compositions of the above-mentioned Sample Nos. 1, 15, and 115 were each melted using an existing facility under the conventional temperature conditions, and formed into a glass sheet by an overflow down-draw method, followed by being measured for the contents of trace components by X-ray fluorescence analysis. The results are shown in Table 51.

TABLE 51 (wt:ppm) No. 1 No. 15 No. 115 Rh 0.8 0.5 0.6 Pt 0.1 0.1 0.1 Ir 0.1-1 0.1-1 0.1-1 ZrO₂ 300 350 320 Sb₂O₃ <30 <30 <30 Fe₂O₃ 100 90 110 MoO₃ Unmeasured Unmeasured Unmeasured TiO₂ 10 8 12 Na₂O 120 90 100

Example 4

Glasses having the glass compositions of the above-mentioned Sample Nos. 1, 15, and 115 were each melted using an existing facility other than the facility used in [Example 3] at a higher temperature than in the conventional conditions, and formed into a glass sheet by an overflow down-draw method, followed by being measured for the contents of trace components by X-ray fluorescence analysis. The results are shown in Table 52.

TABLE 52 (wt:ppm) No. 1 No. 15 No. 115 Rh 0.6    0.4 0.9 Pt Unmeasured Unmeasured Unmeasured Ir Unmeasured Unmeasured Unmeasured ZrO₂ 1,200 500 1,500 Sb₂O₃ Unmeasured Unmeasured Unmeasured Fe₂O₃ 130 300 100 MoO₃ 10  3 20 TiO₂ Unmeasured Unmeasured Unmeasured Na₂O Unmeasured Unmeasured Unmeasured 

1. An alkali-free glass sheet, comprising as a glass composition, in terms of mol %, 55% to 80% of SiO₂, 10% to 25% of Al₂O₃, 0% to 4% of B₂O₃, 0% to 30% of MgO, 0% to 25% of CaO, 0% to 15% of SrO, 0% to 15% of BaO, 0% to 5% of ZnO, and 0% to less than 1.0% of Y₂O₃+La₂O₃, being substantially free of an alkali metal oxide, and having a strain point of 750° C. or more.
 2. The alkali-free glass sheet according to claim 1, wherein the alkali-free glass sheet satisfies a relationship of [SiO₂]+14×[Al₂O₃]−15×[B₂O₃]+6×[MgO]+[CaO]+14×[SrO]+16×[BaO]≥360 mol %.
 3. The alkali-free glass sheet according to claim 1, wherein the alkali-free glass sheet satisfies a relationship of 17.8×[SiO₂]+23.1×[Al₂O₃]+3.7×[B₂O₃]+12.9×[MgO]+14.1×[CaO]+15.5×[SrO]+15.0×[BaO]+7.2×[ZnO]≥1,786 mol %.
 4. The alkali-free glass sheet according to claim 1, wherein the alkali-free glass sheet has a content of Rh of from 0.1 ppm by mass to 3 ppm by mass.
 5. The alkali-free glass sheet according to claim 1, wherein the alkali-free glass sheet has a Young's modulus of 82 GPa or more.
 6. The alkali-free glass sheet according to claim 2, wherein the alkali-free glass sheet satisfies a relationship of 17.8×[SiO₂]+23.1×[Al₂O₃]+3.7×[B₂O₃]+12.9×[MgO]+14.1×[CaO]+15.5×[SrO]+15.0×[BaO]+7.2×[ZnO]≥1,786 mol %. 